The recovery of surfactants from organic mediums is of great economic and environmental interests in the field of petrochemicals sector. The aim of this study was to recover poly-dispersed nonionic surfactant (TX-100) from organic medium by the use of dehydrated and rehydrated kaolin. It was found that the presence of water after kaolin rehydration decreases considerably the amount of TX-100 adsorption from 28.7 μmol.g−1 onto dehydrated kaolin to 23.4 μmol.g−1 onto rehydrated kaolin. The estimation of the number of statistical layers of water deposited on kaolin was observed to be about 7 to 9. The effect of type of solvents (heptane, cyclohexane and benzene) on the adsorption onto rehydrated kaolin revealed a reduction in the adsorbed quantity; the adsorbed amounts were found to be 28.7 μmol.g−1, 26.7 μmol.g−1 and 24.2 μmol.g−1 in heptane, cycloheptane and benzene phases, respectively. On the other hand, it was observed that a temperature increased from 20 °C to 35 °C and 45 °C negatively affects the adsorption of TX-100 onto dehydrated and/or hydrated kaolin in heptane medium.
The biotribocorrosion behavior of newly developed nanocristalline near β-types Ti-15Nb and Ti-15Mo alloys surfaces, sintered by powder metallurgy and sequentially milled, has been investigated in SBF simulated body fluid (PBS solution) at OCP, an applied potential in the passive region and EIS. Reciprocating sliding tests using a ball-on-plate tribometer under differentes applied loads 3, 7 and 10 N load and anodic potentials were applied to evaluate the effect of applied lad and the effect of Nb and Mo elements on tribocorrosion behaviors of samples. Results showed that, Ti-Nb exhibited better anticorrosive properties than Ti-Mo. Under tribological action the nanostructured both of alloys showed similar friction coefficient, while Ti-Nb present lower tendency to corrosion compared to Ti-Mo. Furthermore, Nb diffusion increased the repassivation rate with respect to Ti-Mo surfaces due to its stable passive film. Due to the high chemical reaction rate in β-type Ti-15Mo alloy as compared to Ti-15Nb. The β- Ti-15Nb showed lower volume loss, lower friction coefficient values and exhibited better corrosion resistance during tribocorrosion tests than Ti-15Mo. Prevailing electrochemical conditions between -1 and 2 V influences the wear accelerated corrosion by increasing it with the applied potential and slightly increases the mechanical wear. Also, wear accelerated corrosion can be predicted by existing models as a function of electrochemical and mechanical parameters of the titanium alloys. However, considering biomedical applications, the β- Ti15 Mo and Ti15Nb alloys may be good candidates with low elastic modulus and without toxic alloying elements.
Aiming to develop alloys with better properties for orthopedic applications, the focus of the present research was to evaluate the effect of Mo at.% content on structural, mechanical, and tribological properties of hot isostatically pressed Ti-xMo (x = 4, 8, 12, 15, and 20 at.%) alloys. The structural evolution, mechanical properties, and tribological behavior of the nanostructured Ti-xMo alloys were evaluated using x-ray diffraction, scanning electron microscope, and ball-on-disk tribometer. Wear tests were conducted under different applied loads of 2, 8, and 16 N. Experimental results indicated that the structural evolution and morphological changes of the milled alloys were sensitive to their molybdenum (Mo) content. The morphological characterization showed that the crystallite size and the particle size decreased with increasing Mo content (at.%) reaching the lowest values of 27 and 26 nm in the case of Ti-15Mo and Ti-20Mo, respectively. On the other hand, the coefficient of friction and wear rates were found to be decreasing with increasing Mo content.
The hydrophilic-hydrophobic surface area of alumina powder (Al₂O₃) oxidized at different temperatures was determined on the base of adsorption of water and butane vapor at 25°C. In the order to study the influence of thermal oxidation upon hydrophilic/hydrophobic character of the surface, samples of Al₂O₃ were characterized using granulometry, SEM and BET surface area measurement. SEM results showed that the thermal treatment does not affect the morphology of the Alunima. However, the increase of treatment temperature from 250 to 900°C results in changing of the hydrophilic-hydrophobic balance of Al₂O₃ surface.
The bio-tribocorrosion behavior of newly developed near β-types Ti-15Nb and Ti-15Mo alloys was investigated in Phosphate-Buffered Saline (PBS) under different loads. Open-Circuit Potential (OCP), friction coefficient, wear volume and wear rate were evaluated. The results revealed that Ti-15Nb alloy exhibited lower wear rate, lower friction coefficient and better corrosion resistance during tribocorrosion than the Ti-15Mo alloy. This can be attributed to the diffusion of Nb which increases the repassivation rate (formation of a protective layer) in the Ti-15Nb alloy. In contrast Ti-15Mo shows a significantly higher rate of chemical reaction.
Low modulus β-type Ti-15Nb alloys were prepared by subjecting them to different sintering temperatures (800, 900, 1000 and 1100 °C) and their morphological and structural properties were evaluated. X-ray diffraction analysis was used for the morphological characterization which indicated that the mean pore and crystallite size continuously decreased with increasing sintering temperature to reach the lowest values of 41 nm and 27.5 nm at 1100 °C, respectively. Moreover, the higher sintering temperature resulted in higher relative density, greater hardness and young’s modulus of the Ti-15Nb alloys. Wear tests were conducted using a ball-on-plate type Oscillating tribometer, under different applied loads (2, 8 and 16 N) to evaluate their tribological characterization. The wear rate and friction coefficient were lower at higher sintering temperature. This enhancement in tribological properties was attributed to a grain refinement. The Ti-15Nb alloys sintered at 1100 °C showed the best tribological performance.
Ti–Ni powder compacts were prepared by mechanical alloying (MA), followed by hot isostatic pressing (HIP). Afterwards, the samples were sintered at different temperatures (950, 1050, 1150 and 1250 °C). Microhardness, density, crystallite size as well as microstrain of the sintered samples were measured and analyzed. Wear characteristics in phosphate-buffered saline (PBS) solution was tested under different applied loads of 2 N, 10 N, and 20 N, respectively. The results indicated that the crystallite size continuously decreases with increasing sintering temperature and reaches the lowest value of 31.3 nm at 1250 °C. The relative density of the sample sintered at 1250 °C is 98.0%. Moreover, the higher sintering temperatures lead to the higher relative density and the increase in hardness and young’s modulus of the sample. At the same time the friction coefficient and wear rate were lower for the samples sintered at 1250 °C. This improvement in friction and wear resistance is attributed to the grain size refinement. Ti–Ni sintered at 1250 °C showed good tribological performance under all test conditions.
Surfactants are widely used in many chemical industries and as primary components of cleaning detergents due to their specific characteristics, which in turn results in high pollution of domestic and industrial wastewaters by such substances. In this study, the mechanistic pathways of the adsorption of cationic benzyl-dimethyl-dodecyl ammonium bromide (BDDAB) and anionic sodium dodecyl sulfate (SDS) surfactants on kaolinite clay in water were investigated. The results showed that the adsorption of anionic surfactant (SDS) on kaolinite is better compared with cationic surfactant (BDDAB), wherein the ♦maximum adsorption capacity was found 161.4 μmol g−1 and 234 μmol g−1 for BDDAB and SDS, respectively. Adsorption kinetics were the best suited to pseudo-second-order model for both BDDAB and SDS with an adsorption rate constant of 0.028 g μmol−1 min−1 and 0.023 g μmol−1 min−1, respectively. Meanwhile, the adsorption of BDDAB by kaolinite showed that the isotherm adsorption tended to follow the Langmuir-Freundlich and Freundlich isotherm models. However, the SDS adsorption isotherm obeyed only the Langmuir-Freundlich model.
The effect of milling time on the microstructure and mechanical properties of Ti-6Al-4Fe alloys
(2021)
Replacement of toxic and expensive vanadium (V) in medical grade titanium alloys with cheaper and non-toxic elements such as iron (Fe) or niobium (Nb), is an important step forward in developing safer and less expensive biomaterials. Evaluating the effect of different process parameters such as the milling time on the properties of these newly developed alloys helps in understanding and controlling their behavior. Hence, in this study, the influence of ball-milling duration (2, 6, 8, 12 and 18 h) on crystalline structure, phase evolution, densification, and mechanical characteristics of biomedical nanocrystalline Ti-6Al-4Fe (wt. %) alloys is investigated. X-ray diffraction (XRD) confirmed that after 6 h of milling, aluminum (Al) and Fe completely dissolved into Ti matrix to form a solid solution of Ti (Al, Fe). XRD further revealed that the crystallite size decreased from 56 to 30 nm and the micro-strain increased with an increase in milling time. A decrease in porosity along with an increase in density is also observed for the alloys with increasing milling time. Moreover, the values of porosity obtained for the developed Ti-6Al-4Fe alloys ranged from 1 to 12 %, which is comparable to the porosity of one of the cortical bones making it a potential candidate for bone replacements. Microhardness measurements showed that the hardness of the Ti-6Al-4Fe alloys was greater than the hardness of the conventional Ti-6Al-4V alloys. It was observed that the Ti-6Al-4Fe alloy fabricated with the powders milled for 2 h showed the lowest value of Young’s Modulus. Milling time also had a significant effect on the surface roughness of the alloy samples, which showed a decreasing trend with increasing milling times.
Structural, and tribological properties of nanostructured α + β type titanium alloys for total hip
(2022)
Titanium alloys are in demand for various biomedical applications and the most popular among them being, Ti–6Al–4V. Hence, in this study, Ti–6Al–7Nb are fabricated through the route of mechanical milling using different sintering temperatures. X-ray diffraction and hardness tests were conducted to characterize the developed sams to evaluate the effect of sintering temperatures on the structural and mechanical properties. It is observed that the sams sintered at a temperature of 1250 °C had the smallest crystallite and pore size, with enhanced relative density and mechanical properties. Tribological tests were conducted at varying normal loads to characterize the wear and frictional behaviour and showed that the sams sintered at 1250 °C presented the lowest friction coefficient and wear rate.