TY - JOUR A1 - Ayerdi, J. J. A1 - Aginagalde, A. A1 - Llavori, I. A1 - Bonse, Jörn A1 - Spaltmann, Dirk A1 - Zabala, A. T1 - Ball-on-flat linear reciprocating tests: Critical assessment of wear volume determination methods and suggested improvements for ASTM JF - Wear N2 - In the present work it was shown the importance of the correct selection, implementation, and reporting of wear volume computation method and quanitifies the potential errors. KW - Wear KW - Sliding KW - Surface KW - Analysis KW - ASTM KW - D7755-11 PY - 2021 DO - https://doi.org/10.1016/j.wear.2021.203620 VL - 470-471 SP - 3620 AN - OPUS4-52080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Reichelt, Manuel A1 - Cappella, Brunero T1 - Atomic force microscope study of friction at the submicron-scale during tribotests with self-mated steel JF - Journal of Tribology N2 - Friction at the microscale during reciprocal sliding tribotests was studied for the first time with self-mated steel (100Cr6/AISI 52100) taking advantage of an atomic force microscope (AFM). To this aim, microsized steel particles were glued to the AFM-cantilever and employed as colloidal tips to perform tribotests on a steel disc. The torsion of the cantilever, which correlates with the friction force, was measured during the tests. Few tests with the same load did not yield any wear and show that the load and adhesion contributions to friction stay constant when the shape of the test particle does not change. Most of the presented tribotests engendered wear. For those tests, the increase of friction during the tribotests was attributed to the emerging plowing contribution. Furthermore, analysis of both torsion and local slope gives information on the creation of wear particles and their influence on friction. KW - Friction KW - Microtribology KW - Sliding KW - Wear PY - 2022 DO - https://doi.org/10.1115/1.4054251 VL - 144 IS - 10 SP - 1 EP - 9 PB - ASME AN - OPUS4-54839 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Spaltmann, Dirk A1 - Hartelt, Manfred A1 - Woydt, Mathias T1 - Ultra-high frequency tribometer for reciprocating sliding motion JF - TriboTest N2 - A novel tribometer has been designed using commercially available components for sliding motion at 40kHz with amplitude between 2.5 and 5µm. The tribometer is equipped with means to measure amplitude, frequency, power required to keep the sample in motion and load applied. The effective motion between the two contacting bodies is monitored. These data are used to evaluate the coefficient of friction. The wear rate was determined after the tests. The set-up was tested using novel, non-commercial substrates such as AlFeCrTi-alloys and tungsten carbide-based coatings as well as Magnéli-type coatings (Tin-2Cr2O2n-1 and TinO2n-1). This paper presents the principle of the ultra-high frequency tribometer and first tribological quantities of materials and coatings tested. KW - Frequency KW - Tribometer KW - Sliding KW - Friction KW - Wear KW - Aluminium alloy KW - Oscillation KW - Magnéli-type phases PY - 2007 DO - https://doi.org/10.1002/tt.41 SN - 1354-4063 SN - 1557-685X VL - 13 IS - 4 SP - 153 EP - 164 PB - Coppin CY - Deal AN - OPUS4-16047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Habig, Karl-Heinz T1 - High temperature tribology of ceramics JF - Tribology International KW - Ceramics KW - Alumina KW - Zirconia KW - Friction KW - Wear KW - Sliding PY - 1989 SN - 0301-679X SP - 75 EP - 90 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-2446 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The tribological and mechanical properties of niobium carbides (NbC) bonded with cobalt of Fe3Al JF - Wear N2 - The tribological and mechanical properties of niobium carbide bonded with 8 vol.-% (NbC-8Co), 12 vol.-% of cobalt (NbC-12Co) or 12 vol.-% of Fe3Al (NbC-12Fe3Al) are presented. Rotating discs made of metal-bonded niobium carbide were mated against alumina (99.7%) under unlubricated (dry) unidirectional sliding tests (0.1 m/s to 12.0 m/s; 22 °C and 400 C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles). Microstructure and phase compositions were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where NbC bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a benchmark. Binderless NbC (HP-NbC1) and the metal-bonded NbCs exhibited low wear rates under dry sliding associated with P·V high load carrying capacities. NbC-based hard metal bonded with 12 vol.-% of Fe3Al resulted in a higher hardness level than for 12 vol.-% cobalt. The tribological profile established revealed a strong position of NbC-bearing materials under tribological considerations and for closed tribosystems against established reference tribo-couples. KW - Sliding KW - Ceramic KW - Oscillation KW - Strength KW - Modulus KW - High temperatures KW - Friction KW - Wear KW - NbC KW - Niobium carbide KW - Cobalt KW - Fe3Al KW - Hard metal PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-316129 DO - https://doi.org/10.1016/j.wear.2014.09.007 SN - 0043-1648 VL - 321 SP - 1 EP - 7 PB - Elsevier CY - Amsterdam AN - OPUS4-31612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Niobcarbid - Ein vergessener Hartstoff für den Verschleißschutz in offenen und geschlossenen Tribosystemen JF - Tribologie und Schmierungstechnik N2 - Das tribologische Profil von binderlosem NbC und mit 8% bzw. mit 12% Cobalt oder 12% Fe3Al gebundenem NbC wird unter unidirektionaler Gleitreibung (v= 0,1-10 m/s, T= 22°C und 400°C) und unter oszillierender Gleitreibung vergleichend gegenüber Ingenieurkeramiken und Hartmetallen dargestellt. Zusätzlich werden die 4-Punkt-Biegebruchfestigkeit, elastische Eigenschaften (E,G) bis 1.000�C die lastabhängige Mikrohärte sowie die Phasenzusammensetzung und Gefügestrukturen vorgestellt. Die Verschleißkoeffizienten des binderlosen NbC lagen bei T unterhalb von 10-6 mm³/N?m, während diejenigen der cobaltgebundenen NbCs mit ansteigender Gleitgeschwindigkeit von 2-4 10-6 mm³/N?m bei 0,1 m/s auf 5-7 10-7 mm³/N.m bei 10 m/s abnahmen. Die Verschleißkoeffizienten bei 400°C lagen für die NbCs generell unterhalb von 10-6 mm³/N.m. Das tribologische Lasttragevermögen im Trockenlauf, ausgedrückt als PV-Wert, nimmt mit ansteigender Gleitgeschwindigkeit auf 100 W/mm² zu. Bedingt durch die geringe Löslichkeit von NbC in Legierungen offenbarten erste Zerspanversuche mit verschiedenen Stählen eine gegenüber WC-basierten Schneidstoffen signifikant angehobene Zerspanungsvolumina. Somit offenbart NbC in offenen und geschlossenen Tribosystemen Anwendungspotentiale. KW - Gleiten KW - Reibung KW - Verschleiß KW - Oszillation KW - NbC KW - Niobcarbid KW - Cobalt KW - Fe3Al KW - Hartmetall KW - Festigkeit KW - Hohe Temperaturen KW - Sliding KW - Friction KW - Wear KW - Oscillation KW - Niobium carbide KW - Hard metal KW - Strength KW - Modulus KW - High temperatures PY - 2015 SN - 0724-3472 VL - 62 IS - 3 SP - 5 EP - 13 PB - Expert Verlag CY - Renningen AN - OPUS4-33493 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -