TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Donėlienė1, J. A1 - Rudzikas, M. A1 - Rades, Steffi A1 - Dörfel, Ilona A1 - Peplinski, Burkhard A1 - Sahre, Mario A1 - Pellegrino, F. A1 - Maurino, V. A1 - Ulbikas, J. A1 - Galdikas, A. T1 - Electron Microscopy and X-Ray Diffraction Analysis of Titanium Oxide Nanoparticles Synthesized by Pulsed Laser Ablation in Liquid N2 - A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation. T2 - Microscopy & Microanalysis 2018 CY - Baltimore, MD, USA DA - 05.08.2018 KW - Nanoparticles KW - Titanium oxide KW - Laser ablation in liquid KW - Electron microscopy KW - XRD PY - 2018 AN - OPUS4-46502 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hodoroaba, Vasile-Dan A1 - Yamamoto, K. A1 - Grulke, E. A. T1 - Size and shape distribution of bipyramidal TiO2 nanoparticles by transmission electron microscopy – an inter-laboratory comparison N2 - Extraction of true, 3D shape (and size) of non-spherical nanoparticles (NPs) is associated with errors by conventional 2D electron microscopy using projection images. Significant efforts within the ISO technical committee TC 229 ‘Nanotechnologies’ are aimed at establishing accurate TEM and SEM measurement of NP size and shape as robust, standard procedures. Study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated titania nano-powder for which size and shape distribution of primary crystallites of irregular shape must be measured accurately. To be noticed is e. g. the fact that the measurement procedure allows only manual selection of the particles clearly distinguishable for analysis as well as manual definition of the contour of the imaged NPs. An inter-laboratory exercise on titania NPs (pure anatase, grown by hydrothermal synthesis) of well-defined non-spherical shape, i.e. bipyramidal has been recently started within ISO/TC 229 under similar conditions as for the irregular shaped titania. Overlapped particles were allowed to be considered, as long as they are clearly distinguishable. One decisive NP selection criterion was to analyze only those NPs with a roundness value below 0.7, i.e. the NPs laying on the support foil and, hence, with projection areas clearly deviating from perfect circles (R=1). The overall evaluation (for 15 labs) of the size descriptors (area, Feret, minFeret, perimeter) and shape descriptors (aspect ratio, roundness, compactness, extent) by analysis of variance is just to be finished and included in ISO/WD 21363 Nanotechnologies -- Protocol for particle size distribution by transmission electron microscopy. KW - Nanoparticles KW - Electron microscopy KW - Titanium oxide KW - Particle size distribution PY - 2018 UR - https://www.cambridge.org/core/journals/microscopy-and-microanalysis/article/size-and-shape-distribution-of-bipyramidal-tich-nanoparticles-by-transmission-electron-microscopy-an-interlaboratory-comparison/9E2FA0C716DB5F881E3032D014DFD52B DO - https://doi.org/10.1017/S1431927618009017 SN - 1431-9276 SN - 1435-8115 VL - 24 IS - S1 (August 2018) SP - 1706 EP - 1707 PB - Cambridge University Press CY - New York, NY, U.S.A. AN - OPUS4-46005 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jakubowski, Norbert A1 - Müller, L. A1 - Traub, Heike A1 - Esteban-Fernández, D. A1 - Panne, Ulrich A1 - Wanka, Antje A1 - Kneipp, J. T1 - Method development for metal detection at cellular levels by ICP-MS N2 - An overview about different analytical approaches will be presented of how to detect metals in individual biological cells by use of ICP-MS. For this purpose, we are using different sample introduction systems for ICP-MS for detection, imaging and quantification of metals at cellular levels. By use of laser ablation, we have studied the up-take by and distribution of nanoparticles in single cells. Recently we have developed staining techniques to measure protein and DNA content of cells and identifying the cell status by immunoassays using metal-tagging of antibodies. New research based on cell arrays will be shortly discussed. Using pneumatic nebulization and microdroplet generation, we have also studied the up-take of nanoparticles and toxic metals as well as essential elements in single cells using different ICP-MS mass spectrometric concepts (sector field instrument, triple-quad instrument, time of flight (CyTOF) instrument). The different ICP-MS based methods will be compared concerning their analytical figures of merit and their strengths and weaknesses will be evaluated. T2 - Projektmeeting CY - Bremen, Germany DA - 18.04.2018 KW - Single cell ICP-MS KW - LA-ICP-MS with cellular resolution KW - Nanoparticles PY - 2018 AN - OPUS4-44851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jakubowski, Norbert A1 - Müller, L. A1 - Traub, Heike A1 - Esteban-Fernández, D. A1 - Panne, Ulrich A1 - Wanka, Antje A1 - Schellenberger, E. A1 - Theuring, F. A1 - Kneipp, J. T1 - Method development for metal detection at cellular levels by ICP-MS N2 - An overview about different analytical approaches will be presented of how to detect metals in individual biological cells by use of ICP-MS. For this purpose, we are using different sample introduction systems for ICP-MS for detection, imaging and quantification of metals at cellular levels. By use of laser ablation, we have studied the up-take by and distribution of nanoparticles in single cells. Recently we have developed staining techniques to measure protein and DNA content of cells and identifying the cell status by immunoassays using metal-tagging of antibodies. New research based on cell arrays will be shortly discussed. Using pneumatic nebulization and microdroplet generation, we have also studied the up-take of nanoparticles and toxic metals as well as essential elements in single cells using different ICP-MS mass spectrometric concepts (sector field instrument, triple-quad instrument, time of flight (CyTOF) instrument). The different ICP-MS based methods will be compared concerning their analytical figures of merit and their strengths and weaknesses will be evaluated. T2 - ACS Annual Meeting CY - New Orleans, LA, USA DA - 18.03.2018 KW - Single cell ICP-MS KW - LA-ICP-MS with cellular resolution KW - Nanoparticles PY - 2018 AN - OPUS4-44799 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jakubowski, Norbert A1 - Müller, L. A1 - Traub, Heike A1 - Esteban-Fernández, D. A1 - Panne, Ulrich A1 - Wanka, Antje A1 - Kneipp, J. T1 - Method development for metal detection at cellular levels by ICP-MS N2 - An overview about different analytical approaches will be presented of how to detect metals in individual biological cells by use of ICP-MS. For this purpose, we are using different sample introduction systems for ICP-MS for detection, imaging and quantification of metals at cellular levels. By use of laser ablation, we have studied the up-take by and distribution of nanoparticles in single cells. Recently we have developed staining techniques to measure protein and DNA content of cells and identifying the cell status by immunoassays using metal-tagging of antibodies. New research based on cell arrays will be shortly discussed. Using pneumatic nebulization and microdroplet generation, we have also studied the up-take of nanoparticles and toxic metals as well as essential elements in single cells using different ICP-MS mass spectrometric concepts (sector field instrument, triple-quad instrument, time of flight (CyTOF) instrument). The different ICP-MS based methods will be compared concerning their analytical figures of merit and their strengths and weaknesses will be evaluated. T2 - 16th Czech-Slovak Spectroscopic Conference CY - Luhacovice, Czech Republic DA - 27.05.2018 KW - Single cell analysis KW - ICP-MS KW - Nanoparticles PY - 2018 AN - OPUS4-45161 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kjaervik, Marit A1 - Dietrich, P. A1 - Thissen, A. A1 - Schwibbert, Karin A1 - Defedov, A. A1 - Wöll, C. A1 - Unger, Wolfgang T1 - Exploring the capabilities of NAP-XPS: Application to metal-organic frameworks, nanoparticles and biofilms N2 - Near-ambient pressure XPS makes it possible to characterise samples not compatible to ultra-high vacuum, and enables the study of liquid-solid, gas-liquid and gas-solid interfaces. NAP-XPS meas-urements of biofilms, suspended nanoparticles and metal-organic frameworks were performed with EnviroESCA developed by SPECS. An interesting application is surface characterisation of biofilms, which are bacterial communities embedded in a self-produced polysaccharide matrix. Various model systems ranging from pure polysaccharides of alginate to biofilms harvested directly from the growth medium have been char-acterised in humid conditions[1]. NAP-XPS also makes it possible to characterise nanoparticles in solution. Silver nanoparticles in aqueous solution were characterised and the Ag 3d-spectrum compared to spectra obtained of dried nanoparticles in UHV-conditions[2]. The binding energy of the Ag 3d-core level peak was shifted by 0,6 eV towards higher binding energy for suspended nanoparticles compared to the dried sample measured in UHV. This can be assigned to a change in surface potential at the water-nanoparticle interface. Metal-organic frameworks (MOFs) are suitable materials for gas storage of small molecules due to their nanoporous, crystalline structure. However, instability in humidity remains an issue for many types of MOFs. XPS-measurements of the MOF-structure HKUST-1 were performed in various NAP-conditions to assess the stability of the sample and its interaction with the gas molecules as water, methanol and pyridine. T2 - 5th AP-XPS Workshop CY - Berlin, Germany DA - 11.12.18 KW - Biofilms KW - E. coli KW - NAP-XPS KW - Metal organic frameworks KW - Nanoparticles PY - 2018 AN - OPUS4-47060 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kuchenbecker, Petra A1 - Hodoroaba, Vasile-Dan A1 - Lindemann, Franziska A1 - Gemeinert, Marion A1 - Wohlleben, W. T1 - Advanced screening method using volume-specific surface area (VSSA) for nanomaterial classification of powders N2 - The EU recommendation for a definition of nanomaterial (2011/696/EU) should allow the identification of a particulate nanomaterial based on the number-based metric criterion according to which at least 50% of the constituent particles have the smallest dimension between 1 and 100 nm. Within the European Project NanoDefine (www.nanodefine.eu) a two-tier approach has been developed, whereby firstly a screening method is applied for the rough classification as a nanomaterial or non-nanomaterial, and for borderline cases a confirmatory method (imaging methods or field flow fractionation) must be considered. One of the measurement methods well suited to particulate powder is the determination of volume-specific surface area (VSSA) by means of gas adsorption as well as skeletal density. The value of 60 m2/cm3 corresponding to spherical, monodisperse particles with a diameter of 100 nm constitutes the threshold for decisioning if the material is a nanomaterial or non-nanomaterial. The correct identification of a nanomaterial by VSSA method (positive test) is accepted by the EU recommendation. However, the application of the VSSA method is associated also by some limitations. The threshold of 60 m2/cm3 is dependent on the particle shape. For particles containing micro-pores or having a microporous coating, false positive results will be produced. Furthermore, broad particle size distributions – as typically for ceramic materials – as well as multi-modal size distributions make necessary to adjust the threshold. Based on examples of commercially available ceramic powders, the applicability of the VSSA approach will be tested (in relation with SEM and TEM measurements) in order to expand the actual knowledge and improve the method. T2 - Jahrestagung der Deutschen Keramischen Gesellschaft mit Symposium Hochleistungskeramik CY - München, Germany DA - 10.04.2018 KW - VSSA KW - Nanoparticles PY - 2018 AN - OPUS4-45097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kunz, Valentin A1 - Kjaervik, Marit A1 - Müller, Anja A1 - Hodoroaba, Vasile-Dan A1 - Unger, Wolfgang T1 - How to meet new challenges in advanced nanoparticle analytics N2 - Three current research projects performed at BAM’s Division for Surface Analysis and Interfacial Chemistry are presented that tackle important challenges with regard to the characterization of nanomaterials: 1) The characterization at ambient pressure, 2) the investigation of core-shell nanoparticles, and 3) the characterization of non-spherical particles by electron microscopy. 1) Surface analytical techniques such as Photoelectron Spectroscopy (XPS) or Secondary Ion Mass Spectrometry (SIMS) typically require measurements in ultra-high vacuum. However, for many applications (e.g. catalysis and nanotoxicology) it is important to know the surface chemical properties of nanomaterials at ambient conditions. Therefore, near-ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) was used to investigate nanoparticles in suspension. The used instrumental set-up allows to directly insert nanoparticle suspensions into the analysis chamber and to measure without prior sample preparation. Compared to dry reference samples measured under high-vacuum, a shift towards higher binding energies was observed for silver nanoparticles in water, indicating a change of surface potential at the water-nanoparticle interface. 2) To determine the dimensions of core-shell nanoparticles (shell thickness, core and total diameter), scanning transmission X-ray microscopy (STXM) was used. The analyzed model system consists of a polytetrafluorethylene (PTFE) core surrounded by a polystyrene (PS) shell, providing a strong X-ray absorption contrast at the C K-edge and a well-defined interface. The introduced STXM‐based methodology yields particle dimensions in agreement with scanning electron microscopy (SEM) results and provides additional information such as the position of the particle core, which cannot be extracted from a SEM micrograph. 3) The accurate measurement of size distributions of non-spherically shaped nanoparticles (representing most of the industrial nanoparticulate materials) is a challenging analytical task. High-resolution electron microscopy (TEM and SEM) is best suited to access the shape of individual nanoparticles. To fill the gap between ideal, monodisperse particles of spherical shape and complex real-world samples, BAM has started the work to develop reference nanoparticles of controlled shape, such as TiO2 platelets, bipyramids, and elongated particles. Results of a recent ISO inter-laboratory comparison will be shown with emphasis on the measurement parameters, descriptors and data analysis. T2 - NanoSafe Conference 2018 CY - Grenoble, France DA - 5.11.2018 KW - Nanoparticles PY - 2018 AN - OPUS4-46730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maurino, V. A1 - Hodoroaba, Vasile-Dan A1 - Pellutiè, L. A1 - Pellegrino, F. A1 - Ortel, Erik A1 - Isopescu, R. T1 - Synthesis of Shape controlled TiO2 N2 - Titanium dioxide is one of the most studied metal oxides due to its chemical, surface, electronic and (photo)catalytic properties, providing this material of multisectorial applications ranging from healthcare, photocatalysis, smart materials with self cleaning and self sterilizing properties and solar energy harvesting. However it is difficult to correlate the functional properties of TiO2 nanomaterials to the properties at single nanoparticle level due to the high polydispersity in shape, size and surface features of the currently available TiO2 nanoparticles (NPs). Although intensive experimental and theoretical studies have been conducted on the reactivity of different surfaces of metal oxides such as TiO2 much less attention is paid on the dependence of functional properties, like photocatalytic activity, dye adsorption, open circuit potential and fill factor in dye sensitized solar cells, on crystal facets in different orientations. One of the goal of SETNanoMetro project was the development of design rules to tune crystal facets of TiO2 NPs in order to optimize and control functional properties. In the present work we have developed a series of design rules in order to obtain sets of anatase TiO2 NPs with low polydispersity and to tune their shape and size by hydrothermal processing of Ti(IV)-Triethanolamine complex in presence of different shape controllers. Through a careful experimental design, a predictive soft model was developed. The model is able to predict the synthesis outcome allowing to tune the shape factor from 5 (prisms) to 1.5 (bipyramids) to 0.2 (platelets). This allows to control the main crystal facets exposed ranging from (100) to (001). Due to the dependence of functional properties of nanomaterials on shape distribution and not only size, the availability of NPs sets with uniform and well defined and tunable shapes can be of paramount relevance in order to produce reference nanomaterials for shape measurement. T2 - NanoWorkshop 2018 (Workshop on reference nanomaterials, current situation and needs: development, measurement, standardization) CY - Berlin, Germany DA - 14.05.2018 KW - Anatase KW - Shape control KW - Hydrothermal synthesis KW - Nanoparticles PY - 2018 AN - OPUS4-45634 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mino, L. A1 - Pellegrino, F. A1 - Rades, Steffi A1 - Radnik, Jörg A1 - Hodoroaba, Vasile-Dan A1 - Spotto, G. A1 - Maurino, V. A1 - Martra, G. T1 - Beyond shape engineering of TiO2 nanoparticles: Post-synthesis treatment dependence of surface hydration, hydroxylation, Lewis acidity and photocatalytic activity of TiO2 anatase nanoparticles with dominant {001} or {101} facets N2 - TiO2 anatase nanoparticles are among the relevant players in the field of light-responsive semiconductor nanomaterials used to face environmental and energy issues. In particular, shape-engineered TiO2 anatase nanosheets with dominant {001} basal facets gained momentum because of the possibility to exploit different and/or improved functional behaviors with respect to usual bipyramidal TiO2 anatase nanoparticles, mainly exposing {101} facets. Nevertheless, such behavior depends in a significant extent on the physicochemical features of surfaces exposed by nanosheets. They can vary in dependence on the presence or removal degree of capping agents, namely, fluorides, used for shape-engineering, and experimental investigations in this respect are still a few. Here we report on the evolution of interfacial/ surface features of TiO2 anatase nanosheets with dominant {001} facets from pristine nanoparticles fluorinated both in the bulk and at their surface to nanoparticles with F− free surfaces by treatment in a basic solution and to totally F− free nanoparticles by calcination at 873 K. The nanoparticles fluorine content and its subsequent evolution is determined by complementary techniques (ion chromatography, TOF-SIMS, XPS, AES, SEM-EDX), probing different depths. In parallel, the evolution of the electronic properties and the Ti valence state is monitored by UV−vis spectroscopy and XPS. The calcination treatment results in {001} facets poorly hydroxylated, hydrated, and hydrophilic, which appear as surface features consequent to the expected (1 × 4) reconstruction. Moreover, IR spectroscopy of CO adsorbed as probe molecule indicates that the Lewis acidity of Ti4+ sites exposed on (1 × 4) reconstructed {001} facets of calcined TiO2 nanosheets is weaker than that of cationic centers on {101} facets of bipyramidal TiO2 anatase nanoparticles. The samples have also been tested in phenol photodegradation highlighting that differences in surface hydration, hydroxylation, and Lewis acidity between TiO2 nanoparticles with nanosheet (freed by F− by calcination at 873 K) and bipyramidal shape have a strong impact on the photocatalytic activity that is found to be quite limited for the nanoparticles mainly exposing (1 × 4) reconstructed {001} facets. KW - Nanoparticles KW - TiO2 KW - F- doping KW - Shape-controlled nanoparticles KW - Nanosheets PY - 2018 DO - https://doi.org/10.1021/acsanm.8b01477 SN - 2574-0970 VL - 1 IS - 9 SP - 5355 EP - 5365 PB - ACS Publications CY - Washington, DC, U.S.A. AN - OPUS4-46157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -