TY - CONF A1 - Madkour, Sherif A1 - Penner, P. A1 - Zhang, X. A1 - Gölzhäuser, A. A1 - Schönhals, Andreas T1 - Dielectric investigations on carbon nanomembranes N2 - Multilayer carbon nanomembrances (CNMs) could pave the way for a new ultrathin functional conductive coatings with tunable electrical, optical, and chemical properties. Due to their molecular thickness, they can also be regarded as “interfaces without bulk” separating regions of different gaseous, liquid, or solid components and controlling the materials exchange between them, making them optimal materials for membranes applications. Furthermore, their physical and chemical properties depend strongly on their structure, molecular composition, and the surroundings of either sides, thus allowing for tailored properties. Here, nanolayers of Aromatic p-terphenylthiol (TPT) self-assembled into 2D carbon monolayers (thickness - 1.6 nm) were synthesized and further crosslinked by ion bombardment, forming CNMs. Here, though a recently developed multilayer nanosheets routine, stacks of 5, 10, 15 and 20 TPT sheets where transferred on top of each other forming a multilayered CNMs. However, this transfer routine could introduce some intrinsic defects to the sheets, which would alter the molecular composition and / or structure, thus consequently the CNMs properties. Therefore, it is essential to characterize defects in “pure” TPT nanomembranes, before tailoring the molecular compositions, e.g. adding functional groups. For this reason, broadband dielectric spectroscopy (BDS) was utilized to characterize any defects that could be rasied during preparation. Due the structure of pure TPT membranes, no dipole moment should exsist. However, the presence of other elements, e.g. water or sulphur, would result in a dipole moment that could be probed by BDS. As a main result, for all different stacked-layer numbers, a clear relaxation process is seen, which moves to higher frequencies with increasing the temperature. The temperature dependence of the relaxation rate of this process is independent of film thickness and can be well described by a common VFT function, hence a corporative motion. This relaxation process was assigned to intrinisic defects in the membranes, introduced during preparation, which was further confimed by a detailed anaylsis of the dielectric strength. This is the first BDS measurment on TPT CNMs. T2 - 9th International Conference on Broadband Dielectric Spectroscopy and its Applications CY - Pisa, Italy DA - 11.09.2016 KW - Carbon nanomembranes PY - 2016 AN - OPUS4-37527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -