Low-temperature atomic layer deposition of indium oxide thin films using trimethylindium and oxygen plasma

  • Indium oxide (InxOy) thin films were deposited by plasma-enhanced atomic layer deposition (PEALD) using trimethylindium and oxygen plasma in a low-temperature range of 80–200 °C. The optical properties, chemical composition, crystallographic structure, and electrical characteristics of these layers were investigated by spectroscopic ellipsometry (SE), x-ray photoelectron spectroscopy (XPS), x-ray diffraction (XRD), as well as current-voltage and capacitance-voltage measurements. The SE results yielded a nearly constant growth rate of 0.56 Å per cycle and a thickness inhomogeneity of ≤1.2% across 4-in. substrates in the temperature range of 100–150 °C. The refractive index (at 632.8 nm) was found to be 2.07 for the films deposited at 150 °C. The PEALD-InxOy layers exhibit a direct (3.3 ± 0.2 eV) and an indirect (2.8 ± 0.1 eV) bandgap with an uptrend for both with increasing substrate temperature. Based on XPS characterization, all InxOy samples are free of carbon impurities and show a temperature-dependent off-stoichiometry indicatingIndium oxide (InxOy) thin films were deposited by plasma-enhanced atomic layer deposition (PEALD) using trimethylindium and oxygen plasma in a low-temperature range of 80–200 °C. The optical properties, chemical composition, crystallographic structure, and electrical characteristics of these layers were investigated by spectroscopic ellipsometry (SE), x-ray photoelectron spectroscopy (XPS), x-ray diffraction (XRD), as well as current-voltage and capacitance-voltage measurements. The SE results yielded a nearly constant growth rate of 0.56 Å per cycle and a thickness inhomogeneity of ≤1.2% across 4-in. substrates in the temperature range of 100–150 °C. The refractive index (at 632.8 nm) was found to be 2.07 for the films deposited at 150 °C. The PEALD-InxOy layers exhibit a direct (3.3 ± 0.2 eV) and an indirect (2.8 ± 0.1 eV) bandgap with an uptrend for both with increasing substrate temperature. Based on XPS characterization, all InxOy samples are free of carbon impurities and show a temperature-dependent off-stoichiometry indicating oxygen vacancies. XRD diffraction patterns demonstrate an onset of crystallization at 150 °C. Consistent with the optical, XPS, and XRD data, the films deposited at ≥150 °C possess higher electrical conductivity. Our findings prove that a low-temperature PEALD process of InxOy is feasible and promising for a high-quality thin-film deposition without chemical impurities on thermally fragile substrates.show moreshow less

Export metadata

Additional Services

Search Google Scholar
Metadaten
Author: Ali MahmoodinezhadORCiD, Carlos MoralesORCiD, Franziska NaumannORCiD, Paul PlateORCiD, Robert MeyerORCiD, Christoph JanowitzORCiD, Karsten HenkelORCiDGND, Małgorzata KotORCiD, Marvin Hartwig ZöllnerORCiD, Christian WengerORCiD, Jan Ingo FlegeORCiD
DOI:https://doi.org/10.1116/6.0001375
ISSN:0734-2101
ISSN:1520-8559
Title of the source (English):Journal of Vacuum Science and Technology A
Document Type:Scientific journal article peer-reviewed
Language:English
Year of publication:2021
Tag:Electrical properties; Ellipsometry; Indium oxide; Plasma-enhanced atomic layer deposition; X-ray diffraction; X-ray photoelectron spectroscopy
Volume/Year:39
Issue number:6
Article number:062406