TY - JOUR A1 - Konadu, D. S. A1 - Pistorius, P. G. H. A1 - Du Toit, M. A1 - Griesche, Axel T1 - Solidification cracking susceptibility of ferritic stainless steels using Modified Varestraint Transvarestraint (MVT) method T2 - Sadhana - Academy proceedings in engineering sciences N2 - The Modified Varestraint Transvarestraint (MVT) test was used to investigate the solidification cracking susceptibility of an unstabilised, a Nb-stabilised and two (Ti + Nb) dual-stabilised ferritic stainless steels. Two different welding speeds of 6 and 3 mm/s using autogenous gas tungsten arc welding were employed. At the welding speed of 6 mm/s, the high-content (Ti + Nb) steel was resistant and the Nb-stabilised steel was marginally susceptible to solidification cracking. At the welding speed of 3 mm/s, the Nb and the high (Ti + Nb) steels were found to be marginally susceptible to solidification cracking while the unstabilised and low-content (Ti + Nb) grades were resistant to solidification cracking. The weld metal microstructures transverse to the welding direction revealed columnar grains in all the samples for both welding speeds. The ferritic stainless steels were generally resistant to solidification cracking, except the Nb-stabilised steel, which was marginally susceptible to solidification cracking. PB - Springer KW - Susceptibility KW - Modified Varestraint Transvarestraint KW - Solidification cracking KW - Ferritic stainless steel KW - Microstructure KW - Welding PY - 2019 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/48938 AN - OPUS4-48938 SN - 0973-7677 VL - 44 IS - 9 SP - Article Number: UNSP 194 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany