TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Falkenhagen, Jana T1 - Combined impact of UV radiation and nitric acid (HNO3) on HDPE jerrycans – comparison of outdoor and lab test N2 - A damaging action of HNO3-55% only occurs in combination with its decomposition into nitrous gases, which can be caused by UV radiation. In a laboratory test, transparent HDPE jerrycans have been exposed to both UV radiation and 55 wt-% nitric acid solution at (41 ± 2)°C, for up to 20 days. For comparison, UV radiant exposure (21 days) and nitric acid exposure (up to 6 weeks) were performed separately, at nearly equal temperatures. The respective damages are compared with FTIR spectroscopy in ATR and HT-gel permeation chromatography (GPC) on a molecular level and with hydraulic internal pressure testing as a component test. For the used jerrycans, relevant oxidation can only be found after the combined exposure. The gradual increase in oxidative damage shows the good reproducibility of the lab exposure. The decomposition of nitric acid into nitrous gases by UV radiation – as well as the jerrycan oxidation – is also observed at lower HNO3 concentration (28 wt- %). Similar results are obtained after outdoor tests. Again, the damage occurs only after combined exposure, in contrast to the exposures to UV only and to HNO3 only, which were conducted in parallel. Outdoor exposures are most readily accepted as they represent possible end-use conditions. However, the reproducibility of these exposures is poor due to the large temporal variations in weather. There are also several safety risks, which is why the number of replicates remains limited. Since the outdoor and lab exposure tests show the same qualitative results, it is appropriate to conduct systematic studies in the laboratory. After 6 days of lab exposure, the oxidation damage is rated as critical, which corresponds to about 1/10 year in Central Europe, according to the UV radiant exposure. It should be noted that this amount can also occur in two sunny weeks. T2 - 24th iapri World Packaging Conference CY - Valencia, Spain DA - 17.06.2024 KW - Ppolyethylene KW - UV exposure KW - Nitric acid KW - Oxidation PY - 2024 VL - 2 SP - 30 EP - 37 PB - ITENE AN - OPUS4-60414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tochtrop, Christoph A1 - von Geibler, Justus A1 - Rückschloss, Jana A1 - Schlegel, Moritz-Caspar T1 - An environmental assessment approach for additional product functions and its application in the case of fridge-freezers N2 - Next to primary functions, energy-related products have an increasing number of additional functions. This affects the overall environmental footprint, but the question is how? A number of European policy strategies, initiatives and measures, such as the Green Deal, the Circular Economy Action Plan,the Ecodesign Directive and the EU Energy Labelling, aim to ensure that the environmental impact of the overall product is better determined, communicated and finally reduced. A core element of these efforts is the DIN EN 4555x series of standards. However, there is currently no comprehensive and systematic classification of the additional product functions or an approach to assess the associated positive and negative environmental impacts. Therefore, we present in this study an environmental assessment approach for additional product functions and illustrate its application in the case of fridge-freezers. A key element of the life-cycle-oriented methodology is an assessment matrix to categorize and evaluate the direct, indirect and systemic impacts of products’ functions. Based on semiquantitative assessments of experts, the matrix provides an indication of how the additional function affects the overall environmental product impact as well as specific product aspects such as durability or reparability. Based on the results experts can discuss and better understand how specific functions can influence various stages of the product life cycle and how intended systemic changes or rebound effects could occur. As part of the approach, a representative survey was conducted to analyze consumers’ knowledge and information needs. Based on the results, recommendations for purchasing decisions and the consumer information were developed. This paper presents the results from the assessment of the additional functions of fridge-freezers. T2 - EGG+ Electronics Goes Green 2024+ CY - Berlin, Germany DA - 18.06.2024 KW - Circular Economy KW - ESPR KW - Material efficiency KW - Ecodesign KW - Policy making KW - Standardization KW - Consumer PY - 2024 SN - ISBN 978-3-00-079329-5 SP - 87 EP - 97 AN - OPUS4-60400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlegel, Moritz-Caspar A1 - McAlister, Catriona A1 - Rama, Mathieu T1 - Pioneering durability in electronics - The role of standardisation in policymaking and vice versa N2 - This paper highlights the role of standardisation in enabling greener electronics in the EU. It presents an analysis of the evolving landscape of material efficiency standardization, the majority of which has been undertaken in the framework of the European Ecodesign Directive, soon to be repealed by the Ecodesign for Sustainable Products Regulation. The impending policy shift will include a very broad extension of product scope, a strengthening of the way in which material efficiency aspects are addressed, and wider potential for product labelling. During the stakeholder consultation process, the European Commission announced that the durability of products would be one of the major topics in the new regulatory approach - hence the specific focus of this paper on durability scoring. The paper first examines the policy and standardization context, and then provides an overview of material efficiency indexes and scoring systems currently in place or being developed. It highlights where standardization is following policymaking, and where standardization is paving the way for more circular products. Scoring systems and indexes could potentially be used for both (i) setting minimum requirements for products entering the EU market, and (ii) consumer labels on material efficiency aspects such as product durability that could trigger environmentally sustainable purchase decisions. Subsequently, a methodological framework for a comprehensive durability scoring system that could be developed in standards is proposed, and the potential for these to be used as a basis for product legislation is explored. Potential durability criteria are listed, divided into technical, servicerelated and further aspects. Technical aspects include external factors that influence the durability of products such as drop/shock resistance. Service-related aspects include, for example, pre-purchase information provision on battery replaceability or availability of software updates. Other aspects include for example pro. T2 - EGG+ Electronics Goes Green 2024+ CY - Berlin, Germany DA - 18.06.2024 KW - Circular Economy KW - Durability KW - Material efficiency KW - Ecodesign KW - ESPR KW - Labelling KW - Consumer PY - 2024 SN - ISBN 978-3-00-079329-5 SP - 56 EP - 62 AN - OPUS4-60399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lu, Xin A1 - Hicke, Konstantin A1 - Krebber, Katerina T1 - Distributed fiber optic sensing for monitoring of underground facilities N2 - Distributed fiber optic sensing (DFOS) technique is a promising and robust non-destructive testing tool that can seamlessly acquire environmental conditions over large scales. Therefore, it has found extensive applications in structural health monitoring. Its appeal for monitoring underground facilities lies in the intrinsic properties of the optical fiber, such as immunity to magnetic interference, small size, chemical inertia, etc. This paper provides a concise overview of DFOS applications in underground facility monitoring. Following a brief introduction to the workingbnprinciple of the DFOS technique, various examples are provided to demonstrate how distributed fiber sensors contribute to monitoring underground facilities. The paper presents unpublished field test results with an emphasis in the energy sector, including monitoring gas storage facilities, geothermal reservoir exploration, and ground movement detection. Furthermore, the paper identifies several directions for enhancing the DFOS system. T2 - SPIE Photonics Europe CY - Strasbourg, France DA - 07.04.2024 KW - Structure health monitoring KW - Geothermal borehole KW - Distributed fiber optic sensing KW - Ground movement KW - Leakage detection PY - 2024 DO - https://doi.org/10.1117/12.3023571 SN - 0277-786X VL - 13001 SP - 1 EP - 10 PB - SPIE AN - OPUS4-60384 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Stührenberg, Jan A1 - Tandon, Aditya A1 - Dragos, Kosmas A1 - Bartholmai, Matthias A1 - Strangfeld, Christoph A1 - Smarsly, Kay T1 - Implementation and validation of robot-enabled embedded sensors for structural health monitoring N2 - In the past decades, structural health monitoring (SHM) has matured into a viable supplement to regular inspections, facilitating the execution of repair and maintenance work in the early stages of structural damage. With the advent of wireless technologies and advancements in information and communication technologies, civil infrastructure has been increasingly instrumented with wireless sensor nodes to record, analyze, and communicate data relevant to SHM. A promising method for SHM is to embed sensors directly into concrete for recording SHM data from inside structural elements. In this paper, a sensor system for embedment into concrete is proposed, able to assess SHM data recorded from concrete. Power is supplied to the sensors on-demand by quadruped robots, which also collect the SHM data via radio-frequency identification (RFID), providing an automated and efficient SHM process. In laboratory experiments, the capability of the sensor system of automatically collecting the SHM data using quadruped robots is validated. In summary, the integration of RFID technology and robot-based inspection presented in this study demonstrates a vital approach to evolve current SHM practices towards more digitalized and automated SHM. T2 - 11th European Workshop On Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Structural health monitoring KW - RFID-based sensors KW - Smart sensors KW - Embedded sensors KW - Legged robots KW - Quadruped robots PY - 2024 SP - 1 EP - 8 AN - OPUS4-60335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ronen, A. A1 - Vogel, Christian A1 - Leube, Peter A1 - Ben Efraim, R. A1 - Nir, O. A1 - Chaudhary, M. A1 - Futterlieb, M. A1 - Panglisch, S. T1 - DEFEAT-PFAS: Detection, Quantification, and Treatment of Per- and Polyfluoroalkyl Substances (PFAS) in Groundwater N2 - The research project focuses on tackling the detection, measurement, and elimination of per- and polyfluoroalkyl substances (PFAS) from polluted groundwater, with a particular emphasis on addressing short (C4-C7) and ultrashort (C1-C3) chain PFAS. Given the widespread use of PFAS in various products, they are commonly found in groundwater near industrial and military sites in Germany and Israel. Moreover, recent regulations limiting the use of long chain PFAS have led industries to shift towards shorter chain alternatives. Hence, our efforts are geared towards refining detection, quantification, and removal methods for short and ultrashort chain PFAS. In terms of detection, ww are developing passive sampling devices capable of collecting and tracking the temporal distribution of PFAS species in groundwater. This will enable us to analyze contaminations in German and Israeli groundwater using cutting-edge analytical techniques. Additionally, contaminated groundwater will undergo a two-stage treatment process aimed at concentrating the relatively low PFAS concentrations using innovative membrane technologies such as closed-circuit reverse osmosis and mixed matrix composite nanofiltration membrane adsorbers. Subsequently, the streams containing higher PFAS concentrations will be treated through coagulation, with the remaining PFAS being adsorbed onto carbonaceous nanomaterials. The outcome of this research will include the creation of advanced tools for detecting, measuring, and eliminating PFAS from polluted groundwater, while also enhancing our understanding of the scope of these contaminations. T2 - German Israeli Water Technology Status Seminar CY - Koblenz, Germany DA - 18.06.2024 KW - Ground water KW - Per- and Polyfluoroalkyl substances (PFAS) KW - Remediation PY - 2024 UR - https://indico.scc.kit.edu/event/4029/attachments/7552/12045/Proceedings_Ger-Isr-Coop_Status-Seminar-2024.pdf SP - 33 EP - 36 AN - OPUS4-60331 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Völzke, Holger T1 - Brittle Failure Limits of Spent Fuel Claddings Subjected to Long-Term Dry Interim Storage Conditions N2 - The mechanical properties of spent fuel claddings can be adversely affected under the conditions of long-term dry interim storage, so that the failure limits may be reached in case of mechanical loads during handling or transport after storage. Pre-storage drying and the early stage of interim storage can expose the cladding to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation and pool storage. During slow cooling of a cladding tube under internal pressure, radial hydrides may precipitate in zirconium-based cladding alloys. This can lead to embrittlement of the material and sudden failure of the cladding integrity under mechanical stress. In order to prevent brittle failure, numerical methods are being developed to predict the mechanical behaviour and identify limiting conditions. Experimental investigations, numerical analyses and evaluation methods are discussed. An established experimental method for characterising cladding materials is the Ring Compression Test (RCT). Some test results on irradiated cladding tubes after operation in pressure water reactors are publicly available. However, it is helpful to carry out studies on unirradiated surrogate claddings with similar material properties to reduce the effort associated with irradiated samples in hot cells and to perform material tests with a wider range of parameters. On the basis of such experimental data, load-displacement curves have been numerically analysed for a selection of cladding materials. Radial hydrides can cause a sample to break suddenly due to fracture even at low deformation. Noticeable load drops in the RCT are caused by unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting adjacent hydrides. The cohesive zone approach was used to simulate the failure process taking into account the radial hydride morphology. The developed method can adequately describe both the deformation and failure behaviour of irradiated as well as unirradiated claddings of zirconium-based alloys with radial hydrides under RCT conditions. Limiting conditions can be expressed in terms of fracture energy and cohesive strength. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Plants - Meeting the Moment CY - Vienna, Austria DA - 10.06.2024 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 SP - 1 EP - 10 AN - OPUS4-60323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barretto, T. A1 - Gentes, S. A1 - Braun, J. A1 - Averin, Anton A1 - Lecompagnon, Julien A1 - Stroncik, N. T1 - Automated non-destructive internal corrosion detection on radioactive drums (ZIKA) N2 - The aim of the ZIKA research project, funded by the BMBF funding program FORKA (FKZ:15S9446 A-C), is the automated detection of internal corrosion of radioactive drums using non-destructive testing (NDT). The newly gained findings will be combined with research results from the previous project EMOS (FKZ:15S9420), which dealt with the external damage of drums. Using NDT, internal corrosion and possible internal sources of damage can be identified before they become a safety-relevant issue. However, if internally sourced damages can be seen externally, the integrity of the damaged drum is no longer guaranteed, which has significant consequences. Therefore, early detection before integrity failure is of particular importance for interim storage facilities with low- and medium-level radioactive waste drums. T2 - Kerntechnik 2024 CY - Leipzig, Germany DA - 11.06.2024 KW - Corrosion detection KW - Non-destructive testing KW - Automated inspection system PY - 2024 SP - 1 EP - 5 AN - OPUS4-60322 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin A1 - Farago, Patrick A1 - Mayer, Felix ED - Angulo, Sergio ED - Landmann, Mirko T1 - New sources for secondary gypsum N2 - In order to protect natural gypsum deposits and to compensate for the decreasing amount of Flue Gas Desulfurization (FGD) gypsum it is necessary to develop and explore new sources of gypsum. For this purpose, the potentials of different gypsum wastes are investigated in the study “GipsRec 2.0”, funded by the Federal Ministry of Education and Research (Germany). On the one hand, the project worked on a new processing technology for gypsum fiberboards (GFB). While the recycling of gypsum plasterboards has already been carried out on an industrial scale for several years, the recycling of gypsum fiberboards (GFB) has proven to be challenging. Gypsum fiberboards from demolition sites and offcuts from GFB production were used for these investigations. The tests were conducted on a technical scale. Furthermore, various synthetic gypsums are being investigated with regard to their suitability for gypsum production. The analyses are carried out on production residues. In this project, a promising process for gypsum fiberboard recycling could be developed, as well as other waste gypsums are investigated and evaluated with regard to their potential as secondary raw material. In addition, selected process routes are assessed for their environmental impact using a life cycle assessment (LCA) approach. T2 - RILEM - V International Conference Progress of Recycling in the Built Environment CY - Weimar, Germany DA - 10.10.2023 KW - Gypsum recycling KW - Gypsum fiberboards and synthetic gypsum KW - Environmental evaluation PY - 2023 VL - V SP - 1 EP - 10 PB - RILEM Publications Sarl CY - Bagneux, France AN - OPUS4-60315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Schukar, Marcus A1 - Woody, Paul A1 - Wang, Bin A1 - Breithaupt, Mathias A1 - Kriegsmann, Andreas T1 - Distributed fiber optic strain sensing for structural health monitoring of 70 MPa hydrogen vessels N2 - We report on the development and testing of 70 MPa hydrogen pressure vessels with integrated fiber optic sensing fibers for automotive use. The paper deals with the condition monitoring of such composite pressure vessels (CPVs) using the optical backscatter reflectometry (OBR) applied for a distributed fiber optic strain sensing along fully integrated polyimide-coated single-mode glass optical fiber (SM-GOF). The sensing fibers were embedded into the vessel structure by wrapping them over the polymer liner during the manufacturing process of the carbon fiber reinforced polymer (CFRP). Detecting local strain events by the integrated fiber optic sensors can be an opportunity for monitoring the material degradation of CPVs under static and cyclic loading. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Fiber optic sensor KW - Distributed strain sensing KW - Composite pressure vessel KW - Structural health monitoring KW - Fiber-reinforced plastics PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-603105 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-60310 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -