TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Hellmann, D. T1 - Fracture mechanics model for predicting fatigue strength of metallic alloys containing large second phase particles T2 - ECF 19 - 19th European conference on fracture - Fracture mechanics for durability, reliability and safety T2 - ECF 19 - 19th European conference on fracture - Fracture mechanics for durability, reliability and safety CY - Kazan, Russia DA - 2012-08-26 KW - Fatigue strength KW - S-N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks KW - Bruchmechanik KW - Schwingfestigkeit KW - Bauteilbewertung PY - 2012 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/27278 AN - OPUS4-27278 SN - 978-5-905576-18-8 IS - Proceeding-ID 116 SP - 1 EP - 14 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany