TY - CONF A1 - Vöse, Markus A1 - Fedelich, Bernard T1 - Simulation of creep damage in a Cu polycrystal under multiaxial loading T2 - CREEP 2015 - 13th International conference on creep and fracture of engineering materials and structures N2 - The stress States of components under Service conditions differ in general from the loading conditions that are routinely applied during material testing. When data that results, e.g., from uniaxial testing should be used for lifetime assessment, a good understanding of the failure behaviour in dependence of the stress state is necessary. For polycrystalline materials under high temperature loading, the development of creep damage is one important factor that limits a component’s lifetime. For cases where creep damage is related to the nucleation and growth of grain boundary cavities, the local normal stress acting on a grain boundary has been found to have a strong influence on the damage development. Hence, creep damage is usually localized along planes that lie perpendicular to the maximum principal tensile stress. T2 - CREEP 2015 - 13th International conference on creep and fracture of engineering materials and structures CY - Toulouse, France DA - 31.05.2015 PY - 2015 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/33455 AN - OPUS4-33455 SP - 175 EP - 176 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany