TY - JOUR A1 - Stark, Wolfgang A1 - Jaunich, Matthias A1 - McHugh, J. T1 - Carbon-fibre epoxy prepreg (CFC) curing in an autoclave analogue process controlled by dynamic mechanical analysis (DMA) T2 - Polymer Testing N2 - Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification. PB - Elsevier Science CY - Amsterdam [u.a.] KW - Prepreg KW - CFC KW - Curing KW - DMA KW - DSC KW - Autoclave KW - Gelation KW - Vitrification KW - Glass transition PY - 2013 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/29479 AN - OPUS4-29479 SN - 0142-9418 VL - 32 IS - 8 SP - 1487 EP - 1494 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany