TY - JOUR A1 - Höhne, Patrick A1 - Mieller, Björn A1 - Rabe, Torsten T1 - Slurry development for spray granulation of ceramic multicomponent batches T2 - Journal of Ceramic Science and Technology N2 - The granules commonly yielded by spray drying procedures exhibit a hard shell and an irregular, dimpled shape, which is often described as donut-like morphology. Sintered parts produced from such granules suffer from microstructural defects and reduced mechanical properties resulting from these disadvantageous granule properties. Using the example of alumina, zirconia and zirconia-toughened alumina (ZTA) batches, this paper shows that the morphology of the granules can be tuned by adjusting slurry stability. High zeta potential is essential to optimally disperse the particles. But to achieve spherical and soft granules the electrostatic repulsion forces between the particles should be reduced before spray granulation. Electrostatic repulsion forces were changed with the addition of nitric acid. Measurements of zeta potential and viscosity, as well as sedimentation investigations with an optical centrifuge were used for precise slurry assessment as a major precondition for optimal and reproducible adjustment of slurries before spray drying. Sedimentation analysis using an optical centrifuge was performed to investigate different influences like that of additive composition, solids content or pH-value on the sedimentation behavior. Adequately flocculated slurries lead to homogeneous, soft granules that can be easily deformed and pressed. The fraction of donut-shaped particles and the rigidity of granules were reduced. Consequently, the sintered parts produced from these granulates show improvements regarding porosity, pore size distribution, sintered density and biaxial strength. PB - Göller Verlag KW - Slurry optimization KW - Optical centrifugation KW - Destabilization KW - Spray drying KW - Biaxial strength PY - 2018 UR - https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/46225 AN - OPUS4-46225 SN - 2190-9385 VL - 9 IS - 3 SP - 327 EP - 336 AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany