Ti–Ni powder compacts were prepared by mechanical alloying (MA), followed by hot isostatic pressing (HIP). Afterwards, the samples were sintered at different temperatures (950, 1050, 1150 and 1250 °C). Microhardness, density, crystallite size as well as microstrain of the sintered samples were measured and analyzed. Wear characteristics in phosphate-buffered saline (PBS) solution was tested under different applied loads of 2 N, 10 N, and 20 N, respectively. The results indicated that the crystallite size continuously decreases with increasing sintering temperature and reaches the lowest value of 31.3 nm at 1250 °C. The relative density of the sample sintered at 1250 °C is 98.0%. Moreover, the higher sintering temperatures lead to the higher relative density and the increase in hardness and young’s modulus of the sample. At the same time the friction coefficient and wear rate were lower for the samples sintered at 1250 °C. This improvement in friction and wear resistance is attributed to the grain size refinement. Ti–Ni sintered at 1250 °C showed good tribological performance under all test conditions.
Hot isostatically forged TiAl turbine blades made of TNM-B1 are commercially used in aircraft engines, as they offer significantly lower weight than the traditional nickel-based blades while exhibiting similar strength. Like other TiAl alloys, TNM-B1 displays high peak stress followed by a strong softening behavior (i.e. stress reduction) during hot deformation. This softening can be used to accelerate the deformation process by reducing the processing time and in turn the costs for TNM-B1 parts. In order to avoid increased damage during the accelerated process, a pre-heat treatment (HT) for the hot isostatically pressed material (HIP) is required. To simulate the accelerated forming process, hot compression tests were performed with a DIL805A/D/T dilatometer from TA Instruments (New Castle, Delaware, USA) with different strain rates (0.0013, 0.005, 0.01 and 0.05) and temperatures (T=1150, 1175 and 1200°C). Deformation of the heat-treated state revealed lower flow stress (in both, peak stresses and steady state stresses) and fewer voids compared to the HIP state (Fig. 1.a). The compression test data were used to develop material and temperature specific strain rate profiles based on a material model. Subsequently, hot compression tests were performed with different strain rate profiles (starting strain rates 0.0013 and 0.0052) for the HIP and the HT state. The results were evaluated with regard to their microstructure, deformation, and damage behavior. A reduction of the processing time for all tested strain rates profiles by factors 2-3 could be achieved compared to constant strain rates. Furthermore, the results indicated that the deformation with strain rate profiles (compared to constant strain rates) did not significantly change the resulting microstructure or damage tolerance of the HT state.
Hexavalent chromium pollution from industrial waste water is a serious problem as it can cause adverse effects on the environment. Several methods are used to reduce the harmful effects of this pollutant, especially physico-chemical methods, such as adsorption technology. The present study aims to remove Cr (VI) from industrial sources in a fixed-bed column of activated carbon. The experiments were carried out at natural pH and temperature with a flow rate (5, 10, and 20 mL/min) and bed height (3.5 cm). Breakthrough curves for feed concentrations (0.01, 0.03, and 0.05 mol/L) were investigated. The results indicated a marked decrease up to 99%. The value of the flow constant for the Thomas model decreased with the increase in the concentration of the incoming substance, but increased with the increase in the flow rate.