TY - JOUR A1 - Seher, Julia A1 - Fröba, M. T1 - Shape matters: The effect of particle morphology on the fast-charging performance of LiFePO4/C nanoparticle composite electrodes JF - ACS Omega N2 - For the successful use of lithium-ion batteries in automotive applications, reliable availability of high storage capacity and very short recharging times are essential. In order to develop the perfect battery for a certain application, structure–property relationships of each active material must be fully understood. LiFePO4 is of great interest due to its fast-charging capability and high stability regarding its thermal resistance and chemical reactivity. The anisotropic lithium-ion diffusion through the LiFePO4 crystal structure indicates a strong dependence of the electrochemical performance of a nanostructured active material on particle morphology. In this paper, the relationship of the particle morphology and fast-charging capability of LiFePO4/C core/shell nanoparticles in half-cells was studied. For this purpose, a new multistep synthesis strategy was developed. It involves the combination of a solvothermal synthesis followed by an in situ polymer coating and thermal calcination step. Monodisperse rodlike LiFePO4 nanoparticles with comparable elongation along the b-axis (30–50 nm) and a varying aspect ratio c/a (2.4–6.9) were obtained. A strong correlation of the fast-charging capability with the aspect ratio c/a was observed. When using LiFePO4 nanoparticles with the smallest aspect ratio c/a, the best electrochemical performance was received regarding the specific capacity at high C-rates and the cycling stability. A reduction of the aspect ratio c/a by 30% (3.6 to 2.4) was found to enhance the charge capacity at 10 C up to an order of magnitude (7.4–73 mA h·g–1). KW - LiFePO4 KW - Schnellladung KW - Nanoparticles KW - Carbon KW - Chemical synthesis KW - Electrochemical cells KW - Materials PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-533004 DO - https://doi.org/10.1021/acsomega.1c03432 SN - 2470-1343 VL - 6 IS - 37 SP - 24062 EP - 24069 PB - American Chemical Society CY - Washington, DC AN - OPUS4-53300 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -