TY - JOUR A1 - Jürgens, Maria A1 - Sonntag, Nadja A1 - Olbricht, Jürgen A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - The effect of dwell times on the thermomechanical fatigue life performance of grade P92 steel at intermediate and low strain amplitudes JF - Materials Science and Engineering: A N2 - Results of an extended TMF test program on grade P92 steel in the temperature range of 620 °C - 300 °C, comprising in-phase (IP) and out-of-phase (OP) tests, partly performed with symmetric dwells at Tmax/Tmin, are presented. In contrast to previous studies, the low-strain regime is also illuminated, which approaches flexible operation in a power plant with start/stop cycles. At all strain amplitudes, the material performance is characterized by continuous cyclic softening, which is retarded in tests at lower strains but reaches similar magnitudes in the course of testing. In the investigated temperature range, the phase angle does not affect fatigue life in continuous experiments, whereas the IP condition is more detrimental in tests with dwells. Fractographic analyses indicate creep-dominated and fatigue-dominated damage for IP and OP, respectively. Analyses of the (micro)hardness distribution in the tested specimens suggest an enhanced microstructural softening in tests with dwell times for the low- but not for the high-strain regime. To rationalize the obtained fatigue data, the fracture-mechanics-based D_TMF concept, which was developed for TMF life assessment of ductile alloys, was applied. It is found that the D_TMF parameter correlates well with the measured fatigue lives, suggesting that subcritical growth of cracks (with sizes from a few microns to a few millimeters) governs failure in the investigated range of strain amplitudes. KW - 9-12%Cr steel KW - Thermomechanical fatigue KW - Symmetric dwell periods KW - Low strain KW - Parametric modeling PY - 2021 DO - https://doi.org/10.1016/j.msea.2020.140593 VL - 805 SP - 140593 PB - Elsevier B.V. AN - OPUS4-52374 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Thermomechanical fatigue of heat-resistant austenitic cast iron EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S) JF - International journal of fatigue N2 - TMF tests were carried out on EN-GJSA-XNiSiCr35-5-2 at constant minimum temperature (400 °C) and varying maximum temperatures (Tmax = 700 °C, 800 °C, 900 °C) with hold times of 180 s at Tmax and two phase angles (in-phase (IP), 180° out-of-phase (OP)). The results showed a comparable strength under OP- and IP-TMF loading. At Tmax = 700 °C and 900 °C, the lifetime in IP-tests was slightly longer than that of OP-tests, while it is vice versa at Tmax = 800 °C. The IP-tests at Tmax = 900 °C showed a similar lifetime as OP-tests at Tmax = 700 °C and 800 °C, which was unexpected for such a high testing temperature. All IP-tests at Tmax = 900 °C showed a continuous cyclic softening from the beginning on, which was different from all other testing conditions. Complementary metallographic investigations indicated that under this test condition, intergranular creep damage is present in the volume of the test pieces. T2 - 3rd International Workshop on Thermo-Mechanical Fatigue (TMF-Workshop 2016) CY - Berlin, Germany DA - 27.04.2016 KW - Cast iron KW - Cracks KW - Cyclic softening KW - Microscopy KW - Thermomechanical fatigue PY - 2017 DO - https://doi.org/10.1016/j.ijfatigue.2017.01.009 SN - 0142-1123 SN - 1879-3452 VL - 99 IS - 2 (Special issue: Recent developments in thermo-mechanical fatigue) SP - 295 EP - 302 PB - Elsevier CY - Oxford AN - OPUS4-39680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -