The series of impulse friction stir welding (IFSW) experiments for aluminum alloy 6082-T6 butt joints was performed to obtain micrographs, tensile and hardness test samples and to receive the validation data for a numerical model of the process. Impulse force and frequency were varied to determine the effect of individual process parameters on microstructure evolution and mechanical properties of the welded butt joints. A three-dimensional model was established to simulate temperature distribution, heat generation and contact state between the tool and the workpiece during IFSW. Based on the numerical simulation, the influence of the impulses on heat input, maximum weld temperatures and contact state was found. The combination of impulse force and frequency effected the grain refinement. The influence of impulses on the elongation and hardness of the welded joints during IFSW were determined.
In the current paper, the correlation between the physical size of additively built wire arc specimens and their structure and properties is studied. For the purpose of this work, two oval shaped specimens of different lengths were manufactured under the same technological conditions. The specimens have a length of 200 mm and 400 mm and will be referred to as L200 and L400. The microstructure of the samples was studied using X-ray diffraction analysis (XRD), optical microscopy, and scanning electron microscopy (SEM). The microhardness, yield strength (YS), and ultimate tensile strength (UTS) were determined and their correlation with the technological conditions of specimen build-up was clarified. The results of the carried out experiments indicated that the crystallographic structure of both specimens is similar. The scanning electron microscopy images show a higher concentration of irregularly shaped micro-pores formed near the edge of the αAl grains in the structure of the L400 specimen compared to the L200 one. An increase in the size of the αAl solid solution grains in the case of the L200 specimen towards its top section was noticed using optical microscopy. A slightly lower magnitude change was noticed concerning the L400 specimen. The increase in the size of the aluminum crystals was determined to be the increasing interpass temperature. Due to the much smaller thermal dissipation capacity of the smaller specimen, the interpass temperature of the same increased faster compared to the larger specimen. All of the above-mentioned factors led to a decrease in the microhardness of the specimens at higher stages of build-up. Since the specimens were deposited using similar layer deposition conditions, the resultant YS and UTS data are also highly comparable.
The mass production of metallic components requires high agility in the working process conditioned by the necessity of building details of different shapes and sizes. Changing the size of the components theoretically influences the thermal dissipation capability of the same, which could lead to a change in their structure and mechanical properties. This is particularly important when aluminum alloys are concerned. For this reason, two Al5356 single-track specimens were built using the same technological conditions of layer deposition by varying only their geometrical size. In all cases, the specimens were wire and arc additively manufactured (WAAM) using a process based on gas metal arc welding (GMAW) in the cold arc pulse mode (CAP). The structure of both specimens was studied and defects along their surfaces were detected in the form of micro-pores and micro-cracks. A high concentration of undissolved Mg particles was also detected, along with some standalone Si particles. Uniformity in the build-up process was achieved, which led to the formation of nearly identical structures in the specimens. Subsequently, the resultant mechanical properties were also highly comparable. This indicates that the geometry-related variation in thermal conditions has an insignificant influence on the component’s structure and properties.
For the purpose of this research, single track details were manufactured in the shape of thin walls with a length of 100 mm and a height of 80 mm. Two welding speeds were chosen for this experiment–13.3 mm/s and 20.0 mm/s corresponding to the following heat inputs: 120 J/mm and 80 J/mm. The gas metal arc welding (GMAW) method was used for the build-up of the specimens in the cold arc pulse mode. The structure of the specimens was studied using X-ray diffraction (XRD) analysis carried out with CuKα radiation with a wavelength of 1.5406 Ǻ, optical microscopy, scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDX). Furthermore, the Vickers hardness of the samples was determined using a ZwickRoell DuraScan 10/20 G5 unit at a force of 1 N. A preferred crystallographic orientation towards the (200) plane was observed in all cases, however a vastly textured structure was observed with inclusions of peaks in the (111), (220), and (311) crystallographic planes. The full width at half maximum (FWHM) of samples taken from different stages of build-up was calculated indicating an increase of the dislocation density at the more advanced stages of specimen growth. Despite that an increase of the hardness was observed towards the top of both specimens. This is attributed to the change in the structure of the αAl + Si formations from an irregular one at the bottom of the specimens, towards a fibrous one at the top. The results are discussed in regard to the optimization of the build-up process during wire arc additive manufacturing (WAAM).
Neuartige, werkstoffgerechte Fügeverfahren für Faserkunststoffverbunde setzen die Erwärmung der Materialien voraus. Um die damit verbundenen komplexen Temperaturfelder und -verläufe vorherzusagen, haben das Fraunhofer IAP und die BTU Cottbus-Senftenberg numerische Verfahren entwickelt. Mit diesen können auch verschiedene Strahlungsquellen und Prozessabläufe simuliert werden.
Dieser Beitrag stellt eine Entwicklung, Anpassung und Untersuchung der neuartigen Pinschweißtechnik zur Verbindung thermoplastischer Faserkunststoffverbunde mit metallischen Fügepartnern dar. Die untersuchte Fügetechnik bietet, im Vergleich zu anderen Verfahren, neben einer einseitigen Zugänglichkeit, ein hohes Leichtbaupotenzial. An Multimaterial-Einzelpinverbindungen wurden die CMT-Pinschweißbarkeit charakterisiert und unterschiedliche Fügestrategien erprobt und ausgewertet. Als Bewertungskriterien wurden das Schweißgut sowie der Faser- und Matrixerhalt in Abhängigkeit von den Schweißparametern untersucht. Die mechanische Beanspruchbarkeit der mit dem entwickelten Verfahren erstellten Verbindungen wurde in Scherzugversuchen ermittelt. An Mehrpinverbindungen wurde anschließend der Einfluss der Pinanordnung untersucht und die Auslegung der Fügezone analysiert. Der Fügeprozess wurde an Funktionsmustern und diese wiederum in 3-Punkt-Biegeversuchen validiert sowie mit dem Kleben verglichen.
Modern material-compatible joining methods for fiber-reinforced plastics require the heating of the materials. In order to predict the respective complex temperature fields and curves, the Fraunhofer IAP and the BTU
Cottbus-Senftenberg have developed numerical methods, which are able to simulate different radiation sources and process sequences as well.