TY - JOUR A1 - Gümpel, P. A1 - Leu, F. A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Karpenko, M. T1 - Corrosion resistance of lean alloy alternatives for 300 series stainless steels - Part 2 JF - Stainless steel world N2 - The second part of this paper looks continues the comparative investigation of lean duplex stainless steels, manganese alloyed austenitic and duplex stainless steels and ferritic stainless steels. These new materials were investigated in many different test procedures and in different conditions focused on the application in civil engineering and common use. In addition to electrochemical investigations, all materials were exposed to atmospheric conditions in different surface states. In Part 2, Prof. Gümpel and his team examine the effects of coastal and urban atmospheres on the samples, and presents their final conclusions. KW - Nichtrostender Stahl KW - Duplex KW - Korrosion KW - Beständigkeit KW - Austenitic KW - Ferritic KW - Duplex KW - Manganese alloyed KW - Pitting corrosion KW - Stress corrosion cracking KW - Passive layer KW - Surface condition PY - 2014 SN - 1383-7184 IS - July/August SP - 49 EP - 52 PB - KCI Publ. BV CY - Zutphen AN - OPUS4-31348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Quiroz Penaranda, Vanessa A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Comparison between CO2- and Nd: YAG-laser beam welding of high-strength CrMnNi steels for the automotive industry JF - Welding in the world N2 - IIW-2326 Austenitic and austenitic-ferritic CrMnNi-stainless steels are suitable materials in the transport and automotive industry due to their high corrosion resistance and high strength that allows weight and cost savings. This study focuses on the laser weldability of a commercial lean duplex and an austenitic high manganese stainless steel. The impact of different laser sources, i.e. a 5 kW CO2- and a 4 kW Nd:YAG-laser, and of the main process parameters on the resulting weld quality will be investigated. One important aspect will concern the appearance of weld defects such as pores and hot cracks. The factors causing such internal imperfections will be analysed in order to find effective methods for preventing them. Weld microstructure and the associated corrosion and mechanical properties will be assessed with different techniques and adequate process parameters for high quality welds will be determined. The advantages and limitations of the applied welding processes will be evaluated for future applications. KW - Laser beam welding KW - Stainless steel KW - Austenitic KW - Duplex KW - Weld microstructure KW - Pores KW - Cracks KW - Corrosion KW - Tensile strength PY - 2012 SN - 0043-2288 SN - 1878-6669 VL - 56 IS - 11/12 SP - 129 EP - 142 PB - Springer CY - Oxford AN - OPUS4-27911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Taparli, Ugur Alp A1 - Jacobsen, Lars A1 - Griesche, Axel A1 - Michalik, Katarzyna A1 - Mory, David A1 - Kannengießer, Thomas T1 - In situ laser-induced breakdown spectroscopy measurements of chemical compositions in stainless steels during tungsten inert gas welding JF - Spectrochimica Acta Part B: Atomic Spectroscopy N2 - A laser-induced breakdown spectroscopy (LIBS) system was combined with a bead-on-plate Tungsten Inert Gas (TIG) welding process for the in situ measurement of chemical compositions in austenitic stainless steels during welding.Monitoring the weld pool's chemical composition allows governing the weld pool solidification behavior, and thus enables the reduction of susceptibility to weld defects. Conventional inspection methods for weld seams (e.g. ultrasonic inspection) cannot be performed during the welding process. The analysis system also allows in situ study of the correlation between the occurrence ofweld defects and changes in the chemical composition in theweld pool or in the two-phase regionwhere solid and liquid phase coexist. First experiments showed that both the shielding Ar gas and the welding arc plasma have a significant effect on the selected Cr II, Ni II and MnII characteristicemissions, namely an artificial increase of intensity values via unspecific emission in the spectra. In situ investigations showed that this artificial intensity increase reached a maximum in presence of weld plume. Moreover, an explicit decay has been observedwith the termination of thewelding plumedue to infrared radiation during sample cooling. Furthermore, LIBS can be used after welding to map element distribution. For austenitic stainless steels,Mnaccumulations on both sides of theweld could be detected between the heat affected zone (HAZ) and the base material. T2 - th International Conference on Laser-Induced Breakdown Spectroscopy (LIBS) CY - Chamonix-Mont-Blanc, France DA - 12.09.2016 KW - LIBS KW - TIG KW - Welding KW - Austenitic KW - Stainless steels KW - Chemical composition KW - In situ KW - Measurement PY - 2018 UR - http://www.sciencedirect.com/science/article/pii/S0584854717301064 DO - https://doi.org/10.1016/j.sab.2017.11.012 SN - 0584-8547 VL - 139 SP - 50 EP - 56 PB - Elsevier CY - Amsterdam, Niederlande AN - OPUS4-43122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -