TY - JOUR A1 - Schartel, Bernhard A1 - Balabanovich, Aliaksandr A1 - Braun, Ulrike A1 - Knoll, Uta A1 - Artner, J. A1 - Ciesielski, M. A1 - Döring, M. A1 - Perez, R. A1 - Sandler, J.K.W. A1 - Altstädt, V. A1 - Hoffmann, T. A1 - Pospiech, D. T1 - Pyrolysis of Epoxy Resins and Fire Behavior of Epoxy Resin Composites Flame-Retarded with 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide Additives N2 - The pyrolysis of an epoxy resin and the fire behavior of corresponding carbon fiber-reinforced composites, both flame-retarded with either 10-ethyl-9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide or 1,3,5-tris[2-(9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide-10-)ethyl]1, 3,5-triazine-2,4,6(1H,3H,5H)-trione, are investigated. The different fire retardancy mechanisms are discussed, and their influence on the fire properties assessed, in particular for flammability (limiting oxygen index, UL 94) and developing fires (cone calorimeter with different external heat fluxes of 35, 50, and 70 kW m-2). Adding the flame retardants containing 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide affects the fire behavior by both condensed phase and gas phase mechanisms. Interactions between the additives and the epoxy resin result in a change in the decomposition pathways and an increased char formation. The release of phosphorous products results in significant flame inhibition. The fire properties achieved are thus interesting with respect to industrial exploration. KW - Flame retardance KW - Thermosets KW - Composites KW - Thermogravimetric analysis (TGA) KW - Pyrolysis KW - High performance polymers KW - Epoxy resin PY - 2007 SN - 0021-8995 SN - 1097-4628 VL - 104 IS - 4 SP - 2260 EP - 2269 PB - Wiley InterScience CY - Hoboken, NJ AN - OPUS4-14573 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Braun, Ulrike A1 - Balabanovich, Aliaksandr A1 - Artner, J. A1 - Ciesielski, M. A1 - Döring, M. A1 - Perez, R.M. A1 - Sandler, J.K.W. A1 - Altstädt, V. T1 - Pyrolysis and fire behaviour of epoxy systems containing a novel 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide-(DOPO)-based diamino hardener N2 - Highly soluble 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide-(DOPO)-based diamino hardener (2), bearing its amino groups directly on the DOPO framework, is investigated with respect to its use as a reactive flame retardant in thermosets. A mechanism for decomposition of the corresponding phosphorus-modified epoxy resin system based on a diglycidylether of bisphenol A DGEBA and 2 (DGEBA/2) is proposed and compared to the systems using DGEBA and 4,4'-diaminodiphenylsulfon (DGEBA/DDS) and to a similar system based on the structurally comparable non-reactive DOPO-based compound (DGEBA/DDS/1). Additive 1 changed the decomposition characteristics of the epoxy resin only slightly and phosphorus was released. Incorporating 2 induces two-step decomposition and most of the phosphorus remains in the residue. Furthermore, the fire behaviour of neat epoxy resin systems and a representative carbon fibre-reinforced composite based on DGEBA, DDS and 2 (DGEBA/DDS/2) were examined and compared to that of the analogous composite systems based on DGEBA/DDS and DGEBA/DDS/1. Based on different flame retardancy mechanisms both the reactive compound 2 and the additive compound 1 improve flammability (increase in LOI >13% and achieving V-1 behaviour) of the epoxy resin and composites. Under forced flaming only the flame inhibition of the additive compound 1 acts sufficiently. Lastly, the superior key mechanical properties of the epoxy resin and composite based on 2 are sketched. KW - Decomposition KW - DOPO KW - Flame retardancy KW - Composites KW - Thermosets PY - 2008 DO - https://doi.org/10.1016/j.eurpolymj.2008.01.017 SN - 0014-3057 SN - 1873-1945 VL - 44 IS - 3 SP - 704 EP - 715 PB - Elsevier CY - Oxford AN - OPUS4-16708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Silbernagl, Dorothee A1 - Ghasem Zadeh Khorasani, Media A1 - Cano Murillo, Natalia A1 - Elert, Anna Maria A1 - Sturm, Heinz ED - Glatzel, T. T1 - Bulk chemical composition contrast from attractive forces in AFM force spectroscopy N2 - A key application of atomic force microscopy (AFM) is the measurement of physical properties at sub-micrometer resolution. Methods such as force–distance curves (FDCs) or dynamic variants (such as intermodulation AFM (ImAFM)) are able to measure mechanical properties (such as the local stiffness, kr) of nanoscopic heterogeneous materials. For a complete structure–property correlation, these mechanical measurements are considered to lack the ability to identify the chemical structure of the materials. In this study, the measured attractive force, Fattr, acting between the AFM tip and the sample is shown to be an independent measurement for the local chemical composition and hence a complete structure–property correlation can be obtained. A proof of concept is provided by two model samples comprised of (1) epoxy/polycarbonate and (2) epoxy/boehmite. The preparation of the model samples allowed for the assignment of material phases based on AFM topography. Additional chemical characterization on the nanoscale is performed by an AFM/infrared-spectroscopy hybrid method. Mechanical properties (kr) and attractive forces (Fattr) are calculated and a structure–property correlation is obtained by a manual principle component analysis (mPCA) from a kr/Fattr diagram. A third sample comprised of (3) epoxy/polycarbonate/boehmite is measured by ImAFM. The measurement of a 2 × 2 µm cross section yields 128 × 128 force curves which are successfully evaluated by a kr/Fattr diagram and the nanoscopic heterogeneity of the sample is determined. KW - AFM force spectroscopy KW - Composites KW - Principle component analysis KW - Structure–property correlation KW - Van der Waals forces PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520175 DO - https://doi.org/10.3762/bjnano.12.5 SN - 2190-4286 VL - 12 IS - 5 SP - 58 EP - 71 PB - Beilstein Institute CY - Frankfurt am Main AN - OPUS4-52017 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stark, Wolfgang A1 - Jaunich, Matthias A1 - Mc Hugh, Jarlath T1 - Dynamic mechanical analysis (DMA) of epoxy carbon-fibre prepregs partially cured in a discontinued autoclave analogue process N2 - Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E', loss modulus E' and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures. KW - Composites KW - Epoxy KW - Cross-linking KW - Prepreg KW - Degree of cure KW - Glass transition PY - 2015 DO - https://doi.org/10.1016/j.polymertesting.2014.11.004 SN - 0142-9418 VL - 41 SP - 140 EP - 148 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-32325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sturm, Heinz A1 - Schulz, Eckhard T1 - Local AC current contrast on carbon fiber surfaces imaged by scanning force microscopy N2 - After a delamination process in a C-fiber reinforced polymer composite, the identification of the polymer residue of poly-(phenylene sulphide) on carbon fiber surfaces gives important information on the composite failure mechanism. Using scanning force microscopy (SFM) in its lateral force imaging mode or with the stiffness imaging mode, it is almost impossible to distinguish the two composite components owing to a very low material-based contrast of the local friction and compliance. The new technique using contrast based on a local AC current measurement allows a clear identification of the conducting carbon fiber and the non-conducting polymer coverage. KW - Matrix adhesion KW - Films KW - Photoconduction KW - Composites PY - 1995 DO - https://doi.org/10.1002/actp.1995.010460505 SN - 0323-7648 SN - 1521-4044 VL - 46 IS - 5 SP - 379 EP - 384 PB - Wiley-VCH Verl. CY - Weinheim, Germany AN - OPUS4-6848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sunder, S. A1 - Jauregui Rozo, Maria A1 - Deshpande, H. A1 - Neyer, A. A1 - Papaiya, V. A1 - Meinel, Dietmar A1 - Schartel, Bernhard A1 - Ruckdäschel, H. T1 - Char to the Rescue: Processing and Transfer of Flame-Retardant Epoxy Resins, Adjusting the Fire Behavior and Post-Fire Structural Integrity of Glass Fiber Composites N2 - Epoxy (EP) glass fiber reinforced composites (GFRCs) are extensively used in structural applications due to their excellent thermal and mechanical properties, but their inherent flammability limits fire-safe deployment. While numerous studies examine the flame retardancy of resins or individual composite systems, comprehensive studies evaluating simultaneous improvements in flame retardancy and post-fire mechanical integrity, specifically through prepreg processing, remain challenging. This study investigates the effectiveness and transferability of phosphorus-based flame retardant (FR) systems to diglycidyl ether of bisphenol A (DGEBA) and EP novolac resin matrices and their corresponding bidirectional glass fiber composites via prepregs. The FRs are chosen based on varying modes of action: ammonium polyphosphate with inorganic silicate (APP/InSi) primarily acts in the condensed phase (CP), and aluminum diethyl phosphinate with zinc hydroxystannate (AldietPO2/ZHS) is known to demonstrate both gas-phase (GP) and CP activity. Fire residues are tailored to compensate for structural defects from fire exposure. EP novolac, with higher aromaticity and cross-linking, possesses better inherent flame resistance compared to DGEBA. The novolac composites containing AldietPO2/ZHS simultaneously showed the highest retention of flexural properties after fire exposure and the best fire safety index. The experimental values of the post-fire flexural properties in the composites calibrated damage parameters in two theoretical models. KW - Composites KW - DGEBA KW - Epoxy novolac KW - Post-fire KW - Prepregs PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-643752 DO - https://doi.org/10.1002/pol.20250692 SN - 2642-4169 SN - 2642-4150 VL - 63 IS - 20 SP - 4295 EP - 4309 PB - Wiley AN - OPUS4-64375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sunder, S. A1 - Jauregui Rozo, Maria A1 - Inasu, S. A1 - Schartel, Bernhard A1 - Ruckdäschel, H. T1 - Investigating the changing dynamics of processing, temperature-based mechanics, and flame retardancy in the transfer of ammonium polyphosphate/inorganic silicate flame retardants from epoxy resins to glass fiber composites N2 - Although numerous investigations study the improvement of flame retardancy of epoxy resins using additives, maintaining the flame retardant (FRs) modes of action present in the resins upon transfer to composites is challenging. In this study, ammonium polyphosphate (APP) and inorganic silicate (InSi) are loaded at 10%, 30%, and 50% by weight, in a diglycidyl ether of bisphenol A (DGEBA) resin cured with dicyandiamide and transferred to bidirectional (BD) glass fiber (GF) composites. Although a 50% loading of the FRs impacts the curing kinetics of the resin system, the effect on the glass transition temperature of the resin system remains negligible compared to reactive FRs in the state of the art integrated into the resin's chemical structure. Increasing the FR content improved the heat release characteristics in both the resins and composites. However, the charring mode of action is completely suppressed in the formulation with 10% APP + InSi. A 30% concentration of the FRs restored the charring action in the composite and the GFs provide increased protective layer action upon transfer to the composites. This study highlights the importance of accounting for the changing dynamics related to processing and flame retardancy upon transferring FRs from resins to composites. KW - Composites KW - Flame retardance KW - Resins KW - Synthesis and processing techniques PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610484 DO - https://doi.org/10.1002/app.55988 SN - 1097-4628 VL - 141 IS - 39 SP - 1 EP - 18 PB - Wiley CY - New York, NY AN - OPUS4-61048 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sypaseuth, Fanni D. A1 - Gallo, Emanuela A1 - Çiftci, Serhat A1 - Schartel, Bernhard T1 - Polylactic acid biocomposites: approaches to a completely green flame retarded polymer N2 - Basic paths towards fully green flame retarded kenaf fiber reinforced polylactic acid (K-PLA) biocomposites are compared. Multicomponent flame retardant Systems are investigated using an amount of 20 wt% such as Mg(OH)2 (MH), ammonium polyphosphate (APP) and expandable graphite (EG), and combinations with Silicon dioxide or layered silicate (LS) nanofillers. Adding Kenaf fibers and flame retardants increases the E modulus up to a factor 2, although no compatibilizer was used at all. Thus, in particular adding EG and MH decreases the strength at maximum elongation, and kenaf fibers, MH, and EG are crucial for reducing the elongation to break. The Oxygen index is improved by up to 33 vol% compared to 17 vol% for K-PLA. The HB classification of K-PLA in the UL 94 test is outperformed. All flame retarded biocomposites show somewhat lower thermal stability and increased amounts of residue. MH decreases the fire load significantly, and the greatest reduction in peak heat release rate is obtained for K-PLA/15MH/5LS. Synergistic effects are observed between EG and APP (ratio 2:1) in flammability and fire properties. Synergistic multicomponent systems containing EG and APP, or MH with adjuvants offer a promising route to green flame retarded natural fiber reinforced PLA biocomposites. KW - Biopolymers KW - Composites KW - Flame retardance KW - Natural fibres KW - Thermal decomposition PY - 2017 DO - https://doi.org/10.1515/epoly-2017-0024 SN - 2197-4586 SN - 1618-7229 VL - 17 IS - 6 SP - 449 EP - 462 PB - De Gruyter AN - OPUS4-42872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tabaka, Weronika A1 - Schartel, Bernhard T1 - Less is More: Optimised Fire Performance in Glass Fibre-reinforced Polybutylene Terephthalate Laminates with Concentrated Flame Retardant Top Layer N2 - To achieve optimum fire performance while maintaining mechanical integrity, flame retardants (FR) were strategically concentrated in the surface layer of a two-layer glass fibre-reinforced polybutylene terephthalate (PBT) laminate structure. Three potentially synergistic FR systems were selected to improve the fire performance of glass fibre-reinforced PBT: boehmite (AlOOH) with melamine polyzinc phosphate (MPZnP), aluminium diethyl phosphinates (AlPi) with melamine cyanurate (MC), and expandable graphite (EG) with melamine polyphosphate (MPP). Limited Oxygen Index (LOI) and UL-94 testing highlighted the influence of laminate architecture on flammability. The cone calorimeter results showed that increasing the FR concentration in the top layer significantly reduced both the peak heat release rate (PHRR) and the maximum average rate of heat emission (MARHE), with improvements depending on the specific FR system used. The laminate L-PBT/GF/AlOOH/MPZnP with a 2:2 thickness ratio showed outstanding performance, achieving a 45 % reduction in MARHE compared to composites with uniform FR distribution. This result showcases the superior thermal barrier properties and synergistic behaviour of AlOOH and MPZnP. The fire performance of laminates containing AlPi and MC was strongly influenced by the distribution and concentration of AlPi/MC. The EG/MPP system was found to be highly effective, forming a protective intumescent layer that significantly reduced both HRR and MARHE, demonstrating the effectiveness of strategically concentrating FR in the top layer. KW - Glass fibres KW - PBT KW - Flame retardants KW - Composites KW - Laminates KW - Fire behaviour KW - Flammability PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-626381 DO - https://doi.org/10.1016/j.jcomc.2025.100577 SN - 2666-6820 VL - 16 SP - 1 EP - 15 PB - Elsevier CY - Amsterdam AN - OPUS4-62638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - Comparison of the sliding behavior of several polymers in gaseous and liquid hydrogen N2 - The development of hydrogen technologies entails high safety requirements in distribution and dispensing infrastructure. Therefore, it is necessary to pursue research on material compatibility in hydrogen, especially for critical parts with tribological issues. The focus of this study is to evaluate the influence of hydrogen on a wider range of commercially available polymer materials. Thereby, the friction and wear behavior of different grades of TPE, POM, PA66, PA12, PPA, PEEK, PPS, PTFE, PAI, PI and PBI were investigated against a rotating steel disk (AISI 304). Filled and unfilled polymers from different suppliers were evaluated at room temperature in air, vacuum and hydrogen gas (H2) as well as in liquid hydrogen at - 253°C (LH2). The sliding behavior of the polymer materials is discussed by means of surface analyses, whereby special attention is paid to the formation of a transfer film. According to the results at ambient temperature, the effect of hydrogen environment on the tribological behavior of neat polymers may be related to lack of moisture, but also to saturated hydrocarbons in gaseous hydrogen. In liquid hydrogen, the best tribological performances were achieved with neat PA polymers as well as PPS and PI composites. KW - Polymers KW - Composites KW - Sliding wear KW - Hydrogen KW - Cryogenic temperature PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597123 DO - https://doi.org/10.2474/trol.18.217 SN - 1881-2198 VL - 18 IS - 5 SP - 217 EP - 231 PB - Japanese Society of Tribologists AN - OPUS4-59712 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -