TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Beier, H. Th. T1 - Fatigue strength and life determination of weldments based on fracture mechanics T2 - 3rd international Symposium on fatigue design and material defects (FDMD 2017) N2 - The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common ΔK concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit and the finite life branch of the S-N curve are determined. Besides a brief introduction into the approach, validation examples are presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels (S355NL and S960QL) of quite different strengths, different weld geometries due to different welding techniques (WIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5. PB - ScienceDirect CY - Lecco, Italy T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Weldments KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/43850 AN - OPUS4-43850 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438500 SN - 2452-3216 VL - 7 SP - 407 EP - 414 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany