TY - CONF A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Influence of heat input on cooling rates and mechanical properties of laser hybrid welded thick structural steels N2 - The laser hybrid welding process offers many advantages such as the high penetration depth and high welding speed, and it is characterized by its low heat input compared to the arc-based welding processes, which makes the laser hybrid welding process as a suitable alternative process when welding thick-walled steels. However, there are some challenges when using laser hybrid welding process for thick steels. Due to the uneven cooling conditions and the inhomogeneous filler wire mixing, a typical laser hybrid weld can be divided into two different zones over the depth: the arc-dominated zone on the upper part and the laser-dominated zone in the root part. This leads to different mechanical properties in a laser hybrid welded joint. Due to the high cooling rates and the lack of filler wire in the laser-dominated zone, this area is more critical regarding the mechanical properties, especially the Charpy impact toughness. A low heat input can lead to undesired microstructure consisting of martensite, hardening and deteriorated impact toughness due to the high cooling rate, where higher heat inputs can lead to grain-coarsening and even loss of impact strength. This study deals with the influence of the welding speed and resulting heat input on the cooling rates, the microstructure and the mechanical properties of single-pass laser hybrid welded steels of S355J2 with thickness up to 30 mm. The experiments were performed with a 20-kW fibre laser system and a contactless electromagnetic weld backing on up to 30 mm thick steels in butt-joint configuration in 1G welding position. The cooling time was measured in three different locations near to fusion lines corresponding to different heights of the seam using a special configuration with pyrometers, collimators, and optical fibres. The test specimens for the Charpy impact testing and tensile testing were extracted in up to three different depths. Based on the experiments, a heat input of 1.3 kJ/mm - 1.6 kJ/mm, 2 kJ/mm - 2.4 kJ/mm and 3.7 kJ/mm were recommended when single-pass laser hybrid welding of 20 mm, 25 mm and 30 mm thick structural steels in regard to the minimum requirements of the mechanical properties, respectively. The optical measurement of the cooling times in different depths could be carried out reproducibly. T2 - Advances in Welding and Metal Additive Manufacturing Technologies 2023 CY - Istanbul, Türkiye DA - 30.10.2023 KW - Laser hybrid welding KW - Electromagnetic backing KW - Charpy impact toughness KW - Thick-plate welding KW - Thermal cycles PY - 2023 AN - OPUS4-58942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -