β-type Ti–20Nb–13Zr alloys with low Young’s modulus were prepared at different sintering temperatures (950, 1050, 1150, and 1250 °C). The morphological and structural characteristics of as-prepared samples were investigated by several methods. Wear tests were conducted using a ball-on-plate type oscillating tribometer under different applied loads (2, 10, and 20 N). The morphological characterization indicated that the mean pore and crystallite size continuously decreased with increasing sintering temperature to reach lowest values of 40 nm and 38 nm at 1250 °C, respectively. The relative density of the 1250 °C sintered sample was as high as 98.7%. Moreover, the higher sintering temperature resulted in higher relative density and closed porosity of the sample. Both the friction coefficient and wear rate were lower in the sample sintered at 1250 °C as compared to other samples. This enhancement in tribological properties was attributed to a closed porosity.
This paper serves as an overview of the ongoing research in the field of multiscale and multidisciplinary analysis of deformation and damage in the case of oligocrystalline structures. The research focuses on experimental measurement and numerical calculation of ductile failure in the X2CrNiMo18-15-3 (AISI 316L) stainless steel. An embedding numerical technique is employed where crystal plasticity theory is used to represent plastic deformation in the material and element removal technique based on Rice&Tracey damage model for ductile void growth to simulate damage initiation inside the material, which is observed in the experiments. Additionally, the crystal plasticity model is supported by a hierarchical multiscale approach connecting nano-, micro- and meso-scales.