The effect of milling time on the microstructure and mechanical properties of Ti-6Al-4Fe alloys
(2021)
Replacement of toxic and expensive vanadium (V) in medical grade titanium alloys with cheaper and non-toxic elements such as iron (Fe) or niobium (Nb), is an important step forward in developing safer and less expensive biomaterials. Evaluating the effect of different process parameters such as the milling time on the properties of these newly developed alloys helps in understanding and controlling their behavior. Hence, in this study, the influence of ball-milling duration (2, 6, 8, 12 and 18 h) on crystalline structure, phase evolution, densification, and mechanical characteristics of biomedical nanocrystalline Ti-6Al-4Fe (wt. %) alloys is investigated. X-ray diffraction (XRD) confirmed that after 6 h of milling, aluminum (Al) and Fe completely dissolved into Ti matrix to form a solid solution of Ti (Al, Fe). XRD further revealed that the crystallite size decreased from 56 to 30 nm and the micro-strain increased with an increase in milling time. A decrease in porosity along with an increase in density is also observed for the alloys with increasing milling time. Moreover, the values of porosity obtained for the developed Ti-6Al-4Fe alloys ranged from 1 to 12 %, which is comparable to the porosity of one of the cortical bones making it a potential candidate for bone replacements. Microhardness measurements showed that the hardness of the Ti-6Al-4Fe alloys was greater than the hardness of the conventional Ti-6Al-4V alloys. It was observed that the Ti-6Al-4Fe alloy fabricated with the powders milled for 2 h showed the lowest value of Young’s Modulus. Milling time also had a significant effect on the surface roughness of the alloy samples, which showed a decreasing trend with increasing milling times.
The effect of low energy plasma immersion ion implantation and deposition of titanium on microstructure, defect structure and hydrogen trapping in zirconium alloy Zr-1Nb was studied. Defect structure and distribution were analyzed by Doppler broadening using slow positron beam. The surface microstructure after modification is represented by nanostructured Ti grains with random orientation. The gradient distribution of titanium as well as vacancy type defects were analyzed. The concentration of vacancy type defects is rising with increasing bias voltage. Gas-phase hydrogenation of the Ti-modified Zr-1Nb alloy was performed at 400 °C for 60 min. The strong interaction of hydrogen with vacancy type defects was demonstrated. Two different changes in the defect structure after hydrogenation were observed: when a titanium film is formed on the surface (after deposition at 500 V) hydrogen trapping occurs with the formation of titanium hydride phases, while in the implanted layer (deposition at 1000 and 1500 V) hydrogen is trapped due to interaction with vacancy type defects. The physical basis of Ti diffusion and its influence on the evolution of defect structure after surface modification and hydrogenation were discussed.