TY - JOUR A1 - Plichta, T. A1 - Sirjovona, V. A1 - Zvonek, M. A1 - Kalinka, Gerhard A1 - Cech, V. T1 - The Adhesion of Plasma Nanocoatings Controls the Shear Properties of GF/Polyester Composite JF - Polymers N2 - High-performance fibre-reinforced polymer composites are important construction materials based not only on the specific properties of the reinforcing fibres and the flexible polymer Matrix but also on the compatible properties of the composite interphase. First, oxygen-free (a-CSi:H) and oxygen-binding (a-CSiO:H) plasma nanocoatings of different mechanical and tribological properties were deposited on planar silicon dioxide substrates that closely mimic E-glass. The nanoscratch test was used to characterize the nanocoating adhesion expressed in terms of critical normal load and work of adhesion. Next, the same nanocoatings were deposited on E-glass fibres, which were used as reinforcements in the polyester composite to affect its interphase properties. The shear properties of the polymer composite were characterized by macro- and micromechanical tests, namely a short beam shear test to determine the short-beam strength and a single fibre push-out test to determine the interfacial shear strength. The results of the polymer composites showed a strong correlation between the short-beam strength and the interfacial shear strength, proving that both tests are sensitive to changes in fibre-matrix adhesion due to different surface modifications of glass fibres (GF). Finally, a strong correlation between the shear properties of the GF/polyester composite and the adhesion of the plasma nanocoating expressed through the work of adhesion was demonstrated. Thus, increasing the work of adhesion of plasma nanocoatings from 0.8 to 1.5 mJ·m−2 increased the short-beam strength from 23.1 to 45.2 MPa. The results confirmed that the work of adhesion is a more suitable parameter in characterising the level of nanocoating adhesion in comparison with the critical normal load. KW - Mechanical properties KW - Plasma nanocoatings KW - Glass fibre KW - Polymer composite KW - Short-beam strength KW - Interfacial shear strength KW - Work of adhesion PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521844 DO - https://doi.org/10.3390/polym13040593 VL - 13 IS - 4 SP - 593 PB - MDPI CY - Basel,Schweiz AN - OPUS4-52184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Theiler, Geraldine A1 - Gradt, Thomas A1 - Banova, Z. A1 - Schlarb, A.K. T1 - PEEK-Komposite für Reibsysteme in der Vakuumtechnik JF - Tribologie und Schmierungstechnik N2 - Aim of the investigation is to characterize selected PEEK-composites in vacuum environment. Oscillating sliding friction was investigated with a pin-on-disc configuration in high vacuum (10-5 mbar) at room temperature, -40 °C, +100 °C and +160 °C. The contact pressure was 1 MPa and 7 MPa respectively , the maximum sliding velocity 0.1 m/s. Furthermore, tests in ultra high vacuum (10-9 mbar) were carried out with flat and spherical pins at 1 MPa and 60 MPa respectively. Among the tested materials MoS2 filled PEEK shows the best tribological performance in vacuum. Particularly, in the lower temperature range and at higher loads the friction behaviour is improved by MoS2 content. KW - Vakuum KW - Polymer composite KW - Tribology KW - PEEK Komposite KW - Hochvakuum KW - Temperatureinfluss KW - MoS2 KW - Grafit KW - PEEK composites KW - High vacuum KW - Influence of the temperature KW - Graphite PY - 2008 SN - 0724-3472 VL - 55 IS - 5 SP - 25 EP - 30 PB - Expert Verlag CY - Renningen AN - OPUS4-18306 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -