TY - JOUR A1 - Meng, M. A1 - Zhang, R. A1 - Fa, X. A1 - Yang, J. A1 - Cheng, Z. A1 - Qiao, X. A1 - Ou, J. A1 - Würth, Christian A1 - Resch-Genger, Ute T1 - Core−Shell NaYF4:Yb3+/Tm3+@NaGdF4:Ce3+/Eu3+ Nanoparticles for Upconversion and Downconversion Dual-Mode Fluorescence-Based Temperature Sensing JF - Applied Nano Materials N2 - NaYF4 as the core and NaGdF4 as the outer layer were used to obtain NaYF4:Yb3+/Tm3+@NaYF4:Ce3+/Eu3+ nanoparticles. Physical and morphological investigations indicated that the obtained nanoparticles were prepared in a hexagonal shape, with the NaGdF4 shell layer uniformly encapsulated on the NaYF4 core. Strong Tm3+ upconversion emission peaks were observed for a 980-nm-laser-excited sample, while strong Eu3+ downconversion emission peaks were observed for a 254-nm-laser-excited sample. By zonal doping of Tm3+ and Eu3+, their fluorescence intensity can be significantly increased; more importantly, simultaneous temperature measurements with dual-mode upconversion/downconversion can be achieved. The temperature measurement properties of the dual mode were also investigated, and it was discovered that the upconversion 3F3 → 3H6 and 1G4 → 3F4 thermocouple energy levels gave the best temperature measurements with maximum absolute and relative sensitivities of 0.0877 K−1 and 1.95% K−1, respectively, which are better than the current temperature measurement sensitivities of most rare-earth-based materials. This material was prepared as fiber-optic temperature-sensing probes to detect the temperature in the environment in real time and was found to perform excellently for temperature measurement. KW - Upconversion nanoparticle KW - Lanthanide KW - Sensing; temperature KW - Photophysics PY - 2022 DO - https://doi.org/10.1021/acsanm.2c01611 VL - 5 IS - 7 SP - 9266 EP - 9276 PB - American Chemical Society AN - OPUS4-55363 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -