TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Eich, Gerd T1 - Galvanised constructional elements in contact with prestressing steel tendons JF - Materials and corrosion N2 - In order to clarify under which practical conditions real risks for hydrogen-induced stress corrosion cracking of prestressing steels exist laboratory investigations in aqueous solutions and concrete as well as tests with stressed prestressing steels were carried out. While different distances between steel and zinc (cathode and anode) showed only a negligible influence on the polarisation of the steel a significant dependence on the area ratio steel/zinc was observed. A critical area ratio of 10:1 can be defined above which polarisation of the steel to hydrogen evolution potentials is unlikely. The results obtained in the laboratory concerning the critical area ratio were confirmed by on-site investigations in a precasting plant. Exposure tests with hydrogen loading did not lead to fractures during the testing time for approved prestressing steels. The characteristic mechanical values determined immediately after the hydrogen loading tests did not show significant changes. Thus, an indirect contact between prestressing steels and galvanised elements can be estimated as uncritical. But a direct contact has to be excluded by compliance with DIN 1045-1, i.e minimal distance of 2 cm between prestressing steel and galvanised elements. PY - 2008 DO - https://doi.org/10.1002/maco.200804114 SN - 0947-5117 SN - 1521-4176 VL - 59 IS - 2 SP - 131 EP - 138 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-16724 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -