TY - JOUR A1 - Stark, Wolfgang T1 - Investigation of curing behaviour of melamine/phenolic (MP) thermosets JF - Polymer testing N2 - Commercially available melamine/phenolic (MP) moulding compounds used for manufacturing electro installation parts were investigated by laboratory thermal analysis methods: Dynamic Mechanical Analysis (DMA), Differential Scanning Calorimetry (DSC) and Dielectric Analysis (DEA). The results were compared with on-line measurements in a compression mould using incorporated dielectric and ultrasound sensors. Softening and cross-linking behaviour were analyzed. For on-line process monitoring, only the ultrasound method worked well. The dielectric method was distorted by water formed as a by-product from the poly-condensation reaction. KW - Thermoset KW - Melamine KW - Phenol KW - Moulding compound KW - Cross-linking KW - DSC PY - 2010 DO - https://doi.org/10.1016/j.polymertesting.2010.05.008 SN - 0142-9418 VL - 29 IS - 6 SP - 723 EP - 728 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-20982 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stark, Wolfgang A1 - Bartusch, Jürgen A1 - Döring, Joachim A1 - Mc Hugh, Jarlath T1 - Making cure visible: monitoring the crosslinking process using integrated ultrasound sensors JF - JEC Composites Magazine N2 - A special ultrasonic measuring system was developed to monitor the cross-linking process, enabling interaction with the manufacturing process in order to optimise part quality and reduce cycle times. KW - Thermoset KW - Ultrasound sensors KW - Mould KW - Rtm KW - Gelation KW - Vitrification PY - 2008 SN - 1639-965X IS - 38 SP - 64 EP - 66 PB - JEC CY - Paris AN - OPUS4-18610 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stark, Wolfgang A1 - Goering, Harald A1 - Michel, U. A1 - Bayerl, H. T1 - Online monitoring of thermoset post-curing by dynamic mechanical thermal analysis DMTA JF - Polymer testing N2 - Thermosetting moulding compounds are synthetic materials which can be easily formed in the molten state and achieve high temperature stability due to a cross-linking process which takes place during manufacture. To ensure thermal and mechanical properties, post-curing of moulded phenolic resin components is necessary for high quality applications. In the industrial practice, post-curing time-temperature-programs are heuristically acquired. In this paper, dynamical mechanical thermal analysis is employed to determine optimal post-curing conditions for injection moulded parts from phenolic resin. KW - DMTA KW - Moulding compound KW - Thermoset KW - Phenolic resin KW - Post-curing PY - 2009 DO - https://doi.org/10.1016/j.polymertesting.2009.02.005 SN - 0142-9418 VL - 28 IS - 6 SP - 561 EP - 566 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-19822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tang, S. A1 - Wachtendorf, Volker A1 - Klack, Patrick A1 - Qian, Lijun A1 - Dong, Y. A1 - Schartel, Bernhard T1 - Enhanced flame-retardant effect of montmorillonite/phosphaphenanthrene compound in an epoxy thermoset JF - RSC Advances N2 - A phosphaphenanthrene and triazinetrione group containing flame retardant (TAD) is combined with organically modified montmorillonite (OMMT) in epoxy resin thermosets (EP) to improve the performance of the flame-retardant system. When only 1 wt% OMMT/4 wt% TAD is introduced into the EP, the limited oxygen index (LOI) rises from 26% to 36.9% and a V-0 rating is achieved in a UL 94 test. The decomposition and pyrolysis products in the gas phase and condensed phase were characterized using thermogravimetry-Fourier transform infrared spectroscopy (TG-FTIR). The influence on the decomposition of EP, such as the increase in char yield, is limited with the incorporation of OMMT; a large amount of the phosphorus is released into the gas phase. The flame-retardant effect evaluation based on cone calorimeter data testified that OMMT improves the protective-barrier effect of the fire residue of OMMT/TAD/EP on the macroscopic scale, while TAD mainly causes flame inhibition. The fire residues showed a corresponding macroscopic appearance (digital photo) and microstructure (scanning electron microscope [SEM] results). The protective barrier effect of OMMT and the flame-inhibition effect of TAD combined to exert a superior flame-retardant effect, resulting in sufficient flame-retardant performance of OMMT/TAD/EP KW - Flame retardant KW - Nanocomposite KW - DOPO KW - Thermoset KW - Epoxy resin KW - TG-FTIR PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388865 DO - https://doi.org/10.1039/c6ra25070j SN - 2046-2069 VL - 7 IS - 2 SP - 720 EP - 728 AN - OPUS4-38886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -