TY - JOUR A1 - Werner, Tiago A1 - Blasón, Sergio A1 - Madia, Mauro A1 - Kruse, Julius A1 - Benedetti, Matteo T1 - Determination of fatigue crack propagation thresholds using small-scale specimens JF - Procedia Structural Integrity N2 - The damage tolerance approach is widely used in the design and estimation of inspection intervals of safety-relevant metallic components subject to fatigue loading. The approach relies on the knowledge of the fatigue crack propagation characteristics, wherein a relevant role is played by the fatigue crack propagation threshold. Nevertheless, the use of material data determined by testing on conventional specimens is not straightforward in the case of thin-walled components such as turbine blades or additively manufactured parts, in which the local variation of material properties in highly stressed regions must be considered. In these cases, the possibility of investigating the fatigue crack propagation properties on a limited portion of material is crucial. For this purpose, a new test procedure has been developed for small-scale specimens which allows the determination of the intrinsic fatigue crack propagation threshold and the near-threshold regime. The validity and limitations of the method are demonstrated on the high strength steel S960QL, along with a comparison with data determined by testing on conventional geometries. T2 - FATIGUE DESIGN 2021 CY - Online meeting DA - 17.11.2021 KW - Fatigue crack propagation threshold KW - Small-scale specimens KW - High strength steel KW - Crack-tip constraint KW - Damage tolerance PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544967 DO - https://doi.org/10.1016/j.prostr.2022.03.031 SN - 2452-3216 VL - 38 SP - 300 EP - 308 PB - Elsevier B.V. AN - OPUS4-54496 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. T1 - Failure and damage tolerance aspects of railway components JF - Engineering failure analysis N2 - Railway structures such as rails and axles are safety relevant components since any failure includes the risk of catastrophic derailment. This paper gives a brief overview on the most important potential failure scenarios driven by fatigue crack initiation and propagation and discusses the effects of important influencing factors such as vehicle weight and speed, track quality and environmental conditions. The present paper summarizes earlier work of the authors in this field. KW - Railway rails KW - Railway axles KW - Fatigue crack propagation KW - Damage tolerance KW - Fracture mechanics PY - 2011 DO - https://doi.org/10.1016/j.engfailanal.2010.06.001 SN - 1350-6307 SN - 1873-1961 VL - 18 IS - 2 SP - 534 EP - 542 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-22639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. A1 - Köhler, G. A1 - Lawton, A. A1 - Vormwald, M. A1 - Beier, H.T. A1 - Klinger, Christian A1 - Cerný, I. A1 - Rudlin, J. A1 - Heckel, Thomas A1 - Klingbeil, Dietmar T1 - Safe life and damage tolerance aspects of railway axles - A review JF - Engineering fracture mechanics N2 - The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection. KW - Railway axle KW - Safe life design KW - Damage tolerance KW - Fatigue strength KW - Fatigue crack propagation KW - Inspection intervals PY - 2013 DO - https://doi.org/10.1016/j.engfracmech.2012.09.029 SN - 0013-7944 SN - 1873-7315 VL - 98 SP - 214 EP - 271 PB - Elsevier Science CY - Kidlington AN - OPUS4-27779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Bruno, Giovanni A1 - Buffière, J.-Y. A1 - Wegener, T. A1 - Niendorf, T. A1 - Wu, T. A1 - Zhang, X. A1 - Kashaev, N. A1 - Meneghetti, G. A1 - Hrabe, Nik A1 - Madia, Mauro A1 - Werner, Tiago A1 - Hilgenberg, Kai A1 - Koukolikova, M. A1 - Prochazka, R. A1 - Dzugan, J. A1 - Möller, B. A1 - Beretta, S. A1 - Evans, Alexander A1 - Wagener, R. A1 - Schnabel, K. T1 - Damage tolerant design of additively manufactured metallic components subjected to cyclic loading: State of the art and challenges JF - Progress in materials science N2 - This article is an outcome of a workshop on Fatigue of Additive Manufactured Metallic Components jointly organized by the Federal Institute for Materials Research and Testing (BAM) Berlin, Germany and the National Institute of Standards and Technology (NIST) Boulder, CO, U.S.A. The aim of the workshop was a comprehensive discussion of the specific aspects of additively manufactured (AM) components in regard to failure under cyclic loading. Undoubtedly, a better understanding and the further development of approaches for damage tolerant component design of AM parts are among the most significant challenges currently facing the use of these new technologies. This article presents a thorough overview of the workshop discussions. It aims to provide a review of the parameters affecting the damage tolerance of AM parts with special emphasis on the process parameters intrinsic to the AM technologies, the resulting defects and residual stresses. Based on these aspects, concepts for damage tolerant component design for AM are reviewed and critically discussed. KW - Additive manufacturing KW - Fatigue loading KW - Component assessment KW - Damage tolerance KW - Defects KW - Residual stresses PY - 2021 DO - https://doi.org/10.1016/j.pmatsci.2021.100786 SN - 0079-6425 VL - 121 PB - Elsevier CY - Amsterdam AN - OPUS4-51937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Schödel, M. A1 - Beier, H.T. T1 - Parameters affecting the damage tolerance behaviour of railway axles JF - Engineering fracture mechanics N2 - The paper provides a discussion on damage tolerance options applied to railway axles and factors influencing the residual lifetime as well as the required inspection interval. These comprise material properties such as the scatter of the da/dN–ΔK curve, the fatigue crack propagation threshold ΔKth and the toughness of the material. Parameters affecting axle loading such as the press fit, rotating bending, load history and mixed crack opening modes are discussed. Finally the influence of the initial crack geometry on residual lifetime is simulated. KW - Railway axles KW - Damage tolerance KW - Fatigue crack propagation PY - 2011 DO - https://doi.org/10.1016/j.engfracmech.2010.03.013 SN - 0013-7944 SN - 1873-7315 VL - 78 IS - 5 SP - 793 EP - 809 PB - Elsevier Science CY - Kidlington AN - OPUS4-22491 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -