TY - GEN A1 - Shezad, Nasir A1 - Safdar, Muddasar A1 - Arellano-Garcia, Harvey A1 - Tai, Cheuk-Wai A1 - Chen, Shaojiang A1 - Seo, Dong-Kyun A1 - You, Shujie A1 - Vomiero, Alberto A1 - Akhtar, Farid T1 - Deciphering the role of APTES in tuning the metal support interaction of NiO nanolayers over hierarchical zeolite 13X for CO2 methanation T2 - Carbon Capture Science & Technology N2 - The development of robust nickel catalysts on porous substrates offers great potential for converting carbon dioxide (CO2) into methane, thereby helping to address the global warming and sustainability challenges. This study investigates the dispersion and stability of Ni nanolayers by grafting bifunctional groups over the hierarchical zeolite 13X (h13X) support using (3-aminopropyl)triethoxysilane (APTES). The Ni nanolayers, with a thickness of 1.5-7 nm, were deposited around the edges of h13X and analyzed using STEM imaging. A clear shift in the binding energies was observed by XPS analysis, substantiating the enhanced metalsupport interaction (MSI) between NiO and h13X. The influence of reaction temperature on APTES incorporation into h13X was revealed by H2-TPR and CO2-TPD, with notable variations in the reducibility and surface basicity profiles of the catalysts. The optimized catalyst exhibited CO2 conversion of 61% with CH4 selectivity of 97% under GHSV of 60,000 mlgCat-1h-1 at 400 oC and 1 bar and demonstrated robust stability over a period of 150 h without discernible degradation. The enhanced performance could be attributed to the strengthened MSI and reduced size of Ni nanolayers over h13X. These findings highlight the development of robust heterogeneous catalysts by changing the surface chemistry of support material for various catalytic applications. KW - CO2 methanation KW - Catalyst stability KW - Metal-support interaction KW - APTES functionalization KW - Nickel nanolayers KW - Hierarchical zeolite Y1 - 2025 UR - https://www.sciencedirect.com/science/article/pii/S2772656825000636 U6 - https://doi.org/10.1016/j.ccst.2025.100424 VL - 15 SP - 1 EP - 11 PB - Elsevier CY - Amsterdam ER -