TY - JOUR A1 - Boateng, Francis Twumasi A1 - Ewert, Uwe A1 - Kannengießer, Thomas A1 - Zscherpel, Uwe A1 - Griesche, Axel A1 - Kromm, Arne A1 - Hohendorf, Stephan A1 - Redmer, Bernard T1 - Real-time radiography for observation of crack growth during GTA (Gas Tungsten Arc) welding JF - Welding in the world N2 - In situ crack detection in the mushy zone and the solid weld of a gas tungsten arc (GTA) weld using X-ray imaging during welding is a new research area for NDT inspection. Usually, NDT flaw detection is done after the complete solidification of the weld seam. In this paper, we present the use of real-time radiography with a minifocus X-ray source (YXLON X-ray tube Y.TU 225-D04) and a 75μm pixel size digital detector array (Dexela 1512) for the acquisition of 2D radiographic images by a sequence of exposures with time intervals of 80 ms for hot crack detection during single pass bead-on-plate GTA welding of 3 mm thick plates of aluminium alloy AlMgSi (6060). An analysis of the crack distribution in the weld sample is conducted from the acquired 2D radiographs and its corresponding 3D volumetric reconstruction achieved by linear coplanar digital laminography. This in situ approach opens new possibilities in the field of hot crack research by having the direct information of both the crack initiation and growth and its correlation to the welding parameters. KW - Hot cracking KW - Radiography KW - GTA welding KW - Aluminium alloys KW - Real-time operation PY - 2016 DO - https://doi.org/10.1007/s40194-016-0351-7 SN - 0043-2288 SN - 1878-6669 VL - 60 IS - 5 SP - 931 EP - 937 AN - OPUS4-37128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cabeza, Sandra A1 - Müller, Bernd R. A1 - Pereyra, R. A1 - Fernández, R. A1 - González-Doncel, G. A1 - Bruno, Giovanni T1 - Evidence of damage evolution during creep of Al–Mg alloy using synchrotron X-ray refraction JF - Journal of applied crystallography N2 - In order to provide further evidence of damage mechanisms predicted by the recent solid-state transformation creep (SSTC) model, direct observation of damage accumulation during creep of Al–3.85Mg was made using synchrotron X-ray refraction. X-ray refraction techniques detect the internal specific surface (i.e. surface per unit volume) on a length scale comparable to the specimen size, but with microscopic sensitivity. A significant rise in the internal specific surface with increasing creep time was observed, providing evidence for the creation of a fine grain substructure, as predicted by the SSTC model. This substructure was also observed by scanning electron microscopy KW - Aluminium alloys KW - Creep KW - Damage KW - Synchrotron X-ray refraction KW - Electron microscopy KW - subgrain structure PY - 2018 DO - https://doi.org/10.1107/S1600576718001449 SN - 1600-5767 VL - 51 SP - 420 EP - 427 PB - Wiley AN - OPUS4-44619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Coniglio, Nicolas A1 - Cross, Carl Edward T1 - Characterization of solidification path for Aluminium 6060 weld metal with variable 4043 filler dilution JF - Welding in the world N2 - Aluminium alloy 6060 is typical of a family of Al-Mg-Si extrusion alloys, which are considered weldable only when using an appropriate filler alloy such as 4043 (Al-5Si) or 5356 (Al-5Mg). This study concerns the thermal analysis and solidification path determination of aluminium alloy 6060 diluted with variable amounts of 4043. Casting of controlled mixtures of alloys 6060 and 4043 was used to simulate different weld dilutions in order to facilitate thermal analysis. Thermal analysis and metallography were applied in order to reveal solidification reactions and phases, and allow calculation of solid fraction versus temperature curves. Although the liquidus temperature was little affected, different phases formed with increased 4043 dilution, with a trend toward lower temperature reactions and a larger fraction interdendritic constituent. KW - Aluminium alloys KW - Light metals KW - Solidification cracking KW - Cracking KW - Defects KW - Hot cracking KW - Analysis techniques KW - Cooling KW - Cooling rate KW - Temperature KW - Practical investigations KW - Microstructure KW - Dilution KW - Reference lists PY - 2006 UR - http://www.iiw-iis.org/ SN - 0043-2288 SN - 1878-6669 VL - 50 IS - 11/12 SP - 14 EP - 23 PB - Springer CY - Oxford AN - OPUS4-14219 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cross, Carl Edward A1 - Böllinghaus, Thomas T1 - The Effect of Restraint on weld Solidification Cracking in Aluminium JF - Welding in the world KW - Aluminium alloys KW - Light metals KW - Solidification cracking KW - Cracking KW - Defects KW - Hot cracking KW - Crack initiation KW - Strain KW - Restraint PY - 2006 SN - 0043-2288 SN - 1878-6669 VL - 50 IS - 11/12 SP - 51 EP - 54 PB - Springer CY - Oxford AN - OPUS4-14220 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fernández, R. A1 - Bokuchava, G. A1 - Bruno, Giovanni A1 - Serrano Munoz, Itziar A1 - González Doncel, G. T1 - On the dependence of creep-induced dislocation configurations on crystallographic orientation in pure Al and Al-Mg JF - Journal of Applied Crystallography N2 - The peak broadening in neutron diffraction experiments on tensile specimens of pure Al (99.8%) and an Al-Mg alloy pre-deformed at different creep strains is analysed. These results are combined with the kernel angular misorientation of electron backscatter diffraction data from the creep-deformed microstructures. It is found that differently oriented grains possess different microstrains. These microstrains vary with creep strain in pure Al, but not in the Al-Mg alloy. It is proposed that this behaviour can explain the power-law breakdown in pure Al and the large creep strain observed in Al-Mg. The present findings further corroborate a description of the creep-induced dislocation structure as a fractal, predicated on previous work. KW - Creep KW - Aluminium alloys KW - Dislocations KW - Fractals KW - Diffraction peak width PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575527 DO - https://doi.org/10.1107/S1600576723003771 SN - 0021-8898 VL - 56 IS - Pt 3 SP - 764 EP - 775 AN - OPUS4-57552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nadammal, Naresh A1 - Kailas, Satish A1 - Szpunar, Jerzy A1 - Suwas, Satyam T1 - Development of microstructure and texture during single and multiple pass friction stir processing of a strain hardenable aluminium alloy JF - Materials Characterization N2 - In the present study, microstructure and texture development during single and multiple pass friction stir processing (FSP) of a strain hardenable wrought AlMg alloy (AA5086) was investigated. Subtle differences were observed while comparing with heat treatable alloys in the nucleation mechanism of the recrystallized microstructure observed in the nugget zone. Strain induced boundary migration was the dominant mechanism of microstructure evolution in the alloy, which influenced the crystallographic texture development by weakening it. Micro-texture measurements reveal variations in the crystallographic texture along the thickness of the sample. Recrystallization texture components were observed in the nugget zone indicative of a pronounced static recrystallization in the alloy as compared to the heat treatable alloys. Bulk texture measurements within the nugget zone of the optimally processed sample reveal a relatively dominant C component of shear texture. Average grain size in the nugget zone remained the same and the bulk crystallographic texture components were retained during multiple-pass FSP. The lower strain energies involved and the enhanced recovery processes due to the high temperature materials processing of the alloy during FSP resulted in a stable microstructure and texture. In summary, FSP could be promoted as a competent and suitable secondary processing technique for the bulk production of ultra-fine-grained materials in strain hardenable aluminium alloys. KW - Friction stir processing KW - Aluminium alloys KW - Electron back-scattered diffraction KW - Crystallographic texture KW - Dynamic recrystallization PY - 2018 UR - https://www.sciencedirect.com/science/article/pii/S1044580317336136 DO - https://doi.org/10.1016/j.matchar.2018.03.044 SN - 1044-5803 SN - 1873-4189 VL - 140 SP - 134 EP - 146 PB - Elsevier B.V CY - Amsterdam, The Netherlands AN - OPUS4-45125 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Perret, William A1 - Thater, Raphael A1 - Alber, U. A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Case study for welding simulation in the automotive industry JF - Welding in the world N2 - Welding is one of the most widely used joining processes in structural applications, like in car body production in the automotive industry. It is well-known that distortions and residual stresses occur during and after the welding process. Many procedures exist to decrease these negative heat effects of welding, but are often coupled with highly cost intensive experiments. For several decades, simulation models have been developed to understand and predict the heat effects of welding and to reduce experimental effort. In the production planning of various Original Equipment Manufacturers (OEM), some simulation tools are already well established, e.g. for crash test, forming or casting simulations. For welding, the demand is high but the implementation of welding simulation software is still not established yet. Welding is a complex process and the development of a flexible simulation tool, which produces good simulation results without expert knowledge in simulation, is not an easy task. In this paper, a welded assembly from the automotive industry has been simulated and compared to experimental data. Temperature fields and transient distortion distributions have been measured with thermocouples and with an optical 3D deformations analysis tool, respectively. The simulation has been run with a commercially available welding simulation software. The simulated temperature fields match the numerical ones perfectly. The simulated distortions are also qualitatively in best agreement with the experimental ones. Quantitatively, a difference of approximately 20 % between the simulated and the measured distortions is visible; this is acceptable considering the simplifications and assumptions of the simulation model. The global time to solution to get these results without expert knowledge in welding simulation was between 4 and 6 weeks, which is a reasonable time frame for an industrial application of welding simulation. KW - Automobiles KW - Distortion KW - Simulating KW - Temperature KW - Welding KW - Aluminium alloys KW - Al Mg Si alloys KW - Automobile engineering KW - Finite elements analysis KW - Mathematical models KW - MIG welding KW - Residual stresses KW - Vehicle bodies PY - 2011 DO - https://doi.org/10.1007/BF03321546 SN - 0043-2288 SN - 1878-6669 VL - 55 IS - 11/12 SP - 89 EP - 98 PB - Springer CY - Oxford AN - OPUS4-25029 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, André A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam welding of aluminium alloys under the influence of an electromagnetic field JF - Physics Procedia N2 - During laser beam welding of aluminum alloys an electromagnetic field may favour pore outgassing through the top oxide layer. High frequencies cause a small penetration depth and thus exert a stabilizing effect on the weld surface. The point at which the laser beam between the two magnetic poles hits the workpiece surface is crucial to the influence of the magnetic field on the weld surface roughness. Using analyzed parameters for different laser points of application cause a change in weld surface roughness could be observed. The weld surface roughness could be reduced by 50%. The outgassing effect in terms of a reduction of pores could be observed for all parameter sets investigated. T2 - Lasers in manufacturing conference 2013 CY - Munich, Germany DA - 13.05.2013 KW - Electromagnetically controlled laser beam welding KW - Surface roughness KW - Porosity prevention KW - Aluminium alloys PY - 2013 DO - https://doi.org/10.1016/j.phpro.2013.03.045 SN - 1875-3892 VL - 41 SP - 4 EP - 11 PB - Elsevier B.V. CY - Amsterdam [u.a.] AN - OPUS4-28147 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Symietz, Christian A1 - Lehmann, Erhard A1 - Gildenhaar, Renate A1 - Hackbarth, Andreas A1 - Berger, Georg A1 - Krüger, Jörg T1 - Mechanical stability of Ti6Al4V implant material after femtosecond laser irradiation JF - Journal of applied physics N2 - The surface of a titanium alloy (Ti6Al4V) implant material was covered with a bioactive calcium alkali phosphate ceramic with the aim to accelerate the healing and to form a stronger bond to living bone tissue. To fix the ceramic powder we used a femtosecond laser, which causes a thin surface melting of the metal. It is a requirement to prove that the laser irradiation would not reduce the lifetime of implants. Here we present the results of mechanical stability tests, determined by the rotating bending fatigue strength of sample rods. After describing the sample surfaces and their modifications caused by the laser treatment we give evidence for an unchanged mechanical stability. This applies not only to the ceramic fixation but also to a comparatively strong laser ablation. KW - Aluminium alloys KW - Bending strength KW - Bioceramics KW - Bone KW - Calcium compounds KW - Fatigue KW - Fatigue testing KW - High-speed optical techniques KW - Laser ablation KW - Melting KW - Orthopaedics KW - Prosthetics KW - Rods (structures) KW - Surface treatment KW - Titanium alloys KW - Vanadium alloys PY - 2012 DO - https://doi.org/10.1063/1.4737576 SN - 0021-8979 SN - 1089-7550 VL - 112 IS - 2 SP - 023103-1 - 023103-5 PB - American Institute of Physics CY - Melville, NY AN - OPUS4-26200 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -