For the reliability of many welded structures like pipelines or offshore wind parks, it is necessary to ensure high mechanical properties such as strength and toughness of the entire material. In order to improve quality of weld joints, flux cored rods and wires containing different nanoparticles (ZrO2, LaB6 and Al2O3) were manufactured and welded with the TIG and MAG welding processes. Influence of these nanoparticles on the microstructure and mechanical properties of the weld joints were investigated. The acicular ferrite and improved strength of the weld metals were observed by the addition of 0.2 wt.% of iron powder with ZrO2 nanoparticles to the filling of flux cored wires.
Welded joints of aluminum alloy 6082-T6 formed by the method of pulse friction stir welding are studied. The effect of the power and frequency of the pulses on the microstructure and mechanical properties of the welded joints is determined. Application of an additional pulse during the welding affects the surface quality and the shape of the weld, the distribution of the oxide layer and of particles of the hardening phase, and the grain size in the zone of dynamic recrystallization.
Welded joints of aluminum alloy 6082-T6 formed by the method of impulse friction stir welding are studied. The effect of the power and frequency of the pulses on the microstructure and mechanical properties of the welded joints is determined. Application of an additional pulse during the welding affects the surface quality and the shape of the weld, the distribution of the oxide layer and of particles of the hardening phase, and the grain size in the zone of dynamic recrystallization.
Impulse Friction Stir Welding (IFSW) was utilized to join 6082–T6 alloy plates at various impulse frequencies. A distinctive feature of IFSW is the generation of mechanical impulses that enhances the forging action of the tool, and thereby, alters the weld microstructure. The microstructural evolution in the Stir Zone (SZ) with special focus on the strengthening precipitation behavior, and overall mechanical properties of the IFSW joints have been investigated. It was demonstrated that the strengthening β″ precipitates reprecipitated in the SZ of the IFSW joints during natural aging. In contrast, no precipitates were found in the SZ of the Friction Stir Welding (FSW) weld. Partial reversion of β″ after IFSW is supposed to occur due to more developed subgrain network and higher dislocation density introduced by impulses that accelerated precipitation kinetics. Dynamic recrystallisation was facilitated by impulses resulting in a fine, homogeneous structure. There was no significant difference between the microhardness in the SZ, tensile and yield strength of the FSW and IFSW joints. However, the application of impulses demonstrated the smoothing of the hardness reduction in the transition region at the advancing side. The shift of the fracture location from the Heat-Affected Zone (HAZ) by FSW to the SZ as well as higher elongation of the joints by IFSW of lower frequencies could be related to the grain refinement and the change of the grain orientation.
The effect of heat treatment at various temperatures (650, 850, 1050, and 1100°C) and dwell times (10 min and 1 h) on the metallurgical and microstructural evolution as well as on the related tensile properties of stainless steel 316L processed by selective laser melting (SLM) has been systematically evaluated. The metallurgical and microstructural features such as defects, stability of the columnar–cellular structure and substructure, second phase particles, and phase transformation imparted by SLM and heat treatment have been discussed. It has been shown that the processing conditions specific to SLM significantly alter the kinetics of phase evolution compared to standard welding techniques which affects the accuracy of the prediction. The influence of these characteristics on tensile properties and hardness was elucidated. It was disclosed that with increasing heat treatment temperature there was a gradual increase in elongation but a decrease in strength related to the dislocation density and the development of the microstructure.
Microhardness variations across the friction stir welded (FSW) and impulse friction stir welded (IFSW) AA2024–T351 joints have been elucidated by the transformations of the S–Al2CuMg phase with a special focus on a distinguished hardness peak within the heat-affected zone (HAZ) of the impulse welds. The increase in hardness within the stir zone (SZ) originated from the partial re-precipitation of the initial Guinier-Preston-Bagaryatsky zones (GPB) and metastable S needles, previously dissolved.) Formation and growth of stable S precipitates via coalescence accounted for the softening through the thermo-mechanically affected zone (TMAZ). The peak strengthening within the HAZ of the IFSW joints was mainly caused by the dense needle-shaped S particles, which can be explained by a mutual influence of the process specific temperature and strain cycles. Dislocations and subgrain boundaries introduced to the material due to plastic deformation facilitated the nucleation of strengthening S precipitates in the HAZ. It demonstrates that the impact of deformation should be considered by the characterization of the precipitation development in the HAZ.
Prediction of mechanical properties of welded steel X70 pipeline using neural network modelling
(2020)
An artificial neural network (ANN) model was developed to predict tensile and impact properties of a submerged arc helical welded (SAHW) pipeline steel API X70 based upon its chemical composition. Weight percent of the elements was considered as the input, while the tensile and Charpy impact properties were considered as the outputs. Scatter diagrams and two statistical parameters (absolute fraction of variance and relative error) were used to evaluate the prediction performance of the developed artificial neural network model. The predicted values were found to be in excellent agreement with the experimental data and the current model has a good learning precision and generalization (for training, validation and testing data sets). The results revealed that the developed model is very accurate and has a strong potential for capturing the interaction between the mechanical properties and chemical composition of welded high strength low alloy (HSLA) steels.
The objective of this study was to investigate the effect of the high welding speed on the mechanical properties and their relations to microstructural characteristics of butt friction stir welded joints with the use of 6082-T6 aluminum alloy. The aluminum sheets of 2.0 mm thick were friction stir welded at low (conventional FSW) and high welding speeds (HSFSW) of 200 and 2500 mm/min, respectively. The grain size in the nugget zone (NZ) was decreased; the width of the softened region was narrowed down as well as the lowest microhardness value located in the heat-affected zone (HAZ) was enhanced by HSFSW. The increasing welding speed resulted in the higher ultimate tensile strength and lower elongation, but it had a slight influence on the yield strength. The differences in mechanical properties were explained by analysis of microstructural changes and tensile fracture surfaces of the welded joints, supported by the results of the numerical simulation of the temperature distribution and material flow. The fracture of the conventional FSW joint occurred in the HAZ, the weakest weld region, while all HSFSW joints raptured in the NZ. This demonstrated that both structural characteristics and microhardness distribution influenced the actual fracture locations.
The temperature influence on the microstructure evolution and microhardness of the agehardenable aluminium alloy 6082 T6 during friction stir welding was defined. In order to achieve this aim, the thermocycles calculated using the developed 3D Finite Element Model were physically simulated on the Gleeble-3800 in the points which located in the different zones of the weld. The microstructure in the chosen points after Gleeble testing was investigated as well as the microhardness was measured. The results were consequently compared with the relevant results obtained after friction stir welding. It was shown that the microstructure and microhardness profile are influenced not only by temperature but by deformation. The increase in hardness in different zones after FSW compared to Gleeble testing can be explained by the grain refinement in the nugget zone as well as the hardening precipitate distribution along the weld which can occur more rapidly due to the deformation influence.
Amethod for assessing the effect of the temperature of friction stir welding on the microstructure and mechanical properties of welded joints of aluminum alloy D16AT is suggested. The temperature cycles in different zones of a welded joint are determined by mathematical simulation. The computed temperature cycles are implemented in a Gleeble-3800 system. It is shown that the welding temperature affects little the evolution of the microstructure in different zones of the welded joints of alloy D16AT.