TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Bork, Claus-Peter T1 - Corrosion fatigue of X46Cr13 at 60 °C exposed to CO2-saturated geothermal brine T2 - EUROCORR 2012 - The European corrosion congress N2 - In geothermal power plants the materials used in pumps are loaded cyclically and exposed constantly to the highly corrosive hot thermal water. The lifetime reduction of AISI 420C (X46Cr13, 1.4034) is demonstrated in in-situ-laboratory experiments (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO2). S-N plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion fatigue behavior. Maximum number of cycles (here 12.5 x 106 cycles to failure) is reached at σa =173 MPa. No typical fatigue strength exists and passive corrosion fatigue may be identified as failure cause. T2 - EUROCORR 2012 - The European corrosion congress CY - Istanbul, Turkey DA - 2012-09-09 KW - Steel KW - Corrosion fatigue KW - Corrosion chamber KW - CCS KW - CO2-storage PY - 2012 SP - 1 EP - 11 AN - OPUS4-28586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -