TY - GEN A1 - Mańkowska, Ewa A1 - Mazur, Michał A1 - Domaradzki, Jarosław A1 - Mazur, Piotr A1 - Kot, Małgorzata A1 - Flege, Jan Ingo T1 - Hydrogen Gas Sensing Properties of Mixed Copper–Titanium Oxide Thin Films T2 - Sensors N2 - Hydrogen is an efficient source of clean and environmentally friendly energy. However, because it is explosive at concentrations higher than 4%, safety issues are a great concern. As its applications are extended, the need for the production of reliable monitoring systems is urgent. In this work, mixed copper–titanium oxide ((CuTi)Ox) thin films with various copper concentrations (0–100 at.%), deposited by magnetron sputtering and annealed at 473 K, were investigated as a prospective hydrogen gas sensing material. Scanning electron microscopy was applied to determine the morphology of the thin films. Their structure and chemical composition were investigated by X-ray diffraction and X-ray photoelectron spectroscopy, respectively. The prepared films were nanocrystalline mixtures of metallic copper, cuprous oxide, and titanium anatase in the bulk, whereas at the surface only cupric oxide was found. In comparison to the literature, the (CuTi)Ox thin films already showed a sensor response to hydrogen at a relatively low operating temperature of 473 K without using any extra catalyst. The best sensor response and sensitivity to hydrogen gas were found in the mixed copper–titanium oxides containing similar atomic concentrations of both metals, i.e., 41/59 and 56/44 of Cu/Ti. Most probably, this effect is related to their similar morphology and to the simultaneous presence of Cu and Cu2O crystals in these mixed oxide films. In particular, the studies of surface oxidation state revealed that it was the same for all annealed films and consisted only of CuO. However, in view of their crystalline structure, they consisted of Cu and Cu2O nanocrystals in the thin film volume. KW - mixed copper–titanium oxides KW - Cu2O KW - TiO2 KW - (CuTi)Ox KW - hydrogen gas sensing KW - thin films KW - magnetron sputtering Y1 - 2023 U6 - https://doi.org/10.3390/s23083822 SN - 1424-8220 VL - 23 IS - 8 ER - TY - GEN A1 - Mazur, Michał A1 - Kapuścik, Paulina A1 - Weichbrodt, Wiktoria A1 - Domaradzki, Jarosław A1 - Mazur, Piotr A1 - Kot, Małgorzata A1 - Flege, Jan Ingo T1 - WO3 Thin-Film Optical Gas Sensors Based on Gasochromic Effect towards Low Hydrogen Concentrations T2 - Materials N2 - Hydrogen gas sensors have recently attracted increased interest due to the explosive nature of H2 and its strategic importance in the sustainable global energy system. In this paper, the tungsten oxide thin films deposited by innovative gas impulse magnetron sputtering have been investigated in terms of their response to H2. It was found that the most favourable annealing temperature in terms of sensor response value, as well as response and recovery times, was achieved at 673 K. This annealing process caused a change in the WO3 cross-section morphology from a featureless and homogenous form to a rather columnar one, but still maintaining the same surface homogeneity. In addition to that, the full-phase transition from an amorphous to nanocrystalline form occurred with a crystallite size of 23 nm. It was found that the sensor response to only 25 ppm of H2 was equal to 6.3, which is one of the best results presented in the literature so far of WO3 optical gas sensors based on a gasochromic effect. Moreover, the results of the gasochromic effect were correlated with the changes in the extinction coefficient and the concentration of the free charge carriers, which is also a novel approach to the understanding of the gasochromic phenomenon. KW - Tungsten oxide (WO3) KW - gas impulse magnetron sputtering KW - thin film KW - gasochromic properties KW - optical properties KW - annealing KW - optical hydrogen gas sensor Y1 - 2023 U6 - https://doi.org/10.3390/ma16103831 SN - 1996-1944 VL - 16 IS - 10 ER -