TY - CHAP A1 - Fellah, Mamoun A1 - Hezil, Naouel A1 - Abderrahim, Karima A1 - Samad, Mohammed Abdul A1 - Montagne, Alex A1 - Mejias, Alberto A1 - Iost, Alain A1 - Kossman, Stephania A1 - Chekalkin, Timofey A1 - Obrosov, Aleksei A1 - Weiß, Sabine T1 - Investigating the Effect of Sintering Temperature on Structural and Tribological Properties of a Nanostructured Ti–20Nb–13Zr Alloy for Biomedical Applications T2 - Characterization of Minerals, Metals, and Materials N2 - β-type Ti–20Nb–13Zr alloys with low Young’s modulus were prepared at different sintering temperatures (950, 1050, 1150, and 1250 °C). The morphological and structural characteristics of as-prepared samples were investigated by several methods. Wear tests were conducted using a ball-on-plate type oscillating tribometer under different applied loads (2, 10, and 20 N). The morphological characterization indicated that the mean pore and crystallite size continuously decreased with increasing sintering temperature to reach lowest values of 40 nm and 38 nm at 1250 °C, respectively. The relative density of the 1250 °C sintered sample was as high as 98.7%. Moreover, the higher sintering temperature resulted in higher relative density and closed porosity of the sample. Both the friction coefficient and wear rate were lower in the sample sintered at 1250 °C as compared to other samples. This enhancement in tribological properties was attributed to a closed porosity. KW - Ti-20Nb-13Zr KW - Nanobiomaterials KW - Tribological behaviour KW - Nanotribology KW - Sintering KW - Biomedical applications Y1 - 2020 SN - 978-3-030-36628-5 SN - 978-3-030-36627-8 U6 - https://doi.org/10.1007/978-3-030-36628-5_61 SN - 2367-1181 SN - 2367-1696 SP - 619 EP - 629 PB - Springer CY - Cham ER - TY - GEN A1 - Fellah, Mamoun A1 - Hezil, Naouel A1 - Touhami, Mohamed Zine A1 - Hussien, Mohammed A. A1 - Montagne, Alex A1 - Mejias, Alberto A1 - Iost, Alain A1 - Kossman, Stephania A1 - Chekalkin, Timofey A1 - Obrosov, Aleksei A1 - Weiß, Sabine T1 - Effect of Sintering Temperature on Mechanical and Tribological Behavior of Ti–Ni Alloy for Biomedical Applications T2 - TMS 2020 149th Annual Meeting & Exhibition Supplemental Proceedings N2 - Ti–Ni powder compacts were prepared by mechanical alloying (MA), followed by hot isostatic pressing (HIP). Afterwards, the samples were sintered at different temperatures (950, 1050, 1150 and 1250 °C). Microhardness, density, crystallite size as well as microstrain of the sintered samples were measured and analyzed. Wear characteristics in phosphate-buffered saline (PBS) solution was tested under different applied loads of 2 N, 10 N, and 20 N, respectively. The results indicated that the crystallite size continuously decreases with increasing sintering temperature and reaches the lowest value of 31.3 nm at 1250 °C. The relative density of the sample sintered at 1250 °C is 98.0%. Moreover, the higher sintering temperatures lead to the higher relative density and the increase in hardness and young’s modulus of the sample. At the same time the friction coefficient and wear rate were lower for the samples sintered at 1250 °C. This improvement in friction and wear resistance is attributed to the grain size refinement. Ti–Ni sintered at 1250 °C showed good tribological performance under all test conditions. KW - Ti–Ni KW - Nanobiomaterials KW - Tribological behaviour KW - Sintering KW - Biomedical applications Y1 - 2020 SN - 978-3-030-36295-9 SN - 978-3-030-36296-6 U6 - https://doi.org/10.1007/978-3-030-36296-6_157 SN - 2367-1181 SN - 2367-1696 SP - 1701 EP - 1710 PB - Springer CY - Cham ER - TY - GEN A1 - Baigonakova, Gulsharat A1 - Marchenko, Ekaterina A1 - Chekalkin, Timofey A1 - Kang, Ji-hoon A1 - Weiß, Sabine A1 - Obrosov, Aleksei T1 - Influence of Silver Addition on Structure, Martensite Transformations and Mechanical Properties of TiNi–Ag Alloy Wires for Biomedical Application T2 - Materials N2 - The microstructural and functional behavior of TiNi-based wires with a silver content of 0–1.5 at.% was evaluated. The concentration range for Ag doping determined for the TiNi wires with potential for the medical industry was 0–0.2 at.%. Microstructure analysis of TiNi wires with different silver contents at room temperature indicated a multiphase structural state. Various internal structures with tangled grain boundaries were formed by intense plastic deformation. The nanocrystalline structure and phase state of wire with the minimum silver content (0.1 at.% Ag) provide full shape recovery, the greatest reversible strain, and optimal strength and ductility. TiNi ingots with a high Ag content (0.5–1.5 at.%) cracked under minimum load due to excess silver that crystallized along the grain boundaries and broke cohesion bonds between the TiNi grains. KW - shape memory alloy KW - silver KW - doping KW - mechanical properties KW - nanostructured material KW - wire Y1 - 2020 UR - https://www.mdpi.com/1996-1944/13/21/4721 U6 - https://doi.org/10.3390/ma13214721 SN - 1996-1944 VL - 13 IS - 21 ER - TY - GEN A1 - Kokorev, Oleg A1 - Chekalkin, Timofey A1 - Marchenko, Ekaterina A1 - Yasenchuk, Yuri A1 - Gunther, Sergey A1 - Serebrov, Vladimir A1 - Chernyshova, Alena A1 - Obrosov, Aleksei A1 - Kang, Ji-hoon T1 - Exploring the role of surface modifications of TiNi-based alloys in evaluating in vitro cytocompatibility: a comparative study T2 - Surface Topography: Metrology and Properties N2 - The aim of this study was the comparative analysis of in vitro bio-testing of solid and porous TiNi samples with modified surfaces (intact, oxidated, and etched). Tests for cytocompatibility, hemolysis, and cytotoxicity (MTT) as well as visualization by confocal and scanning electron microscopy have shown that the chemically modified samples are the most cytocompatible. The intact and etched samples did not induce hemolysis greater than 2%, and thus they comply with the ISO 10993-4:2018 standard for hemolysis by blood-contacting biomaterials. Direct culture of etched samples with MCF-7 cells and human leukocytes showed low cytotoxicity. At the same time, the cytotoxicity of samples oxidated at 500 °C was significantly greater than that of the etched samples. Confocal and electron microscopy also confirmed the abovementioned quantitative data. The cells attached to the etched surface in numbers sufficient for them to be able to grow and proliferate on this substrate in vitro. These findings indicate that solid and porous TiNi alloy with surface modifications achieved by a cost-effective method is biotolerable and promising for clinical use and for tissue engineering. KW - biocompatibility KW - cytocompatibility KW - TiNi alloys KW - tissue engineering KW - surface modification Y1 - 2020 UR - https://iopscience.iop.org/article/10.1088/2051-672X/abc0f9/meta U6 - https://doi.org/10.1088/2051-672X/abc0f9 SN - 2051-672X VL - 8 IS - 4 ER -