TY - GEN A1 - Pfennig, Anja A1 - Wojtas, P. A1 - Spengler, I. A1 - Linke, B. A1 - Kranzmann, Axel ED - Villacampa, V. ED - Brebbia, C.A. ED - Mammoli, A.A. T1 - Influence of heat treatment on the corrosion behavior of steels exposed to CCS environment T2 - Energy and Sustainability III N2 - The influence of heat treatment on pit corrosion needs to be considered to guarantee reliability and safety during the injection of compressed emission gasses – mainly containing CO2 – into deep geological layers (CCS-technology, Carbon Capture and Storage). In laboratory experiments different heat treated steels used as injection pipe with 13% Chromium and 0.46% Carbon (X46Cr13, 1.4034) as well as 0.2% Carbon (X20Cr13, 1.4021) were tested. Also X5CrNiCuNb16-4 (1.4542) was investigated as typical steel used for geothermal pumps. Keeping stable environmental conditions in laboratory experiments the samples were exposed to the distinct synthetic aquifer environment saturated with technical CO2 at a flow rate of 3 l/h for up to 6 months. Independent of the exposure time the least amount of pits is found on hardened steels with martensitic microstructure where X5CrNiCuNb16-4 shows fewer pits than X46Cr13 and X20Cr13. Regarding steels with similar Cr-content the higher Ccontent in 1.4034 results in fewer pits compared to 1.4021. KW - Steel KW - Heat treatment KW - Pit corrosion KW - CCS KW - CO2-injection KW - CO2-storage PY - 2011 SN - 978-1-84564-508-3 DO - https://doi.org/10.2495/ESUS110411 SN - 1746-448X SN - 1743-3541 SP - 487 EP - 498 PB - WIT Press CY - Southampton, UK AN - OPUS4-23840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -