In the cast condition g titanium aluminide alloys that solidify completely through the b phase are
characterized by fine and homogeneous microstructures, weak textures and low segregation. For these reasons such alloys have a relatively good workability and can be closed-die forged without preceding ingot breakdown even if the alloys contain no large fractions of the b phase at the working temperature. The present work was devoted to a combined study of the constitution and microstructural morphologies that develop in various two-step heat treatments of a single-step forged b solidifying alloy. The
study included high-energy X-ray diffraction for in situ investigations of the constitution at the heat treatment temperature. It was observed that the phase ransformations are quite sluggish in the material which results in fine microstructures and some conditions that significantly deviate from thermodynamic equilibrium. Further, tensile and creep testing was carried out on the different material conditions in order to identify the range in which the properties can be varied. It is found that this easily forgeable material exhibits comparable strength, ductility and creep strength as more conventional peritectically solidifying alloys.
Recent research on Co-based and CoNi-based alloys revealed that the Co–Al–W-system provides interesting properties, however, the high content of W addition triggers high mass density of alloys which limits its industrial application. Therefore, new high temperature superalloys based on the Co–Ni–Al–Ti-system with high content Cr and strengthened by γ′-(Ni,Co)3(Cr,Al,Ti) precipitates, have been developed, and the effect of different refractory element additions was investigated. STEM-EDS and HEXRD were employed to determine the elemental partitioning behavior and the lattice misfit between the γ and γ′ phases. Ta and Nb strongly concentrate within the γ′ phase, whereas Mo weakly partitions to the γ phase. W distributes equally between the γ and γ′ phases. These new superalloys have an unexpectedly high positive misfit compared with some conventional Ni-based superalloys and Co-based superalloys. Nb and Ta additions increase the lattice misfit further, while Mo and W decrease the lattice misfit. The effect of refractory elements alloying on the yield stress at room temperature was evaluated by analyzing the contributions of different strengthening mechanisms. Alloying with Nb or Ta significantly improves precipitation strengthening by increasing the antiphase boundary energy. Mo has the highest solid solution strengthening effect in the γ phase, followed by W. Compared with some conventional Ni-based superalloys, the investigated new CoNi-based superalloys exhibited better mechanical properties at high temperature, which indicates that these compositionally complex alloys are possible candidates for high temperature applications.
Microstructure development and hardness of a powder metallurgical multi phase gamma-TiAl based alloy
(2012)
Influence of alloy composition and thermal history on carbide precipitation in γ-based TiAl alloys
(2017)
Influence of Quenching Rates on the Transformation of Ternary Phases in Nb-rich γ-TiAl Alloys
(2011)
Ti-Al3Ti metal-intermetallic laminate (MIL) composites are known as promising structural materials due to the unique combination of their specific properties. However, their application is still limited due to the extremely high brittleness of the Al3Ti phase. In this study, we attempt to address this issue by changing the D022 crystal structure of Al3Ti to the more ductile L12 structure by alloying it with silver. To select the best fabrication regimes of Ti-Ti(Al1−xAgx)3 composites, in situ synchrotron X-ray diffraction analysis was performed to reveal the chemical reactions occurring upon heating the Ti-Al-Ag sample. The analysis showed that the highest amount of Ti(Al1−xAgx)3 phase with the L12 structure appears at 930 °C. This temperature was chosen for subsequent spark plasma sintering experiments. Scanning electron microscopy, energy dispersive X-ray analysis, and X-ray diffraction analysis revealed that the sintered sample consisted mainly of Ti, Ti(Al1−xAgx)3, and a minor fraction of the Ag-Al compound distributed in the central parts of the intermetallic layers and at the grain boundaries. Modification of the titanium trialuminide crystal structure positively affected the properties of the composite, providing a 60% increase in fracture toughness. The Ag-Al phase also contributed to toughening, causing an additional crack deflection effect.
In-situ synchrotron-based high energy X-ray diffraction (HEXRD) and ex-situ Gleeble tests were conducted to investigate the deformation behavior of the βo(ωo) phase in a Ti4Al3Nb alloy. In samples compressed at 600 and 800 °C, the brittle ωo phase deforms mostly elastically, resulting in the failure of the Ti4Al3Nb alloy by premature fracture. In a sample deformed at 900 °C, the ωo phase mostly transforms into the βo phase under uniaxial loading. Moreover, the ductility of a Ti4Al3Nb alloy is largely enhanced at this temperature. In a sample deformed at 1000 °C, dynamic recrystallization (DRX) of the βo phase extensively takes place. Direction 1 (D1) and Direction 2 (D2) deviating from the loading direction with an angle of 65° ± 5° and 15° ± 5° are selected to analyze the lattice strain evolution of (110)βo lattice planes. At the late stage of macro strain hardening, deformed[removed]βo//D1 oriented grains bear a higher load due to the occurrence of DRX in[removed]βo//D2 oriented grains. Subsequently, DRX continues in[removed]βo//D1 oriented βo grains. The coordinated deformation of βo grains ensures the good deformability of a Ti4Al3Nb alloy at 1000 °C.
In modern β-solidified TiAl alloys, the decomposition of α2 phase is frequently observed during heat treatment or high-temperature deformation of the alloys. In this study, high-temperature deformation and decomposition mechanisms of α2 phase in a Ti-45Al-8.5Nb-0.2B-0.2W-0.02Y alloy are investigated. In a sample deformed at 800 °C, the precipitation of βo(ωo) phase is observed within the equiaxed α2 phase. The nucleation of ωo particles within the βo matrix indicates the α2→βo→ωo transformation. In addition, numerous γ phase precipitates form within the βo(ω) areas. The α2 lamellae decompose into ultrafine (α2+γ) lamellae and coarsened γ lamellae via α2→α2+γ and α2→γ transformation, respectively. Moreover, the ωo phase nucleates within the ultrafine lamellae via α2→ωo transformation. However, in a sample deformed at 1000 °C, the nucleation of βo particles is sluggish, which is caused by the efficient release of the internal stress via dynamic recrystallization (DRX). These results indicate that complex phase transformations can be introduced by the decomposition of α2 phase in TiAl alloys with a high amount of β-stabilizing elements.