TY - CONF A1 - Laquai, René A1 - Schaupp, Thomas A1 - Müller, Bernd R. A1 - Griesche, Axel A1 - Bruno, Giovanni A1 - Kannengießer, Thomas T1 - 3D imaging of hydrogen assisted cracking in metals using refraction enhanced synchrotron CT T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering (Proceedings) N2 - Hydrogen in metals can cause a degradation of the mechanical properties with possible subsequent hydrogen assisted cracking (HAC). Though, the mechanism of HAC is not completely understood yet and thus suitable methods for in situ investigations to characterise the crack formation are needed. X-ray computed tomography (CT) is a well-known tool for analysing these properties. However, the effective resolution of the detector system limits the detection of small defects by CT. Analyser based imaging (ABI) takes advantage of x-ray refraction at interfaces between volumes of different density, i.e. of cracks, pores, inclusions, etc., within the sample to detect defects smaller than the resolution of the detector system. In this study, measurements on an aluminium alloy weld showed that ABI allows us to resolve the 3D structure of cracks undetected by absorption based CT. Prospective investigations will analyse HAC in steels. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 2015-09-15 KW - Wasserstoffversprödung KW - Wasserstoffunterstützte Rissbildung KW - Röntgenrefraktion KW - CT KW - Hydrogen embrittlement (HE) KW - Hydrogen assisted cracking (HAC) KW - Aluminium alloy KW - X-ray refraction KW - Analyser based imaging KW - Computed tomography (CT) KW - Synchrotron radiation PY - 2015 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/34287 AN - OPUS4-34287 SN - 1435-4934 SP - 1217 EP - 1224 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany