TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Rades, Steffi A1 - Oswald, F. A1 - Narbey, S. A1 - Radnik, Jörg T1 - Time dependent Analysis of Morphology, Elemental and Chemical Composition of CH3NH3PbI3/TiO2 Solar Cell Layered System N2 - The motivation of this work is to produce thin films perovskite solar cells with constant high light conversion efficiency over time. Loss of efficiency may be caused by structural and/or chemical alterations of the complex layered system. As these changes might take place either in the bulk and/or on the surface of the stratified material, analytical tools addressing both key issues are selected and combined. SEM/EDS combined with XPS were chosen as appropriate methodical approach to characterise perovskite laboratory cells in depth and complementary on top, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by three porous thin films of TiO2, ZrO2 and a thick monolithic carbon. The TiO2 film is subdivided into a dense layer covered by a porous one constituted of nanoparticles with a truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. After infiltration of perovskite solution and annealing, EDS spectral maps on cross-sections of the specimen have been measured. The distribution of relevant elements – Si, Sn, Ti, Zr and C – correlates conclusively with layers visible in the acquired SEM images. Lead and iodine are distributed throughout the porous layers C, ZrO2 and TiO2. Specimens were exposed to ambient daylight for 7 weeks. In a SEM micrograph taken of the cross-section of a sample after illumination, the glass substrate and all layers FTO, TiO2, ZrO2 as well as C are clearly identified. EDS data have been acquired under the same measurement conditions as before the illumination. It was found that several weeks of ambient daylight did not change significantly the qualitative elemental composition of lead and iodine throughout the solar cell system. It was confirmed with EDS that nanoparticles identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite crystals. However, a time-dependent compositional and chemical altering was observed with XPS for the near-surface region of the outermost ~10 nm after 2 months of illumination. T2 - EMAS 2017 - 15th European Workshop on MODERN DEVELOPMENTS AND APPLICATIONS IN MICROBEAM ANALYSIS and IUMAS-7 Meeting CY - Konstanz, Germany DA - 07.05.2017 KW - Perovskite KW - Layer analytics KW - SEM/EDX KW - XPS KW - Solar cells PY - 2017 AN - OPUS4-40253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -