TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen A1 - Meyer, A. T1 - About alcohol-initiated polymerization of glycolide and separate crystallization of cyclic and linear polyglycolides N2 - Alcohol-initiated polymerizations of glycolide (GL) catalyzed by tin(II) 2-ethylhexanoate (SnOct2) were carried out in bulk with variation of GA/In ratio, temperature and time. Due to a rather strong competition of cyclization polyglycolide (PGA) free of cycles were never obtained. When the cyclic catalysts 2,2-dibutal-2-stanna − 1,3-dithiolane (DSTL) or 2-stanna 1,3-dioxo-4,5,6,7 bibenzepane (SnBiph) were used in combination with 1,4-butanediol the influence of cyclization was even stronger. Furthermore, the degrees of polymerization were higher than the GA/alcohol ratio due to rapid polycondensation in the solid state. At 160 °C or below, the matrixassisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectra indicated separate crystallization of low molar mass cyclic and linear PGAs from the same reaction mixture (also observed for poly(L-lactide)s). KW - MALDI TOF MS KW - Polyglycolide KW - Ring opening polymerization KW - Cyclization KW - Crystallization PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607282 DO - https://doi.org/10.1016/j.polymer.2024.127440 VL - 309 SP - 1 EP - 9 PB - Elsevier Ltd. AN - OPUS4-60728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hertwig, Andreas A1 - Ermilova, Elena T1 - Optical constants of a single AlN layer on Si N2 - Spectroscopic ellipsometry was used to determine the thickness and dielectric function of a Aluminium Nitride (AlN) layer on a Si wafer. The layer was determined to be 170 nm thick. The layer was provided by AIXTRON and manufactured by means of MOVPE. The data was created using a M2000DI spectroscopic ellipsometer from Woollam Co. Inc. Analysis was done using the CompleteEASE software. The model used is a multi-peak oscillator model for the AlN layer. The data resembles common database values for the material AlN. KW - Aluminium nitride KW - Thin solid layers KW - Spectroscopic ellipsometry KW - Compund semiconductors KW - MOVPE PY - 2024 UR - https://zenodo.org/records/12743500 DO - https://doi.org/10.5281/zenodo.12743499 PB - Zenodo CY - Geneva AN - OPUS4-60661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schusterbauer, Robert A1 - Sahre, Mario A1 - Mrkwitschka, Paul A1 - John, Elisabeth A1 - Lange, Thorid A1 - Zurutuza, A. A1 - Jones, E. A1 - Donskyi, I. A1 - Radnik, Jörg A1 - Hodoroaba, Vasile-Dan T1 - Correlative chemical imaging to reveal the nature of different commercial graphene materials N2 - Since the original report in 2004 by Novoselov and Geim, Graphene gained incredible attention due to its fascinating properties. In the past 20 years, the synthesis and functionalization of graphene has evolved significantly[3]. Different synthesis techniques were developed which led to other graphenerelated materials such as graphene oxide (GO) or elemental-doped graphene. Further chemical functionalization can enhance but also alter or reduce specific properties of the graphene. To reveal the nature of these materials a proper physico‑chemical characterization with different analytical techniques is crucial. Single-layer GO flakes kindly provided by Graphenea (Spain) were prepared for systematic image analysis. These flakes were disposed on an alignment-marked SiO2 substrate and correlatively imaged by scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS) and Raman spectroscopy. The high lateral resolution and/ or extreme surface sensitivity of the mentioned techniques is necessary to explore monolayers. The ToF-SIMS images match well with the SEM and AFM images and provide information about the chemistry. With 2D Raman spectroscopy it is possible to differentiate between the number of stacked single-layer flakes. This is visualized in a 3D image (Figure b). Well-defined GO flakes could be used as a reference material for imaging of graphene-like structures but also of other types of 2D materials. In addition to these monolayer GO flakes, commercial graphene-containing inks (Haydale) with a more complex morphology were also correlatively imaged. ToF-SIMS and SEM images were merged to identify the origin of different chemical fragments. The findings correlate closely with the expectation that the specific functionalizations (with fluorine and nitrogen as marker elements) are present only on the graphene flakes as presumed from the SEM images. Energy-dispersive X-ray spectroscopy (EDX) supports these results, yet with a much lower sensitivity compared to ToF-SIMS. T2 - MaterialsWeek 2024 CY - Limassol, Cyprus DA - 17.06.2024 KW - Graphene oxide flakes KW - ToF-SIMS KW - SEM KW - Raman KW - Correlative imaging PY - 2024 AN - OPUS4-60681 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schusterbauer, Robert A1 - Sahre, Mario A1 - Mrkwitschka, Paul A1 - John, Elisabeth A1 - Lange, Thorid A1 - Zurutuza, A. A1 - Jones, E. A1 - Donskyi, I. A1 - Radnik, Jörg A1 - Hodoroaba, Vasile-Dan T1 - Correlative chemical imaging to reveal the nature of different commercial graphene materials N2 - Since the original report in 2004 by Novoselov and Geim, Graphene gained incredible attention due to its fascinating properties. In the past 20 years, the synthesis and functionalization of graphene has evolved significantly[3]. Different synthesis techniques were developed which led to other graphenerelated materials such as graphene oxide (GO) or elemental-doped graphene. Further chemical functionalization can enhance but also alter or reduce specific properties of the graphene. To reveal the nature of these materials a proper physico‑chemical characterization with different analytical techniques is crucial. Single-layer GO flakes kindly provided by Graphenea (Spain) were prepared for systematic image analysis. These flakes were disposed on an alignment-marked SiO2 substrate and correlatively imaged by scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS) and Raman spectroscopy. The high lateral resolution and/ or extreme surface sensitivity of the mentioned techniques is necessary to explore monolayers. The ToF-SIMS images match well with the SEM and AFM images and provide information about the chemistry. With 2D Raman spectroscopy it is possible to differentiate between the number of stacked single-layer flakes. This is visualized in a 3D image (Figure b). Well-defined GO flakes could be used as a reference material for imaging of graphene-like structures but also of other types of 2D materials. In addition to these monolayer GO flakes, commercial graphene-containing inks (Haydale) with a more complex morphology were also correlatively imaged. ToF-SIMS and SEM images were merged to identify the origin of different chemical fragments. The findings correlate closely with the expectation that the specific functionalizations (with fluorine and nitrogen as marker elements) are present only on the graphene flakes as presumed from the SEM images. Energy-dispersive X-ray spectroscopy (EDX) supports these results, yet with a much lower sensitivity compared to ToF-SIMS. T2 - ECASIA 2024 CY - Gothenburg, Sweden DA - 09.06.2024 KW - Correlative imaging KW - ToF-SIMS KW - SEM KW - Graphene oxide flakes KW - Raman PY - 2024 AN - OPUS4-60680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Waniek, Tassilo A1 - Omar, Hassan A1 - Szymoniak, Paulina A1 - Silbernagl, Dorothee A1 - Sturm, Heinz T1 - The influence of water released from particles in epoxy‐based nanocomposites N2 - AbstractRecent studies have hypothesized that the reinforcing effects of boehmite nanoparticles (BNPs) in polymer nanocomposites (PNCs) are partly related to the particles themselves and partly to the water released from the BNP during curing. In this work, PNCs made from dried BNP (dBNP) with concentrations up to 15 wt% are investigated to differentiate particle and water related effects. The observed trend of the storage modulus in dynamic mechanical thermal analysis measurements was found to be independent of the drying procedure. Stiffness maps from intermodulation atomic force microscopy showed that dBNP leads to a stiffening of the interphase surrounding the particles compared with the unaffected epoxy matrix, while a softer interphase was reported for PNCs with as received BNP. A slight decrease in the glass transition temperature was observed by broadband dielectric spectroscopy related to a lowered crosslink density due to the particles. A significantly higher decrease was reported for PNCs with BNP, attributed to water influencing the curing process. In conclusion, the stiffening of PNC with BNP is related to the particles themselves, while the release of water causes the formation of a soft interphase in the vicinity of the particles and a significant decrease in crosslink density. KW - AFM stiffness of interface KW - Aluminium oxide hydroxide KW - Boehmit nanoparticle KW - Glass transition temperature KW - Broadband dielectric spectroscopy KW - Crosslink density control KW - Structure–property relationship KW - Nanocomposites KW - Thermoset PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606772 DO - https://doi.org/10.1002/app.55937 SN - 0021-8995 SP - 1 EP - 16 PB - Wiley AN - OPUS4-60677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fornacon-Wood, Christoph A1 - Stühler, Merlin R. A1 - Millanvois, Alexandre A1 - Steiner, Luca A1 - Weimann, Christiane A1 - Silbernagl, Dorothee A1 - Sturm, Heinz A1 - Paulus, Beate A1 - Plajer, Alex J. T1 - Fluoride recovery in degradable fluorinated polyesters N2 - We report a new class of degradable fluorinated polymers through the copolymerization of tetrafluorophthalic anhydride and propylene oxide or trifluoropropylene oxide which show up to 20 times quicker degradation than the non-fluorinated equivalents and allow for fluoride recovery. KW - Fluoropolymers KW - Recycling KW - PFAS KW - AFM force distance curves KW - AFM plastic deformation KW - AFM friction analysis PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606768 DO - https://doi.org/10.1039/d4cc02513j VL - 60 SP - 7479 EP - 7482 PB - Royal Society of Chemistry AN - OPUS4-60676 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - George, Janine T1 - Data-driven approaches for materials understanding and design N2 - Bonds and local atomic environments are crucial descriptors of material properties. They have been used to create design rules and heuristics and as features in machine learning of materials properties. Implementations and algorithms (e.g., ChemEnv and LobsterEnv) for identifying local atomic environments based on geometrical characteristics and quantum-chemical bonding analysis are nowadays available. Fully automatic workflows and analysis tools have been developed to use quantum-chemical bonding analysis on a large scale. The lecture will demonstrate how our tools, that assess local atomic environments and perform automatic bonding analysis, help to develop new machine learning models and a new intuitive understanding of materials. Furthermore, the general trend toward automation in computational materials science and some of our recent contributions will be discussed. T2 - Machine Learning of First Principles Observables CY - Berlin, Germany DA - 08.07.2024 KW - Automation KW - Bonding Analysis KW - Machine Learned Potentials PY - 2024 AN - OPUS4-60660 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - DACHS/MOFs/AutoMOFs_3/Synthesis N2 - The DACHS (Database for Automation, Characterization and Holistic Synthesis) project aims to create completely traceable experimental data, covering syntheses, measurements, analyses, and interpretations. DACHS_MOFs focuses on the synthesis and characterisation of metal-organic frameworks, across multiple, automation-assisted experimental series (AutoMOFs), with the overall goal of producing reproducible MOF samples through tracking of the synthesis parameters. DACHS_MOFs is simultaneously used to test the DACHS principles. This upload contain synthesis data from AutoMOFs_3 in HDF5 format (.h5). Each .h5 file contains detailed information on the chemical, experimenal, and synthesis parameters used during the synthesis of a single AutoMOF sample. KW - Synthesis KW - Automation KW - Traceability KW - Procedure PY - 2024 DO - https://doi.org/10.5281/zenodo.11237815 PB - Zenodo CY - Geneva AN - OPUS4-60633 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Menga, D. A1 - Low, Jian Liang A1 - Guilherme Buzanich, Ana A1 - Paulus, B. A1 - Fellinger, Tim-Patrick T1 - The Tetrapyrollic Motif in Nitrogen Doped Carbons and M-N-C Electrocatalysts as Active Site in the Outer-Sphere Mechanism of the Alkaline Oxygen Reduction Reaction N2 - Development and fundamental understanding of precious-group-metal-free electrocatalysts is hampered by limitations in the quantification of the intrinsic activity of different catalytic sites and understanding the different reaction mechanisms. Comparing isomorphic nitrogen-doped carbons, Zn-N-Cs and Fe-N-Cs with the common tetrapyrrolic motif, a catalyst-independent outer-sphere rate-determining step in the alkaline oxygen reduction reaction is observed. Density functional theory (DFT) simulations on tetrapyrrolic model structures indicate the highest occupied molecular orbital (HOMO) level as a good descriptor for the catalytic activity. Contour plots suggest that the electron transfer occurs directly from the tetrapyrrolic coordination site, rather than from the metal center. Metal-free tetrapyrrolic N4 sites are discovered to be highly active oxygen reduction reaction (ORR) active sites in alkaline that reach turnover frequencies (TOF) of 0.33 and 1.84 s−1 at 0.80 and 0.75 VRHE in the order of magnitude of tetrapyrrolic Fe–N4 sites in the acidic ORR. While Zn-coordination lowers the HOMO level and therefore the catalytic activity, Fe-coordination lifts the HOMO level resulting in TOF values of 0.4 and 4 s−1 for tetrapyrrolic Fe–N4 sites at 0.90 and 0.85 VRHE, respectively. At higher mass activities, the peroxide reduction becomes rate-limiting, where highest peroxide production rates are observed for the nitrogen-doped carbon. KW - Tetrapyrollic KW - Motif KW - Nitrogen KW - Carbons KW - Alkaline Oxygen PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606239 DO - https://doi.org/https://doi.org/10.1002/aenm.202400482 SN - 1614-6832 VL - 2024 SP - 1 EP - 8 PB - Wiley-VCH AN - OPUS4-60623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen T1 - Low Molar Mass Cyclic Poly(L-lactide)s: Separate Transesterification Reactions of Cycles and Linear Chains in the Solid State N2 - L-Lactide (LA) was polymerized with neat tin(II) 2-ethylhexanoate (SnOct2) in toluene at 115 °C at low concentration with variation of the LA/Cat ratio. Cyclic polylactides (cPLAs) with number average molecular weights (Mn) between 7 000 and 17 000 were obtained. MALDI-TOF mass spectrometry also revealed the formation of a few percent of linear chains. Crystalline cPLAs with Mn around 9 000 and 14 000 were annealed at 140 °C in the presence of ScOct2 or dibutyl-2-stanna-1,3-dithiolane (DSTL). Simultaneously, crystallites of extended linear chains and crystallites of extended cycles were formed regardless of the catalyst, indicating that transesterification reaction proceeded different for linear chains and for cycles, governed by thermodynamic control. The formation of extended chain crystallites with low dispersity indicates the existence of symproportionation of short and long chains. A complementary experiment was carried out with a PLA ethyl ester composed mainly of linear chains with a small fraction of cycles KW - Polylactide KW - MALDI-TOF MS KW - Annealing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606228 DO - https://doi.org/10.1039/D4SM00567H SN - 1744-6848 SP - 1 EP - 12 PB - Royal Society of Chemistry (RSC) AN - OPUS4-60622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -