TY - JOUR A1 - Schartel, Bernhard A1 - Weiß, André A1 - Mohr, F. A1 - Kleemeier, M. A1 - Hartwig, A. A1 - Braun, Ulrike T1 - Flame retarded epoxy resins by adding layered silicate in combination with the conventional protection-layer-building flame retardants melamine borate and ammonium polyphosphate T2 - Journal of applied polymer science N2 - The pyrolysis and flammability of phosphonium-modified layered silicate epoxy resin nanocomposites (EP/LS) were evaluated when LS was combined with two flame retardants, melamine borate (MB) and ammonium polyphosphate (APP), that also act via a surface protection layer. Thermogravimetry (TG), TG coupled with Fourier Transform Spectroscopy (TG-FTIR), oxygen index (LOI), UL 94 burning chamber (UL 94) and cone calorimeter were used. The glassy coating because of 10 wt % MB during combustion showed effects in the cone calorimeter test similar to nanodispersed LS, and somewhat better flame retardancy in flammability tests, such as LOI and UL 94. Adding APP to EP resulted in intumescent systems. The fire retardancy was particularly convincing when 15 wt % APP was used, especially for low external heat flux, and thus, also in flammability tests like LOI and UL 94. V0 classification is achieved when 15 wt % APP is used in EP. The flame retardancy efficiency of the protection layers formed does not increase linearly with the MB and APP concentrations used. The combination of LS with MB or APP shows antagonism; thus the performance of the combination of LS with MB or APP, respectively, was disappointing. No optimization of the carbonaceous-inorganic surface layer occurred for LS-MB. Combining LS with APP inhibited the intumescence, most probably through an increase in viscosity clearly above the value needed for intumescent behavior. PB - Wiley InterScience CY - Hoboken, NJ KW - Nanocomposites KW - Fire retardance KW - Thermosets KW - Organoclay KW - Ammonium polyphosphate KW - Melamine borate PY - 2010 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/21725 AN - OPUS4-21725 SN - 0021-8995 SN - 1097-4628 VL - 118 IS - 2 SP - 1134 EP - 1143 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany