TY - JOUR A1 - Hünert, Daniela A1 - Schulz, Wencke A1 - Kranzmann, Axel T1 - Corrosion behavior of ferritic and martensitic power plant steels under conditions of dual atmospheres JF - Corrosion N2 - The most efficient construction materials for boiler water walls and superheaters in steam power plants are ferritic and martensitic steels. In practical operation, tubes are exposed simultaneously to combustion gas and air/steam on their opposite surfaces. The corrosion behavior of ferritic-martensitic steels under such dual atmospheres is nondistinctive and has been investigated in a specially designed test equipment between 500°C and 620°C. The power plant conditions were simulated with a flowing and pressurized (80 bar) combustion gas on the inner side of the tube, which contains water (H2O) and carbon dioxide (CO2). On the outer side, tube material was exposed to air. Oxides that formed on the air side under dual atmosphere conditions were significantly different from the oxide scales formed when the alloy was exposed to air only. It is assumed that the anomalous corrosion behavior during the dual atmosphere exposure is due to hydrogen and carbon diffusion through the bulk alloy from the combustion gas side to the air side. Both species are produced when the material reacts with the gas phase. Because of its high diffusivity, hydrogen is thought to affect the corrosion process on the air side from the beginning of the corrosion exposure, whereas carbon reaches the opposite side after a considerably longer time period. KW - Chromium steels KW - Corrosive gases KW - Dual atmosphere KW - High-temperature corrosion KW - Hydrogen transport KW - Mild steel PY - 2010 SN - 0010-9312 SN - 1938-159X VL - 66 IS - 12 SP - 126001-1 - 126001-7 PB - National Association of Corrosion Engineers CY - Houston, Tex. AN - OPUS4-23217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kingsbery, P. A1 - Manzoni, Anna M. A1 - Suarez Ocaño, Patricia A1 - Többens, D. M. A1 - Stephan‐Scherb, C. T1 - High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction JF - Materials and Corrosion N2 - High‐temperature KCl‐induced corrosion in laboratory air was observed in situ utilizing X‐ray diffraction. High Cr‐containing model alloys (Fe‐13Cr, Fe‐18Cr‐12Ni, and Fe‐25Cr‐20Ni) were coated with KCl and exposed to dry air at 560°C. KCl‐free alloys were studied in the equivalent atmosphere as a reference. After exposure to KCl‐free environments, all alloys showed the formation of very thin oxide layers, indicating good corrosion resistance. In contrast, KCl‐bearing alloys showed distinct damage after exposure. KW - Corrosion KW - In-situ diffraction KW - High-temperature corrosion PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600831 DO - https://doi.org/10.1002/maco.202314224 SN - 0947-5117 SP - 1 EP - 10 PB - Wiley VHC-Verlag AN - OPUS4-60083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nofz, Marianne A1 - Dörfel, Ilona A1 - Sojref, Regine A1 - Wollschläger, Nicole A1 - Mosquera Feijoo, Maria A1 - Schulz, Wencke A1 - Kranzmann, Axel T1 - Thin Sol-Gel Alumina Coating as Protection of a 9% Cr Steel Against Flue Gas Corrosion at 650 °C JF - Oxidation of Metals N2 - Samples of sol-gel alumina coated and uncoated P92 steel were exposed to flue gas at 650 °C for 300 h. As result of this treatment a 50 µm thick bi-layered oxide scale had formed on the surface of the uncoated sample. Below the scale a 40 µm thick inner oxidation zone was detected. In contrast, the porous, micron thick alumina coating enabled the formation of a chromium oxide scale with a thickness of some nanometers at the interface between steel substrate and coating. In this case high temperature corrosion of the steel was prevented so far. KW - Steel KW - Oxide coatings KW - High-temperature corrosion KW - TEM KW - SEM PY - 2018 DO - https://doi.org/10.1007/s11085-017-9799-0 SN - 0030-770X SN - 1573-4889 VL - 89 IS - 3-4 SP - 453 EP - 470 PB - Springer AN - OPUS4-44472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Radziszewska, Agnieszka A1 - Kranzmann, Axel A1 - Dörfel, Ilona A1 - Mosquera Feijoo, Maria A1 - Solecka, M. T1 - Microstructure and chemical composition of Fe-Cr alloy tempered in high temperature and atmosphere containing Ar-SO2 JF - Archives of metallurgy and materials N2 - The paper presents the microstructure, chemical and phase composition of thin scale, obtained as a result of high temperature corrosion of X20Cr13 stainless steel. Samples were exposed to gas atmosphere of the following composition: 0.25 vol.% of SO2 and 99.75 vol.% of Ar at 600 °C for 5 h. As a consequence, thin compact scale was formed on steel surface. This scale consisted of three different zones. An amorphous zone was formed close to steel surface. Then, nanocrystalline Zone could be observed. Finally, larger grains were formed during the corrosion process. The analysis of the chemical composition revealed higher concentration of chromium near steel surface. In contrast, to chromium, the content of iron, increased near the scale surface. It was found out that the (Cr, Mn, Fe)5O12 phase appeared in the thin scale. KW - High-temperature corrosion KW - X20Cr13 steel PY - 2016 DO - https://doi.org/10.1515/amm-2016-0262 SN - 1733-3490 SN - 2300-1909 VL - 61 IS - 3 SP - 1607 EP - 1612 PB - De Gruyter CY - Berlin AN - OPUS4-38351 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -