TY - JOUR A1 - Altenkirch, J. A1 - Gibmeier, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Nitschke-Pagel, T. A1 - Hofmann, M. T1 - In situ study of structural integrity of low transformation temperature (LTT)-welds JF - Materials science and engineering A N2 - We discuss the stability of weld residual strain under static and quasi cyclic transverse tensile loading in the elastic and elastic–plastic region. The test welds were joined with low transformation temperature weld filler materials with 10 wt% Cr and varying Ni-content from 8 to 12 wt%. Using neutron diffraction the residual lattice strain in the martensitic α'- and austenitic γ-phase in the fusion zone as well as the ferritic α-phase in the heat affected zone and base metal as induced by welding, superimposed by stepwise tensile loading and after unloading was measured. The amount of retained austenite in the fusion zone increases with increasing Ni-content, but it decreases with increasing load level due to stress induced martensite formation. In the as-welded condition the transverse macroscopic residual lattice strain was found to be in low compression in the fusion zone in each weld, while the heat affected zone was in tension. Local plastic deformation of the γ-phase as a result of yielding during tensile loading in combination with the change in phase fraction resulted in increased macroscopic compression in the fusion zone. The reduced yield strength in the heat affected zone resulted in plastic deformation and a considerable shift into compression. Comparison with the cross weld distribution of the hardness and FWHM of the neutron diffraction interference lines supported the assumption of plastic deformation of the γ- and α-phase in the fusion and heat affected zone, respectively, while the α'-phase in the fusion zone was stressed within the elastic regime only. Microstructural observations as well as measurement of the local γ-phase fraction by means of laboratory X-ray diffraction in the fusion zone strengthen these observations. KW - Low transformation temperature KW - Residual stress KW - Neutron diffraction PY - 2011 DO - https://doi.org/10.1016/j.msea.2011.03.091 SN - 0921-5093 SN - 1873-4936 VL - 528 IS - 16-17 SP - 5566 EP - 5575 PB - Elsevier CY - Amsterdam AN - OPUS4-24359 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gibmeier, J. A1 - Held, A. A1 - Altenkirch, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Buslaps, T. T1 - Real time monitoring of phase transformation and strain evolution in LTT weld filler material using EDXRD JF - Journal of materials processing technology N2 - For a newly developed 10% Cr and 10% Ni low transformation temperature (LTT) weld filler material, the local phase transformation kinetics and the strain evolution during gas tungsten arc welding (GTAW) under real welding conditions was studied. An experimental set-up and a measuring and evaluation strategy are presented to gain a real time insight into the welding process. The experiments were carried out at the beam line ID15@ESRF using a two detector EDXRD (energy dispersive X-ray diffraction) set-up and high energy synchrotron X-rays. The time-resolved diffraction analysis during welding was carried out locally throughout the weld in longitudinal as well as in transverse direction to the weld line to examine the interdependence of the strain state and the transformation kinetics. This comprehension is crucial for the optimization of the weld process, and thus for the tailoring of the resulting residual stress states, which is one of the main issues for the application of LTT alloys. Using the herein proposed approach EDXRD diffraction pattern can be monitored during real welding with a counting rate of 5 Hz. By means of the time resolved diffraction data the local transformation temperatures and times were determined and the local phasespecific strain evolutions are discussed with respect to the transformation rates and the time-delayed phase transformations. KW - In situ synchrotron X-ray diffraction KW - Low transformation temperature KW - Welding PY - 2014 DO - https://doi.org/10.1016/j.jmatprotec.2014.06.008 SN - 0924-0136 SN - 1873-4774 VL - 214 IS - 11 SP - 2739 EP - 2747 PB - Elsevier CY - Amsterdam AN - OPUS4-30955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hensel, J. A1 - Kromm, Arne A1 - Nitschke-Pagel, T. A1 - Dixneit, Jonny A1 - Dilger, K. T1 - Capability of martensitic low transformation temperature welding consumables for increasing the fatigue strength of high strength steel joints JF - Materials Testing N2 - The use of low transformation temperature (LTT) filler materials represents a smart approach for increasing the fatigue strength of welded high strength steel structures apart from the usual procedures of post weld treatment. The main mechanism is based on the effect of the low start temperature of martensite formation on the stress already present during welding. Thus, compressive residual stress formed due to constrained volume expansion in connection with phase transformation become highly effective. Furthermore, the weld metal has a high hardness that can delay the formation of fatigue cracks but also leads to low toughness. Fundamental investigations on the weldability of an LTT filler material are presented in this work, including the characterization of the weld microstructure, its hardness, phase transformation temperature and mechanical properties. Special attention was applied to avoid imperfections in order to ensure a high weld quality for subsequent fatigue testing. Fatigue tests were conducted on the welded joints of the base materials S355J2 and S960QL using conventional filler materials as a comparison to the LTT filler. Butt joints were used with a variation in the weld type (DY-weld and V-weld). In addition, a component-like specimen (longitudinal stiffener) was investigated where the LTT filler material was applied as an additional layer. The joints were characterized with respect to residual stress, its stability during cyclic loading and microstructure. The results show that the application of LTT consumables leads to a significant increase in fatigue strength when basic design guidelines are followed. This enables a benefit from the lightweight design potential of high-strength steel grades. KW - Low transformation temperature KW - Welding KW - Fatigue strength KW - Residual stress PY - 2020 DO - https://doi.org/10.3139/120.111562 VL - 62 IS - 9 SP - 891 EP - 899 PB - Carl Hanser Verlag AN - OPUS4-51180 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollert, J. A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Buslaps, Th. A1 - Kannengießer, Thomas T1 - In situ EDXRD study of MAG-welding using LTT weld filler materials under structural restraint JF - Materials Science Forum N2 - Welding using low transformation temperature (LTT) filler materials is an innovative approach to mitigate detrimental welding residual stresses without cost-intensive post weldtreatments. Due to the local Generation of compressive residual stresses in the weld line by means of a delayed martensite transformation a significant enhancement of the cold cracking resistance of highly stressed welded components can be expected. For the effective usage of These materials a deeper understanding of the microstructural evolution inside the weld material is necessary to determine the complex processes that cause the residual stress formation during welding. Solid-state phase transformation kinetics and the evolution of strain in LTT weld filler materials are monitored in-situ at the instrument ID15A at the ESRF in Grenoble, France. The transferability to real components is implemented by using a realistic MAG welding process under consideration of structural restraint. During welding of multilayer joints, the phase Transformation and phase specific strain evolution of each individual layer is investigated in transmission geometry by means of energy-dispersive X-ray diffraction EDXRD using high energy synchrotron Radiation with a counting rate of 2.5 Hz. The measurement results of a 10% Cr / 10% Ni LTT weld filler are compared to data monitored for the conventional weld filler material G89. The in-situ data clearly indicate a strong effect on the local strain evolution and the formation of compressive strain. This results from the restraint volume expansion during the postponed austenite to martensite transformation of the LTT weld filler, which counteracts the thermal shrinkage. In contrast, for the conventional weld filler material the thermal contraction strains lead to tensile residual strain during welding. Furthermore, the results of in-situ observation during welding Show that the transformation kinetic is dependent on the welding sequence. KW - High energy synchrotron diffraction KW - Low transformation temperature KW - Weld filler KW - Residual stress KW - Welding PY - 2017 DO - https://doi.org/10.4028/www.scientific.net/MSF.905.107 SN - 1662-9752 VL - 905 SP - 107 EP - 113 PB - Trans Tech Publications CY - Switzerland AN - OPUS4-41806 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -