TY - JOUR A1 - Stawski, Tomasz A1 - Karafiludis, Stephanos A1 - Pimentel, Carlos A1 - Montes-Hernández, German A1 - Kochovski, Zdravko A1 - Bienert, Ralf A1 - Weimann, Karin A1 - Emmerling, Franziska A1 - Scoppola, Ernesto A1 - Van Driessche, Alexander E.S. T1 - Solution-driven processing of calcium sulfate: The mechanism of the reversible transformation of gypsum to bassanite in brines N2 - Here, we show that calcium sulfate dihydrate (gypsum) can be directly, rapidly and reversibly converted to calcium sulfate hemihydrate (bassanite) in high salinity solutions (brines). The optimum conditions for the efficient production of bassanite in a short time (<5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the better-known behaviour of the bassanite phase in low-salt environments. In low-salinity aqueous solutions, bassanite is considered to be metastable with respect to gypsum and anhydrite, and therefore gypsum-to-bassanite conversion does not occur in pure water. Interestingly, the high-salinity transformation of gypsum-to-bassanite has been reported by many authors and used in practice for several decades, although its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures was inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline phase for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios. KW - Industrial and Manufacturing Engineering KW - Strategy and Management KW - General Environmental Science KW - Renewable Energy, Sustainability and the Environment KW - Building and Construction KW - Calcium sulfate KW - Gypsum KW - Bassanite KW - Scattering KW - Raman KW - In situ KW - Synchrotron KW - BESSY KW - MySpot PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-594698 UR - https://www.sciencedirect.com/science/article/pii/S0959652624004591#appsec1 DO - https://doi.org/10.1016/j.jclepro.2024.141012 SN - 0959-6526 VL - 440 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-59469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stawski, Tomasz A1 - Besselink, R. A1 - Chatzipanagis, K. A1 - Hövelmann, J. A1 - Benning, L. G. A1 - Van Driessche, E. S. T1 - Nucleation Pathway of Calcium Sulfate Hemihydrate (Bassanite) from Solution: Implications for Calcium Sulfates on Mars N2 - CaSO4 minerals (i.e., gypsum, anhydrite, and bassanite) are widespread in natural and industrial environments. During the last several years, a number of studies have revealed that nucleation in the CaSO4–H2O system is nonclassical, where the formation of crystalline phases involves several steps. Based on these recent insights, we have formulated a tentative general model for calcium sulfate precipitation from solution. This model involves primary species that are formed through the assembly of multiple Ca2+ and SO42– ions into nanoclusters. These nanoclusters assemble into poorly ordered (i.e., amorphous) hydrated aggregates, which in turn undergo ordering into coherent crystalline units. The thermodynamic (meta)stability of any of the three CaSO4 phases is regulated by temperature, pressure, and ionic strength, with gypsum being the stable form at low temperatures and low-to-medium ionic strengths and anhydrite being the stable phase at high temperatures and at lower temperature for high salinities. Bassanite is metastable across the entire phase diagram but readily forms as the primary phase at high ionic strengths across a wide range of temperatures and can persist up to several months. Although the physicochemical conditions leading to bassanite formation in aqueous systems are relatively well established, nanoscale insights into the nucleation mechanisms and pathways are still lacking. To fill this gap and to further improve our general model for calcium sulfate precipitation, we conducted in situ scattering measurements at small-angle X-ray scattering and wide-angle X-ray scattering and complemented these with in situ Raman spectroscopic characterization. Based on these experiments, we show that the process of formation of bassanite from aqueous solutions is very similar to the formation of gypsum: it involves the aggregation of small primary species into larger disordered aggregates, only from which the crystalline phase develops. These data thus confirm our general model of CaSO4 nucleation and provide clues to explain the abundant occurrence of bassanite on the surface of Mars (and not on the surface of Earth). KW - Gypsum' SAXS KW - Calcium sulfate KW - Bassanite KW - Nucleation PY - 2020 DO - https://doi.org/10.1021/acs.jpcc.0c01041 VL - 124 IS - 15 SP - 8411 EP - 8422 PB - American Chemical Society AN - OPUS4-50849 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz A1 - Karafiludis, Stephanos A1 - Pimentel, C. A1 - Montes Hernandez, G A1 - Kochovski, Z A1 - Bienert, Ralf A1 - Weimann, Karin A1 - Emmerling, Franziska A1 - Scoppola, E A1 - Van Driessche, A T1 - Solution-driven processing of calcium sulfate: the mechanism of the reversible transformation of gypsum to bassanite in brines N2 - Calcium sulfate hemihydrate (CaSO4ᐧ0.5H2O), also known as bassanite, has been used as a precursor to produce gypsum (dihydrate, CaSO4ᐧ2H2O) for various construction and decorative purposes since prehistoric times. The main route to obtain hemihydrate is a thermal treatment of gypsum at temperatures typically between 150 °C and 200 °C to remove some of the structural water. In this contribution, we introduce (Fig. 1) a more efficient and sustainable method (T < 100 °C) that enables the direct, rapid, and reversibly conversion of gypsum to bassanite using reusable high salinity aqueous solutions (brines with c[NaCl] > 4 M). The optimum conditions for the efficientproduction of bassanite in a short time (< 5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the typical behaviour of the bassanite phase in low salt environments. Traditionally, hemihydrate is obtained through a solid state thermal treatment because bassanite is considered to be metastable with respect to gypsum and anhydrite in aqueous solutions, and therefore gypsum-to-bassanite conversion should not occur in water. Its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures is inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline structure for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios. T2 - Granada Münster Discussion Meeting GMDM 10 CY - Münster, Germany DA - 29.11.2023 KW - Gypsum KW - Bassanite KW - Calcium sulfate KW - Recycling KW - Scattering PY - 2024 AN - OPUS4-59162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz T1 - Scattering is a powerful tool to follow nucleation and growth of minerals from solutions N2 - In recent years, we have come to appreciate the astounding intricacy of the processes leading to the formation of minerals from ions in aqueous solutions. The original, and rather naive, ‘textbook’ image of these phenomena, stemming from the adaptation of classical nucleation and growth theories, has increased in complexity due to the discovery of a variety of precursor and intermediate species. These include solute clusters (e.g. prenucleation clusters, PNCs), liquid(-like) phases, as well as amorphous and nanocrystalline solids etc.. Does it, however, mean that all the minerals grow through intermediate phases, following a non-classical pathway? In general, the precursor or intermediate species constitute different, often short-lived, points along the pathway from dissolved ions to the final solids (typically crystals in this context). In this regard synchrotron-based scattering (SAXS/WAXS/total scattering) appears to be the perfect tool to follow in situ and in a time-resolved manner the crystallization pathway because of the temporal and spatial length scales that can be directly accessed with these techniques. In this presentation we show how we used scattering to probe the crystallisation mechanisms of calcium sulfate, This system contains minerals that are widespread in diverse natural environments, but they are also important in various industrial settings. Our data demonstrate that calcium sulfate precipitation involves formation and aggregation of sub-3 nm anisotropic primary species. The actual crystallisation and formation of imperfect single crystals of calcium sulfate phases, takes place from the inside of the in itial aggregates. Hence, calcium sulfate follows a non-classical pathway. T2 - X-ray Powder Diffraction at DESY - new opportunities for research and industry CY - Online meeting DA - 22.06.2020 KW - Nucleation KW - Calcium sulfate KW - Diffraction KW - Scattering KW - Synchrotron KW - SAXS/WAXS PY - 2020 AN - OPUS4-50943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz A1 - Wolf, Jakob A1 - Emmerling, Franziska T1 - Smart Machines, New Materials, Automated Future N2 - In pursuing the automated synthesis of metal nanoparticles (NPs), the capabilities of the “Chemputer” are deployed, for the first time, into the field of inorganic chemistry. Metal NPs have a substantial impact across different fields of science, such as photochemistry, energy conversion, and medicine. Among the commonly used nanoparticles, silver NPs are of special interest due to their antibacterial properties and applications in sensing and catalysis. However, many of the methods used to synthesize Ag NPs often do not result in well-defined products, the main obstacles being high polydispersity or a lack of particle size tunability. The Chemputer is a modular, automated platform developed by the Cronin group for execution of multi-step, solution based organic synthesis. The machine has been further implemented at BAM, where we used this setup to perform automated organic syntheses, autonomously controlled by feedback derived from online NMR. In the Chemputer liquids can be transferred across a backbone, constructed from HPLC selection valves and syringe pumps. The Chemputer operates in a batch mode, common laboratory devices, such as heaters and glassware like round bottom flasks, are connected to the backbone, forming reaction modules. Solutions can be manipulated in these modules, and as all operations are controlled through a software script, reproducibility among individual syntheses is high. Likewise, any adjustments of the synthesis conditions, if required, are straightforward to implement and are documented in the reaction log file and a code versioning system. We characterised Chemputer-synthesized nanoparticles using small-angle X-ray scattering, dynamic light scattering and further methods, showing that automated synthesis can yield colloids with reproducible and tuneable properties. The approach is an important first step towards the automation of nanoparticle syntheses in a modular, multipurpose platform. The modularity of the Chemputer opens many possibilities for the synthesis of a variety of different NP morphologies and sizes and potentially more complex structures. These advances and further work can help in the general investigations of silver nanoparticles by supplying a reliable and reproducible method of their synthesis and removing tacit knowledge by significantly reducing the experimental bias. T2 - Analytica 2022 CY - Munich, Germany DA - 21.06.2022 KW - Automated synthesis KW - Nanoparticles PY - 2022 AN - OPUS4-55198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz A1 - de Oliveira Guilherme Buzanich, Ana A1 - Emmerling, Franziska T1 - Evolution of mesoporous frameworks from precipitated struvite-structured metal phosphate materials N2 - Mesoporous transition metal phosphates (TMPs) have attracted major interest due to their high (electro-)catalytic activity suitable for H2 generation, supercapacitors or batteries. Typically, mesoporous materials are synthesized via a template-based route. This way is in the case of TMP because the surfactants used are difficult to remove due to the sensitivity of the mesoporous framework. We present a template-free method including the formation of a precursor phase called M-struvite (NH4MPO4•6H2O, M = Mg2+, Ni2+, Co2+, Ni2+xCo2+1-x) to synthesize mesoporous and amorphous metal phosphates. This method relies on the thermal decomposition of crystalline M-struvite precursors to an amorphous and simultaneous mesoporous phase associated with the degassing of NH3 and H2O. The temporal evolution of mesoporous frameworks and the response of the coordination metal coordination environment was followed with diffraction and spectroscopy based in-situ and ex-situ methods. We highlight the systematic differences in absolute surface area, pore shape, pore size, and phase transitions between the chemical systems. In a complex amorphous structure, thermal decomposed Mg-, Ni- and NixCo1-x-struvites exhibit high surface areas and pore volumes for phosphate materials with a spherical to channel-like pore geometry (240 m²g-1 and 0.32 cm-3 g-1 for Mg and 90 m²g-1 and 0.13 cm-3 g-1 for Ni). In addition to this low-cost, environmentally friendly and simple synthesis, M-struvites could grow as a recycling product from industrial and agricultural wastewaters. These waste products could be upcycled through a simple thermal treatment for further applications. T2 - ECCG7, European Conference on Crystal Growth CY - Paris, France DA - 25.07.2022 KW - Transition metals KW - Phosphates KW - Struvite KW - Amorphous phases KW - Mesoporosity PY - 2022 AN - OPUS4-55491 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz A1 - Van Driessche, A. E. S. T1 - Particle-mediated origins of mesocrystalline disorder in calcium sulfate single crystals N2 - Calcium sulfate minerals are abundant in natural and engineered environments and they exist in the form of three hydrates: gypsum (CaSO4·2H2O), bassanite (CaSO4·0.5H2O), and anhydrite (CaSO4). Due to their relevance in natural and industrial processes, the formation pathways of these calcium sulfate phases from aqueous solution have been the subject of intensive research1. The state-of-the-art of the calcium sulfate formation mechanisms builds upon and goes beyond what we have come to appreciate in the astounding intricacy of other mineral formation processes from ions in aqueous solutions. The original, and rather naive, 'textbook' image of these phenomena, stemming from the adaptation of classical nucleation and growth theories, has increased in complexity due to the discovery of a variety of precursor and intermediate species2. These include solute clusters (e.g. prenucleation clusters, PNCs), liquid(-like) phases, as well as amorphous and nanocrystalline solids etc.. In this context, a number of studies have already revealed that nucleation in the CaSO4-H2O system is non-classical, where the formation of the different crystalline phases involves several steps including a common amorphous precursor1, 3, 4. In this contribution we show that the formation of the amorphous phase involves the aggregation of small primary particles into larger disordered aggregates exhibiting a "brick-in-the-wall" structure5, 6. The actual crystallization occurs by the restructuring and coalescence of the particles ("bricks") into a given calcium sulfate phase depending on the physicochemical conditions of the solution. Importantly, the rearrangement process does not continue until a (nearly-)perfect homogeneous single crystal is obtained. Instead it comes to a stop, or at least significantly slows down. Such a process thus yields a final imperfect mesocrystal, composed of smaller domains rather than a continuous crystal structure, within which the domains are separated by an amorphous (i.e. less ordered) calcium sulfate phase. Hence, the non-classical crystallization process of CaSO4 yields a final imperfect mesocrystal with an overall morphology resembling that of a single crystal, yet composed of smaller nano-domains. Importantly, these observations reveal that organic-free calcium sulfate mesocrystals grown by a particle mediated-pathway preserve in the final crystal structure a “memory” or “imprint” of their non-classical nucleation process, something that has been overlooked until now. Furthermore, the nano-scale misalignment of the structural sub-units within these crystals can propagate through the length-scales, and be expressed macroscopically as misaligned zones/domains in large single crystals (Fig. 1). Indeed, by considering large anhydrite crystals from the famous Naica Mine (“Cueva de los cristales”) we observed a suite of correlated self-similar void defects spanning multiple length-scales7 (Fig 2). These flaws, in the macroscopic crystal, stem from “seeds of imperfection” originating from a particle-mediated nucleation pathway. Hence, building a crystal could be viewed as Nature stacking blocks in a game of Tetris, whilst slowly forgetting the games core concept and failing to fill rows completely. T2 - Granada Münster Discussion Meeting (GMDM) CY - Granda, Spain DA - 30.11.2022 KW - Anhydrite KW - Mesocrystals KW - Calcium sulfate KW - Bassanite KW - Gypsum PY - 2022 AN - OPUS4-56476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz A1 - Van Driessche, A. T1 - Particle-mediated origins of mesocrystalline disorder in calcium sulfate single crystals N2 - Calcium sulfate minerals are abundant in natural and engineered environments and they exist in the form of three hydrates: gypsum (CaSO4·2H2O), bassanite (CaSO4·0.5H2O), and anhydrite (CaSO4). Due to their relevance in natural and industrial processes, the formation pathways of these calcium sulfate phases from aqueous solution have been the subject of intensive research1. The state-of-the-art of the calcium sulfate formation mechanisms builds upon and goes beyond what we have come to appreciate in the astounding intricacy of other mineral formation processes from ions in aqueous solutions. The original, and rather naive, 'textbook' image of these phenomena, stemming from the adaptation of classical nucleation and growth theories, has increased in complexity due to the discovery of a variety of precursor and intermediate species2. These include solute clusters (e.g. prenucleation clusters, PNCs), liquid(-like) phases, as well as amorphous and nanocrystalline solids etc.. In this context, a number of studies have already revealed that nucleation in the CaSO4-H2O system is non-classical, where the formation of the different crystalline phases involves several steps including a common amorphous precursor1, 3, 4. In this contribution we show that the formation of the amorphous phase involves the aggregation of small primary particles into larger disordered aggregates exhibiting a "brick-in-the-wall" structure5, 6. The actual crystallization occurs by the restructuring and coalescence of the particles ("bricks") into a given calcium sulfate phase depending on the physicochemical conditions of the solution. Importantly, the rearrangement process does not continue until a (nearly-)perfect homogeneous single crystal is obtained. Instead it comes to a stop, or at least significantly slows down. Such a process thus yields a final imperfect mesocrystal, composed of smaller domains rather than a continuous crystal structure, within which the domains are separated by an amorphous (i.e. less ordered) calcium sulfate phase. Hence, the non-classical crystallization process of CaSO4 yields a final imperfect mesocrystal with an overall morphology resembling that of a single crystal, yet composed of smaller nano-domains. Importantly, these observations reveal that organic-free calcium sulfate mesocrystals grown by a particle mediated-pathway preserve in the final crystal structure a “memory” or “imprint” of their non-classical nucleation process, something that has been overlooked until now. Furthermore, the nano-scale misalignment of the structural sub-units within these crystals can propagate through the length-scales, and be expressed macroscopically as misaligned zones/domains in large single crystals. Indeed, by considering large anhydrite crystals from the famous Naica Mine (“Cueva de los cristales”) we observed a suite of correlated self-similar void defects spanning multiple length-scales7. These flaws, in the macroscopic crystal, stem from “seeds of imperfection” originating from a particle-mediated nucleation pathway. Hence, building a crystal could be viewed as Nature stacking blocks in a game of Tetris, whilst slowly forgetting the games core concept and failing to fill rows completely. T2 - ECCG: European Conference on Crystal Growth 7 CY - Paris, France DA - 25.07.2022 KW - Anhydrite KW - SAXS KW - Single crystal KW - Mesocrystal PY - 2022 AN - OPUS4-56276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz A1 - Van Dreissche, A. T1 - Particle-mediated origins of mesocrystallinity in calcium sulfate single crystals N2 - Calcium sulfate minerals are abundant in natural and engineered environments in the form of three phases: gypsum (CaSO4·2H2O), bassanite (CaSO4·0.5H2O), and anhydrite (CaSO4). Due to their relevance in natural and industrial processes, the formation pathways of these phases from aqueous solution have been the subject of intensive research, a number of studies have already revealed that nucleation in the CaSO4-H2O system is non-classical, The formation of the different crystalline phases involves several steps including a common amorphous precursor. In this contribution we show that the formation of the amorphous phase involves the aggregation of small primary particles into larger disordered aggregates exhibiting a "brick-in-the-wall" structure. The actual crystallization occurs by the restructuring and coalescence of the "bricks" into a given calcium sulfate phase depending on the physicochemical conditions of the solution. Such a process yields a final imperfect mesocrystal, composed of smaller domains rather than a continuous single crystal structure. These observations reveal that organic-free calcium sulfate mesocrystals grown by a particle mediated-pathway might preserve in the final crystal structure an “imprint” of their growth pathways. Indeed, by considering large anhydrite crystals from the famous Naica Mine we observed a suite of correlated self-similar void defects spanning multiple length-scales. These flaws, in the macroscopic crystal, stem from “seeds of imperfection” originating from an original particle-mediated growth. Hence, building a crystal could be viewed as Nature stacking blocks in a game of Tetris, whilst slowly forgetting the games core concept and failing to fill rows completely. T2 - GeoMinKöln 2022 CY - Cologne, Germany DA - 11.09.2022 KW - Anhydrite KW - Mesocrystals KW - Calcium sulfate PY - 2022 AN - OPUS4-56277 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz T1 - Scattering is a powerful tool to follow nucleation and growth of minerals from solutions N2 - In recent years, we have come to appreciate the astounding intricacy of the formation process of minerals from ions in aqueous solutions. The original ‘textbook’ image o these phenomena, stemming from the adaptation of classical nucleation and growth theories, has increased in complexity due to the discovery of a variety of precursor and intermediate species [e.g. 1], including solute clusters (e.g. prenucleation clusters PNCs), liquid(-like) phases, as well as amorphous and nanocrystalline solids etc. In general, these precursor or intermediate species constitute different, often short-lived points along the pathway from dissolved ions to the final solids (typically crystals in this context). In this regard synchrotron-based scattering (SAXS/WAXS/HEXD appears to be the perfect tool to follow in situ and in a time-resolved manner the crystallization pathways because of the temporal and spatial length scales that can be directly accessed with these techniques. Here, I show how we used scattering to probe the crystallization mechanisms o calcium sulfate. CaSO4 minerals (i.e. gypsum, anhydrite and bassanite) are widespread in natural and industrial environments. During the last several years, a number o studies have revealed indeed that nucleation in the CaSO4-H2O system is non-classical My SAXS data demonstrate that gypsum precipitation, involves formation and aggregation of sub-3 nm primary species. These species constitute building blocks o an amorphous precursor phase [2]. Further, I show how in situ high-energy X-ray diffraction experiments and molecular dynamics (MD) simulations can be combined to derive the atomic structure of the primary CaSO4 clusters seen at small-angles [3]. fitted several plausible structures to the derived pair distribution functions and explored their dynamic properties using unbiased MD simulations based on polarizable force fields. Finally, based on combined SAXS/WAXS, broad-q-range measurements, show that the process of formation of bassanite, a less hydrated form of CaSO4, is very similar to the formation of gypsum: it also involves the aggregation of small primary species into larger disordered aggregates [4]. Based on these recent insights I formulated a tentative general model for calcium sulfate precipitation from solution. This model involves primary species that are formed through the assembly of multiple Ca2+ and SO42- ions into nanoclusters. These nanoclusters assemble into poorly ordered (i.e. amorphous) hydrated aggregates which in turn undergo ordering into coherent crystalline units of either gypsum o bassanite (and possibly anhydrite). Determination of the structure and (meta)stability of the primary species is important from both a fundamental, e.g. establishing a general non-classical nucleation model, and applied perspective; e.g. allow for an improved design of additives for greater control of the nucleation pathway T2 - BAM - Abteilungsseminar 6.3 CY - Online meeting DA - 21.02.2021 KW - Scattering KW - SAXS/WAXS KW - Calcium sulfate PY - 2021 AN - OPUS4-53713 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -