FG Füge- und Schweißtechnik
The formation of acicular ferrite in the structure of weld deposits when welding carbon steels is often associated with the introduction of nonmetallic additives into the electrode material. Fe–alumina composite powders with alumina particles less than 1 µm were used as a filler for cored welding wire and the influence of aluminum oxide additives up to 2,5 wt.% on the structure of the welded seam was studied. It was shown that the addition of aluminum oxide to the welding wire led to the initiation of the formation of intragranular acicular ferrite in the weld deposit and to a more even distribution of hardness through the zones of weld seam.
Numerical models for thermo-mechanical simulation of the welding
residual stresses in laser beam and multi-pass arc welded joints are developed. The models describe the resulting microstructure as a function of the peak temperature, austenization time, cooling time and take into account the microstructure formed after
single or multiple thermal cycles. The results of simulations are validated by neutron diffraction experiments performed on FSD diffractometer at the IBR-2 pulsed reactor in FLNP JINR (Dubna, Russia). The elaborated numerical models are in good agreement
with obtained neutron diffraction data, which enable to study the influence of different conditions and process parameters on the distribution of residual welding stresses.