TY - CONF A1 - Griesche, Axel A1 - Mente, Tobias A1 - Falahat, Ala'A . M. Al A1 - Tengattini, Alessandro A1 - Dal Pont, Stefano A1 - Kardjilov, Nikolay T1 - Crystallographic phase transformations and corresponding temperature distributions during gtaw of supermartensitic stainless steel visualized by nbei N2 - We investigated the phase transformations during butt-welding of supermartensitic steel plates with help of Neutron-Bragg-Edge Imaging (NBEI). Gas tungsten arc welding (GTAW) was used with a motorized torch allowing for automated weldments. The austenitization in the heat affected zone (HAZ) could be clearly visualized at λ = 0.39 nm, a wavelength smaller than the Bragg edge wavelengths of both austenite and martensite. The re-transformation into the martensitic phase during cooling was clearly detected. However, we observed an unexpected additional change in transmission at λ = 0.44 nm, a wavelength larger than the wavelength of the Bragg edges of both the martensitic and austenitic phases. We attribute this change to the Deybe-Waller-Factor that describes the temperature dependence of coherent scattering at a crystal lattice. The observed two-dimensional attenuation map corresponds well with a temperature distribution modelling by software macros in ANSYS [3]. Here, the absolute temperature values could be achieved by calibrating the modelled attenuation with help of a thermocouple placed at the steel plate. This allows in return for a direct two-dimensional temperature reading based on the Debye-Waller-relation between neutron attenuation and sample temperature. T2 - WCNR-12 CY - Idaho Falls, Id, USA DA - 02.06.2024 KW - Neutron KW - Radiography KW - Welding PY - 2024 AN - OPUS4-60242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -