Lattice strain controls the etching of solar wafer surfaces

  • Multi-wire sawing using an abrasive SiC slurry or diamond wires constitutes the main slicing techniques for multi- and monocrystalline silicon crystals in photovoltaics. The massive mechanical load during the sawing process creates a wafer surface layer characterized by lattice defects, pits, fractures, rifts, cracks, amorphous Si and even some high-pressure Si modifications, otherwise known as saw damage.[1] This highly defect-rich surface causes the rapid recombination of electron-hole pairs, requiring that it be removed by etching in order to manufacture solar cells and to generate a surface morphology having a low reflectivity which directly affects the solar cell’s efficiency. However, etching of the saw damage features of a heterogeneous and laterally unevenly distributed etch attack and a significantly higher etch rate compared to the underlying bulk silicon.[2,3] The present study is focused on the question of how mechanically introduced lattice strain in single-crystalline silicon alters the chemical reactivity of theMulti-wire sawing using an abrasive SiC slurry or diamond wires constitutes the main slicing techniques for multi- and monocrystalline silicon crystals in photovoltaics. The massive mechanical load during the sawing process creates a wafer surface layer characterized by lattice defects, pits, fractures, rifts, cracks, amorphous Si and even some high-pressure Si modifications, otherwise known as saw damage.[1] This highly defect-rich surface causes the rapid recombination of electron-hole pairs, requiring that it be removed by etching in order to manufacture solar cells and to generate a surface morphology having a low reflectivity which directly affects the solar cell’s efficiency. However, etching of the saw damage features of a heterogeneous and laterally unevenly distributed etch attack and a significantly higher etch rate compared to the underlying bulk silicon.[2,3] The present study is focused on the question of how mechanically introduced lattice strain in single-crystalline silicon alters the chemical reactivity of the silicon atoms affected by the strain field on a microscopic length scale. The magnitude and local distribution of lattice strain were extracted from confocal Raman microscopy measurements according to Ref. 4. One of the parameters used to describe the reactivity of silicon is the local etch rate, which was derived from the local removal before and after etching by confocal microscopy. Wet-chemical etching was performed with HF-HNO3-H2SiF6 acid mixtures of different concentrations. It was found, that the reactivity of silicon increased linearly with the magnitude of lattice strain. In particular, an increase in tensile strain led to a higher increase in reactivity compared to the increase observed with growing compressive strain. The second decisive parameter is the reactivity of the etch mixture. Diluted acid mixtures with a low reactivity attack only the highest strained Si, whereas more concentrated and therefore more reactive acid mixtures are able to attack even slightly strained Si. Side effects, such as the behavior of amorphous or nanocrystalline Si and the generation of highly reactive intermediary species while etching, are discussed.show moreshow less

Export metadata

Additional Services

Search Google Scholar
Metadaten
Author: Thomas LangnerORCiD, Tim Sieber, Jörg AckerORCiDGND
Title of the source (English):9th European Silicon Days, 9-12 September 2018, Saarbrücken, Germany, Book of abstracts
Publisher:Universität des Saarlandes
Place of publication:Saarbrücken
Editor: David Scheschkewitz, Guido Kickelbick
Document Type:Conference Proceeding
Language:English
Year of publication:2018
Tag:Raman spectroscopy; confocal microscopy; etching; lattice strain; silicon
First Page:S. 201
Faculty/Chair:Fakultät 2 Umwelt und Naturwissenschaften / FG Physikalische Chemie
Einverstanden ✔
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.