The biotribocorrosion behavior of newly developed nanocristalline near β-types Ti-15Nb and Ti-15Mo alloys surfaces, sintered by powder metallurgy and sequentially milled, has been investigated in SBF simulated body fluid (PBS solution) at OCP, an applied potential in the passive region and EIS. Reciprocating sliding tests using a ball-on-plate tribometer under differentes applied loads 3, 7 and 10 N load and anodic potentials were applied to evaluate the effect of applied lad and the effect of Nb and Mo elements on tribocorrosion behaviors of samples. Results showed that, Ti-Nb exhibited better anticorrosive properties than Ti-Mo. Under tribological action the nanostructured both of alloys showed similar friction coefficient, while Ti-Nb present lower tendency to corrosion compared to Ti-Mo. Furthermore, Nb diffusion increased the repassivation rate with respect to Ti-Mo surfaces due to its stable passive film. Due to the high chemical reaction rate in β-type Ti-15Mo alloy as compared to Ti-15Nb. The β- Ti-15Nb showed lower volume loss, lower friction coefficient values and exhibited better corrosion resistance during tribocorrosion tests than Ti-15Mo. Prevailing electrochemical conditions between -1 and 2 V influences the wear accelerated corrosion by increasing it with the applied potential and slightly increases the mechanical wear. Also, wear accelerated corrosion can be predicted by existing models as a function of electrochemical and mechanical parameters of the titanium alloys. However, considering biomedical applications, the β- Ti15 Mo and Ti15Nb alloys may be good candidates with low elastic modulus and without toxic alloying elements.
Ti–Ni powder compacts were prepared by mechanical alloying (MA), followed by hot isostatic pressing (HIP). Afterwards, the samples were sintered at different temperatures (950, 1050, 1150 and 1250 °C). Microhardness, density, crystallite size as well as microstrain of the sintered samples were measured and analyzed. Wear characteristics in phosphate-buffered saline (PBS) solution was tested under different applied loads of 2 N, 10 N, and 20 N, respectively. The results indicated that the crystallite size continuously decreases with increasing sintering temperature and reaches the lowest value of 31.3 nm at 1250 °C. The relative density of the sample sintered at 1250 °C is 98.0%. Moreover, the higher sintering temperatures lead to the higher relative density and the increase in hardness and young’s modulus of the sample. At the same time the friction coefficient and wear rate were lower for the samples sintered at 1250 °C. This improvement in friction and wear resistance is attributed to the grain size refinement. Ti–Ni sintered at 1250 °C showed good tribological performance under all test conditions.
Structured materials can be progressive alternatives to commonly used
flat sheets because of their higher bending stiffness and stability compared to flat sheet metals, made of the same alloy. The application of sheet metals requires accurate information regarding their strength and deformation behavior. Such data are not commonly available and have to be measured by specific test setups and implementation
of tests. The aim of this work is to obtain new knowledge about deformation mechanisms of structured sheet metals. Structured sheet metals (SSM) made of conventional deep-drawing steel DC04 were investigated by means of tensile tests. The influence of the structure type arrangement on the deformation behavior was analyzed. The evolution of local strains was analyzed by means of strain gauge
measurements as well as 3D-displacement measurements with an ARAMIS highresolution camera system. Local orientation changes in different structural elements were measured using the electron backscatter diffraction technique.
Hot isostatically forged TiAl turbine blades made of TNM-B1 are commercially used in aircraft engines, as they offer significantly lower weight than the traditional nickel-based blades while exhibiting similar strength. Like other TiAl alloys, TNM-B1 displays high peak stress followed by a strong softening behavior (i.e. stress reduction) during hot deformation. This softening can be used to accelerate the deformation process by reducing the processing time and in turn the costs for TNM-B1 parts. In order to avoid increased damage during the accelerated process, a pre-heat treatment (HT) for the hot isostatically pressed material (HIP) is required. To simulate the accelerated forming process, hot compression tests were performed with a DIL805A/D/T dilatometer from TA Instruments (New Castle, Delaware, USA) with different strain rates (0.0013, 0.005, 0.01 and 0.05) and temperatures (T=1150, 1175 and 1200°C). Deformation of the heat-treated state revealed lower flow stress (in both, peak stresses and steady state stresses) and fewer voids compared to the HIP state (Fig. 1.a). The compression test data were used to develop material and temperature specific strain rate profiles based on a material model. Subsequently, hot compression tests were performed with different strain rate profiles (starting strain rates 0.0013 and 0.0052) for the HIP and the HT state. The results were evaluated with regard to their microstructure, deformation, and damage behavior. A reduction of the processing time for all tested strain rates profiles by factors 2-3 could be achieved compared to constant strain rates. Furthermore, the results indicated that the deformation with strain rate profiles (compared to constant strain rates) did not significantly change the resulting microstructure or damage tolerance of the HT state.
Hexavalent chromium pollution from industrial waste water is a serious problem as it can cause adverse effects on the environment. Several methods are used to reduce the harmful effects of this pollutant, especially physico-chemical methods, such as adsorption technology. The present study aims to remove Cr (VI) from industrial sources in a fixed-bed column of activated carbon. The experiments were carried out at natural pH and temperature with a flow rate (5, 10, and 20 mL/min) and bed height (3.5 cm). Breakthrough curves for feed concentrations (0.01, 0.03, and 0.05 mol/L) were investigated. The results indicated a marked decrease up to 99%. The value of the flow constant for the Thomas model decreased with the increase in the concentration of the incoming substance, but increased with the increase in the flow rate.
Le milieu médical est un perpétuel demandeur de biomatériaux compatibles surtout en orthopédie. Effectivement le nombre important d’arthroplasties effectuées chaque année ne cesse d’augmenter dans le monde, non seulement du fait vieillissement de la population (à partir de 65 ans), mais aussi de demandes de patients plus jeunes entre 45 ans et 55 ans. Actuellement, les composés à base de titane Ti sont largement utilisés comme des biomatériaux pour leur biocompatibilité, leur résistance à la corrosion et leur faible module d’élasticité. Le molybdène et le zirconium sont parmi les meilleurs éléments alliés parce qu’ils sont non toxiques et non allergiques et offrent d’excellentes propriétés. De plus,Le Zr peut augmenter la trempabilité et la résistance à la corrosion de l'alliage . Mo est un élément fort stabilisant pour la phase des alliages de titane et les alliages à base de Ti-Mo présentent des propriétés mécaniques adéquates compatibilité et bonne cyto-compatibilité . Par conséquent, le système Ti-Mo-Zr, qui a montré une bonnes performances et de magnifiques perspectives dans l’application de biomatériaux, a été intensivementétudié [1,2,3]. Cependant, les alliages de Ti largement utilisés, tels que les interstitiels extra-low (ELI) Ti-6Al-4V (wt.% en poids ), Ti- 5Al-2,5 Fe et Ti-6Al-7Nb, ont le risque de libérer de l'aluminium toxique (Al) et les Ions de vanadium (V) in vivo, ce qui peut causer des problèmes de santé, comme la maladie d’Alzheimer et la neuropathie[4].La métallurgie des poudres (MP), y compris la méthode de mixture des composants en poudre, qui consiste à fritter titane en poudre ou ses mélanges avec d’autres composants en poudre, est un procédé économique à moindre cout. La nanotechnologie est intervenue dans la structuration des biomatériaux à l’échelle nanométrique (entre1nmet 100 nm) par soucis d’amélioration des propriétés mécanique surtout le module de Young.
The osteoarthritis and degenerative diseases osteoporosis as well as trauma lead to the bone mechanical properties degradation due to absence of normal biological self healing processes or excessive loading [1–5]. These problems solution are artificial biomaterials, as surgical implantation of appropriate shapes helps restore function for the otherwise functionally compromised structures [1–5]. Biocompatibility is considered to be optimal once tissue neoformation and later function occurs around implantable devices [6]. The efficacy of biomaterials implants is determined mostly by their surface characteristics such as microstructure, surface morphology, composition and biological properties [2]. Aiming to develop alloys with better properties for orthopedic applications, the focus of the present research was to evaluate the effect of Zr at. % content on structural, mechanical and tribological properties of hot isostatically pressed Ti-25Nb-xZr (x = 5, 10, 15, 20 and 25 at. %) alloys. The structural evolution, and mechanical properties of the nanostructured Ti-Nb-xZr alloys were evaluated using X-Ray diffraction, scanning electron microscope. The mechanical properties were performed using Vickers hardness and berkovich nanoindentation. Experimental results indicated that the structural evolution and morphological changes of the milled alloys were sensitive to their Zirconium (at. %) content. The morphological characterization showed that the crystallite size and the particle size decreased with increasing Zr content (at. %). As well, as the Zr was added to the Ti-25NbXZr system, there was a clear decrease in the Vickers hardness and young’s modulus. On the other hand, the coefficient of friction and wear rates were found to be decreasing with increasing Zr content.
Study of the photocatalytic degradation of Orange methyl dye in the presence of titanium dioxide
(2019)
The use of photocatalytic techniques for water purification and
wastewater treatment is very widespread, in our work we used
TiO2 to photocatalyrate orange methyl (MO). In addition, the
effects of some parameters on photodegradation of MO have
been studied, such as the presence and / or absence of light
(UV). The use of TiO2 showed a high MO degradation
efficiency of up to 98%. The presence of H2O2 in the
photocatalytic reaction may favor the photocatalytic
degradation efficiencies. In addition, the experimental results
have demonstrated an excellent rate of the order of 99%.