TY - JOUR A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard T1 - Adhesion of metals to plasma-induced functional groups at polymer surfaces JF - Surface and coatings technology N2 - The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 3–4 to 10–14 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral “monomers” like ethylene or butadiene the concentration of the functional groups was varied. A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2–CH2). KW - Peel strength KW - Aluminium KW - Polypropylene KW - Poly(tetrafluoroethylene) KW - Pulsed plasma KW - Allyl alcohol KW - Allylamine KW - Acrylic acid KW - Plasma surface treatment KW - Adhesion PY - 2005 SN - 0257-8972 VL - 200 IS - 1-4 SP - 565 EP - 568 PB - Elsevier Science CY - Lausanne AN - OPUS4-10897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Oran, Umut A1 - Swaraj, Sufal A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Surface analysis of Plasma Deposited Polymer Films, 7: "In situ" Characterization of Plasma Deposited Allylamine Films by ToF-SSIMS, XPS and NEXAFS Spectroscopy JF - Plasma processes and polymers N2 - Plasma deposited allylamine films were studied by in situ ToF-SSIMS, XPS and NEXAFS Spectroscopy before exposure to ambient air. The influence of external plasma parameters such as duty cycle, plasma power, and monomer flow rate on (i) unsaturation, (ii) branching and cross-linking, (iii) nitrogen surface concentration and (iv) retention of amino groups was investigated. Harder plasma conditions, which can be obtained when high duty cycles, high plasma power, and low monomer flow rates are employed, increase the unsaturated, branched and cross-linked character of the plasma deposited films, while the surface concentration of N as well as the retention of the monomer's amino group decrease. As proven by NEXAFS findings and cross-checked by ToF-SSIMS results, the allylamine monomer's primary amino groups are partially transformed into other nitrogen functionalities during its plasma polymerization. Amongst them imines and nitriles are the conversion products with the highest probabilities of formation. Another conversion channel is the formation of nitrogen species not participating in the film growth. This is the reason for an increased N loss in plasma deposited allylamine films as observed independently by XPS and ToF-SSIMS when the plasma parameters are changed from mild to hard. KW - Allylamine KW - NEXAFS KW - Plasma polymerization KW - ToF-SSIMS KW - XPS PY - 2006 DO - https://doi.org/10.1002/ppap.200500168 SN - 1612-8850 SN - 1612-8869 VL - 3 IS - 3 SP - 288 EP - 298 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-12272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -