TY - JOUR A1 - Huang, M.D. A1 - Becker-Ross, H. A1 - Okruss, M. A1 - Geisler, S. A1 - Florek, S. A1 - Richter, Silke A1 - Meckelburg, Angela T1 - Direct determination of fluorine in niobium oxide using slurry sampling electrothermal high-resolution continuum source molecular absorption spectrometry T2 - Spectrochimica acta B N2 - Aiming for a round-robin test, a new method for the direct determination of fluorine in niobium oxide has been developed. It is based on the use of high-resolution molecular absorption spectra of calcium mono-fluoride (CaF) generated in the graphite tube, combined with the slurry sampling technique. The absorption measurement was performed at the 606.44 nm CaF rotational line. By using graphite tubes with zirconium carbide (ZrC) modified platform, the molecular absorption sensitivity of CaF has been improved by a factor of 20, and no additional chemical modifier was necessary. Generally, non-spectral interferences were observed in the presence of HCl, H2SO4, and H3PO4. For HCl, additional spectral interference occurred due to an overlap of the absorption spectra of CaF and CaCl. However, due to the absence of these mentioned substances in the current material, such interferences do not exist for this application. The characteristic mass found for the CaF 606.44 nm line was 0.1 ng; the limit of detection was 5 mg fluorine per kg solid sample (3σ criterion). The results obtained by the method were within the range of certified values. Comparing to the classical method such as the pyrohydrolysis-photometric method, the developed new method showed clear advantages regarding sensitivity and specificity. The time requirement for one sample analysis was strongly shortened from several hours to only some minutes. PB - Elsevier CY - Amsterdam KW - Continuum source molecular absorption spectrometry KW - Fluorine determination KW - Niobium oxide KW - Slurry sampling PY - 2014 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/30655 AN - OPUS4-30655 SN - 0584-8547 SN - 0038-6987 VL - 94-95 SP - 34 EP - 38 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany