TY - CONF A1 - Straße, Anne A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Preliminary study to investigate the applicability of optical strain measurement technique for the detection of hot cracks in laser metal deposited layers N2 - Laser metal deposition (LMD) as an additive manufacturing technique became increasingly important in recent years and thus the demand for component safety. This is the reason, for the need for reliable in-situ defect detection techniques. For laser beam weld seams an optical measurement technique based on an optical flow algorithm was successfully used to define the critical straining conditions that lead to hot cracking. This algorithm was adapted for bead-on-plate weld seams on LMD deposited layers of IN718 alloy while performing external strain on the specimen in an externally loaded hot cacking test facility. The resulting transversal hot cracks along the weld seam were localized via X-Ray inspection and the type of cracking confirmed by Scanning Electron Microscopy (SEM). The strain distribution was measured in the vicinity of the solidification front and correlated to the detected hot cracks. Based on the results this technique could be adopted for LMD experiments. T2 - 12th CIRP Conference on Photonic Technologies [LANE 2022] CY - Fürth, Germany DA - 04.09.2022 KW - Strain measurement KW - Optical flow KW - Laser Metal Deposition (LMD) KW - Critical strain PY - 2022 AN - OPUS4-55642 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - LMD coatings as filler material for laser beam welded 30 mm thick plates N2 - The development of high energy laser sources enables single-pass welds of thick plates up to 30 mm, but often additional materials are needed to influence the properties of the weld seams. However, the homogenous distribution of filler materials in form of e.g. electrodes is only possible up to 7 mm while the elements are only traceable up to a depth of 14 mm. To overcome this problem a two-step process is used where first the edges of the weld partners are coated with the filler material by laser metal deposition (LMD) and afterwards are welded by laser beam. Single-pass welds with electromagnetic weld pool support of 30 mm thick S355 J2+N-plates with austenitic AISI 316L-coatings were investigated as well as the influence of the coatings to the penetration depth of the laser beam without electromagnetic weld pool support in double-sided joints. The weld seams were tested by X-ray inspection and cross sections. T2 - 11th CIRP Conference on Photonic Technologies [LANE 2020] CY - Online meeting DA - 07.09.2020 KW - Penetration depth KW - Laser metal deposition (LMD) KW - Laser beam welding KW - Filler material distribution PY - 2020 AN - OPUS4-51276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Quality improvement of laser welds on thick duplex plates by laser cladded buttering N2 - Because of its excellent corrosion resistance, high tensile strength and high ductility, duplex stainless steel 2205 offers many areas of application. Though laser beam welding accompanied by high cooling rates, duplex steels tend to perform higher ferrite contents in weld metal as the base metal, which leads to a reduction of ductility and corrosion resistance of the weld joint. To overcome this problem, a solution, based on buttering the plate edges by laser metal deposition (LMD) with material containing higher Ni concentrations prior to laser welding was suggested. In this context different process parameters for LMD and different mixtures of duplex and nickel powder, were investigated. In a second step the possibility of welding those edges defect free while achieving balanced austenite-ferrite ratio was verified with metallographic analysis, Electron Backscatter Diffraction (EBSD) and impact testing according to Charpy. The improved corrosion resistance was observed with ASTM G48 standard test method. T2 - Lasers in Manufacturing- LiM 2019 CY - Munich, Germany DA - 24.07.2019 KW - Stainless Steel KW - Laser Metal Deposition KW - Laser Beam Welding KW - Duplex PY - 2019 AN - OPUS4-49365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of cladded buffering on thick duplex plates for laser welding N2 - Because of its excellent corrosion resistance, a high tensile strength together with a high ductility, duplex stainless steel 2205 offers many areas of application in the chemical and the offshore industry, to name just two. Though welding, especially laser beam welding accompanied by high cooling rates, duplex steels tend to perform higher ferrite contents in weld metal upon cooling down from melting temperature as the base metal. This trend leads to a reduction of the ductility as well as the corrosion resistance of the weld joint. To overcome this problem a solution, based on buffering the plate edges by laser metal deposition with material containing higher Ni concentrations prior to the laser welding was suggested. This method offers more benefits in comparison to conventional usage of higher Ni-alloyed filler wire due to the better control over Ni-distribution in the weld seam, resulting in balanced austenite- ferrite ratio everywhere in the weld metal. In this context different mixtures of duplex and nickel powder were investigated as well as different process parameters, that enable a smooth surface structure with slightly reduced ferrite contents. In a second step the possibility of welding those edges defect free with standard parameters while achieving balanced austenite- ferrite ratio was verified with metallographic analysis of the microstructure, Electron Backscatter Diffraction (EBSD) and impact testing according to Charpy. The improved corrosion resistance of the welds in comparison to unbuffered ones was observed with the ASTM G48 standard test method. T2 - IIW 2019 CY - Bratislava, Slowakia DA - 07.07.2019 KW - Stainless Steel KW - Laser Metal Deposition KW - Laser Beam Welding KW - Duplex PY - 2019 AN - OPUS4-49366 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Stankevich, Stanislav A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Measurement of thermal cycle and layer hight at multi-pass build-up during LMD-Process N2 - The shape of the parts, created by the technology of laser metal deposition (LMD), is influenced by various parameters, for example, the power and diameter of the laser source spot. The contribution of energy from the laser affects the temperature distribution in the formed layers. The changing temperature in the working area entails a change in the geometry of the layers and affects the stability of the process. In this paper, experiments on the measurement of temperature cycles in the DLMD process with different directions of the filling track are carried out. An infrared camera was used to measure thermal cycles. The calibration of the acquired data (i.e. correspondence table between the intensity of thermal radiation of the material and the absolute temperature) was done with help of two-color pyrometer ex situ and in situ measurements. The experiments are carried out on two materials 316L and Inconel 718. The effect of the maximum temperature on the layer height is shown, and thermal cycles in the formation of layers for different filling strategies are presented. T2 - 1st Workshop on in-situ Monitoring and Microstructure Development in Additive Manufacturing CY - Online meeting DA - 11.12.2020 KW - Laser metal deposition KW - AISI 316L KW - Alloy 718 KW - Thermography PY - 2020 AN - OPUS4-51816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Nahteigenschaftsverbesserung von dickwandigen Laserstrahlgeschweißten Duplexblechen mittels pulveraufgetragenen Pufferschichten N2 - Der Duplexstahl 2205 bietet aufgrund seiner guten Korrosionsbeständigkeit und der hohen erreichbaren Festigkeitswerte bei guter Duktilität, zahlreiche Anwendungsmöglichkeiten. Jedoch wurde beim Schweißen von Duplexstählen eine Verschiebung des Gleichgewichts zwischen Austenit- und Ferritanteil hin zu höheren Ferritgehalten und damit negativen mechanischen und Korrosionseigenschaften beobachtet. Um diesem Umstand entgegenzuwirken, werden häufig spezielle Schweißzusätze mit höheren Nickelanteilen genutzt, welche bei dickwandigen Strukturen jedoch nicht über die gesamte Schweißnahttiefe nachgewiesen werden können. Dies führt zu unterschiedlichen Eigenschaften und einer höheren Korrosionsanfälligkeit im Wurzelbereich. Eine Möglichkeit die gleichmäßige Verteilung von Legierungselementen innerhalb der Naht zu gewährleisten, bietet die Erzeugung von Pufferschichten mittels Laser-Pulver-Auftragschweißen (LPA). In diesem Zusammenhang wurden Duplexpulver mit unterschiedlichen Nickelgehalten und verschiedene LPA-Prozessparameter untersucht, die eine ebene Schichtbildung mit verringerten Ferritgehalten ermöglichen. In einem zweiten Schritt konnte nachgewiesen werden, dass das Laserstrahlschweißen der beschichteten Kanten bei üblichen Prozessparametern möglich ist und zu fehlerfreien Schweißnähten mit ausgeglichenem austenitisch- ferritischem Gefüge führt. Der Einfluss unterschiedlicher Schutzgase und verschiedener Nickelgehalte auf die Gefügestruktur wurde für die Beschichtungen und Laserstrahlschweißungen mit Hilfe von Schliffbildern und Electron Backscatter Diffraction (EBSD) ausgewertet, wobei gezeigt werden konnte, dass bei ausreichend hohem Nickelgehalt ein feinkörniges Gefüge sowohl in der Pufferschicht als auch der Schweißnaht vorliegt. Die Korrosionsbeständigkeit der Schweißnähte wurde durch Korrosionsuntersuchungen überprüft. T2 - WerkstoffWoche 2019 CY - Dresden, Germany DA - 18.09.2019 KW - LPA KW - Duplex KW - Pufferschichten PY - 2019 AN - OPUS4-49656 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Nahteigenschaftsverbesserung von dickwandigen laserstrahlgeschweißten Duplexblechen mittels pulveraufgetragenen Pufferschichten N2 - Der Duplexstahl 2205 bietet aufgrund seiner guten Korrosionsbeständigkeit und der hohen erreichbaren Festigkeitswerte bei guter Duktilität, zahlreiche Anwendungsmöglichkeiten. Jedoch wurde beim Schweißen von Duplexstählen eine Verschiebung des Gleichgewichts zwischen Austenit- und Ferritanteil hin zu höheren Ferritgehalten und damit negativen mechanischen und Korrosionseigenschaften beobachtet. Um diesem Umstand entgegenzuwirken, werden häufig spezielle Schweißzusätze mit höheren Nickelanteilen genutzt, welche bei dickwandigen Strukturen jedoch nicht über die gesamte Schweißnahttiefe nachgewiesen werden können. Dies führt zu unterschiedlichen Eigenschaften und einer höheren Korrosionsanfälligkeit im Wurzelbereich. Eine Möglichkeit die gleichmäßige Verteilung von Legierungselementen innerhalb der Naht zu gewährleisten, bietet die Erzeugung von Pufferschichten mittels Laser-Pulver-Auftragschweißen (LPA). In diesem Zusammenhang wurden Duplexpulver mit unterschiedlichen Nickelgehalten und verschiedene LPA-Prozessparameter untersucht, die eine ebene Schichtbildung mit verringerten Ferritgehalten ermöglichen. In einem zweiten Schritt konnte nachgewiesen werden, dass das Laserstrahlschweißen der beschichteten Kanten bei üblichen Prozessparametern möglich ist und zu fehlerfreien Schweißnähten mit ausgeglichenem austenitisch- ferritischem Gefüge führt. Der Einfluss unterschiedlicher Schutzgase und verschiedener Nickelgehalte auf die Gefügestruktur wurde für die Beschichtungen und Laserstrahlschweißungen mit Hilfe von Schliffbildern und Electron Backscatter Diffraction (EBSD) ausgewertet, wobei gezeigt werden konnte, dass bei ausreichend hohem Nickelgehalt ein feinkörniges Gefüge sowohl in der Pufferschicht als auch der Schweißnaht vorliegt. Die Korrosionsbeständigkeit der Schweißnähte wurde durch Korrosionsuntersuchungen überprüft. T2 - 40. Assistentenseminar der Füge- und Schweißtechnik, WGF (Wissenschaftliche Gesellschaft Fügetechnik) CY - Braunlage, Germany DA - 25.09.2019 KW - LPA KW - Pufferschichten KW - Duplex PY - 2019 AN - OPUS4-49658 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Scheuschner, Nils A1 - Altenburg, Simon A1 - Pignatelli, Giuseppe A1 - Baensch, Franziska A1 - Gornushkin, Igor B. A1 - Meierhofer, Christiane A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - In-situ Prozessüberwachung beim Laser-Pulver-Auftragschweißen (LPA) mittels Thermographie, optischer Emissionsspektroskopie (OES) und Schallemission (AE) N2 - In diesem Vortrag wird ein Überblick über die in-situ Messverfahren gegeben, die im Rahmen des Projektes ProMoAM an der LPA- Anlage eingesetzt wurden. Im Speziellen sind das die Thermographie, die optische Emissionsspektroskopie (OES) und die Akustische Emission (AE). T2 - 41. Assistentenseminar der WGF e.V. CY - Online meeting DA - 02.09.2020 KW - Schallemission KW - Laser-Pulver-Auftragschweißen KW - Thermographie KW - Optische Emissionsspektroskopie PY - 2020 AN - OPUS4-51273 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -