TY - JOUR A1 - Yu, D. A1 - Kleemeier, M. A1 - Wu, Guang Mei A1 - Schartel, Bernhard A1 - Liu, W.Q. A1 - Hartwig, A. T1 - Phosphorus and silicon containing low-melting organic-inorganic glasses improve flame retardancy of epoxy/clay composites JF - Macromolecular Materials and Engineering N2 - New low-melting organic–inorganic glassy polymers containing phosphorus and silicon are synthesized by the reaction between phenylphosphonic acid and methyltrichlorosilane or methyltriethoxysilane. They possess both low-softening points and high onset decomposition temperatures, which are favorable for preparing flame retardant composites. Although the glass by itself is sensitive to water, the composites are not significantly affected in that way. For glass/clay/epoxy composites glass transition temperature (Tg) as well as storage modulus increase with the glass amount. The glasses improve flame retardancy significantly due to flame inhibition and the formation of fire residue working as protection layer during burning. The total heat evolved is reduced by 23–28% for using 5–15 wt.% glass and the maximum HRR even by 58–48%. The latter effect decreases with increasing glass amount due to an adulterate residue deformation. The combination of glass and clay is proposed as a possible route to enhance flame retardancy. KW - Clay KW - Epoxy resin KW - Flame retardancy KW - Organic-inorganic polymer KW - Low-melting glass PY - 2011 DO - https://doi.org/10.1002/mame.201100014 SN - 1438-7492 SN - 1439-2054 VL - 296 IS - 10 SP - 952 EP - 964 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-24516 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -