The osteoarthritis and degenerative diseases osteoporosis as well as trauma lead to the bone mechanical properties degradation due to absence of normal biological self healing processes or excessive loading [1–5]. These problems solution are artificial biomaterials, as surgical implantation of appropriate shapes helps restore function for the otherwise functionally compromised structures [1–5]. Biocompatibility is considered to be optimal once tissue neoformation and later function occurs around implantable devices [6]. The efficacy of biomaterials implants is determined mostly by their surface characteristics such as microstructure, surface morphology, composition and biological properties [2]. Aiming to develop alloys with better properties for orthopedic applications, the focus of the present research was to evaluate the effect of Zr at. % content on structural, mechanical and tribological properties of hot isostatically pressed Ti-25Nb-xZr (x = 5, 10, 15, 20 and 25 at. %) alloys. The structural evolution, and mechanical properties of the nanostructured Ti-Nb-xZr alloys were evaluated using X-Ray diffraction, scanning electron microscope. The mechanical properties were performed using Vickers hardness and berkovich nanoindentation. Experimental results indicated that the structural evolution and morphological changes of the milled alloys were sensitive to their Zirconium (at. %) content. The morphological characterization showed that the crystallite size and the particle size decreased with increasing Zr content (at. %). As well, as the Zr was added to the Ti-25NbXZr system, there was a clear decrease in the Vickers hardness and young’s modulus. On the other hand, the coefficient of friction and wear rates were found to be decreasing with increasing Zr content.
Ti–Ni powder compacts were prepared by mechanical alloying (MA), followed by hot isostatic pressing (HIP). Afterwards, the samples were sintered at different temperatures (950, 1050, 1150 and 1250 °C). Microhardness, density, crystallite size as well as microstrain of the sintered samples were measured and analyzed. Wear characteristics in phosphate-buffered saline (PBS) solution was tested under different applied loads of 2 N, 10 N, and 20 N, respectively. The results indicated that the crystallite size continuously decreases with increasing sintering temperature and reaches the lowest value of 31.3 nm at 1250 °C. The relative density of the sample sintered at 1250 °C is 98.0%. Moreover, the higher sintering temperatures lead to the higher relative density and the increase in hardness and young’s modulus of the sample. At the same time the friction coefficient and wear rate were lower for the samples sintered at 1250 °C. This improvement in friction and wear resistance is attributed to the grain size refinement. Ti–Ni sintered at 1250 °C showed good tribological performance under all test conditions.